Flame-retarding high-temperature-resistant insulation material used for cables and preparation method thereof

A high temperature resistant, cable technology, applied in the direction of rubber insulators, organic insulators, etc., can solve the problems of easy falling off, loss of protection, etc., and achieve the effect of easy to obtain raw materials, reduce reaction time, and high tensile strength

Inactive Publication Date: 2018-06-01
HEFEI SHANGQIANG ELECTRIC TECH CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, cables are used in theaters, subways, and airports. Although they can be fire-resistant and high-temperature resistant to a certain extent, they are easy to fall off after long-term use and lose their protective effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of flame-retardant and high-temperature insulating material for cables in this embodiment includes the following raw materials in parts by weight:

[0034] 28 parts of neoprene rubber, 24 parts of chlorinated polyethylene rubber, 20 parts of fly ash, 16 parts of mica powder, 14 parts of iron oxide powder, 4 parts of antioxidant, 2 parts of flame retardant, 2 parts of plasticizer, heat 1 part of stabilizer, 1 part of ultraviolet absorber, 1 part of benzoyl peroxide.

[0035] The antioxidant in this embodiment is the antioxidant BHT.

[0036] The flame retardant in this embodiment is ammonium dihydrogen phosphate.

[0037] The plasticizer in this example is dibutyl phthalate.

[0038] The heat stabilizer in this embodiment is a metal soap stabilizer; the ultraviolet absorber is an ultraviolet absorber UV-9.

[0039] The preparation method of a flame retardant and high temperature resistant insulating material for cables of the present embodiment includes the fol...

Embodiment 2

[0046] A kind of flame-retardant and high-temperature insulating material for cables in this embodiment includes the following raw materials in parts by weight:

[0047] 32 parts of neoprene rubber, 8 parts of chlorinated polyethylene rubber, 22 parts of fly ash, 20 parts of mica powder, 15 parts of iron oxide powder, 8 parts of antioxidant, 6 parts of flame retardant, 4 parts of plasticizer, heat 1-3 parts of stabilizer, 2 parts of ultraviolet absorber, 2 parts of benzoyl peroxide.

[0048] The antioxidant in this embodiment is the antioxidant BHT.

[0049] The flame retardant in this embodiment is ammonium dihydrogen phosphate.

[0050] The plasticizer in this example is dibutyl phthalate.

[0051] The heat stabilizer in this embodiment is a metal soap stabilizer; the ultraviolet absorber is an ultraviolet absorber UV-9.

[0052] The preparation method of a flame retardant and high temperature resistant insulating material for cables of the present embodiment includes the...

Embodiment 3

[0059] A kind of flame-retardant and high-temperature insulating material for cables in this embodiment includes the following raw materials in parts by weight:

[0060] 30 parts of neoprene rubber, 26 parts of chlorinated polyethylene rubber, 21 parts of fly ash, 18 parts of mica powder, 14.5 parts of iron oxide powder, 6 parts of antioxidant, 4 parts of flame retardant, 3 parts of plasticizer, heat 2 parts of stabilizer, 1.5 parts of ultraviolet absorber, 1.5 parts of benzoyl peroxide.

[0061] The antioxidant in this embodiment is the antioxidant BHT.

[0062] The flame retardant in this embodiment is ammonium dihydrogen phosphate.

[0063] The plasticizer in this example is dibutyl phthalate.

[0064] The heat stabilizer in this embodiment is a metal soap stabilizer; the ultraviolet absorber is an ultraviolet absorber UV-9.

[0065] The preparation method of a flame retardant and high temperature resistant insulating material for cables of the present embodiment include...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flame-retarding high-temperature-resistant insulation material used for cables, which includes, by weight, 28-32 parts of chloroprene rubber, 24-28 parts of chlorinated polyethylene rubber, 20-22 parts of fly ash, 16-20 parts of mica powder, 14-15 parts of iron oxide powder, 4-8 parts of an antioxidant, 2-6 parts of a flame retardant, 2-4 parts of a plasticizer, 1-3 partsof a thermal stabilizer, 1-2 parts of an ultraviolet absorber, and 1-2 parts of benzoyl peroxide. The material is flame-retarding, high-temperature-resistant and insulating, is low in cost and is prepared from easy-to-obtained raw materials, has excellent use value and application prospect.

Description

technical field [0001] The invention relates to the technical field of cables, in particular to a flame-retardant and high-temperature resistant insulating material for cables and a preparation method thereof. Background technique [0002] With the continuous expansion of the scale of China's electric power industry, data communication industry, urban rail transit industry, automobile industry, shipbuilding and other industries, and the rapid increase in the demand for wires and cables, the wire and cable industry still has huge development potential in the future. In the event of a fire, a type of cable that can ensure the integrity of the line can continue to provide power and transmit various signals normally when the fire is high temperature, which provides a guarantee for fire control and survival. [0003] In the prior art, cables are used in dense places such as theaters, subways, and airports. Although they can have the effect of fire resistance and high temperature ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L11/00C08L23/28C08K13/02C08K3/32C08K5/12C08K3/34C08K3/22H01B3/28
CPCC08L11/00C08K2003/2265C08L2201/02C08L2201/08C08L2203/202H01B3/28C08L23/286C08K13/02C08K3/32C08K5/12C08K3/34C08K3/22
Inventor 程劲松
Owner HEFEI SHANGQIANG ELECTRIC TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com