Anti-ultraviolet PVC (Polyvinyl Chloride) gloves and preparation method thereof

An anti-ultraviolet, manufacturing method technology, applied in gloves, clothing, protective clothing, etc., can solve the problems of single function and no anti-ultraviolet, and achieve the effect of simple production process, comfortable wearing and good anti-ultraviolet performance

Inactive Publication Date: 2018-06-15
JIANGSU HUAYUAN GLOVE
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In some processing plants, the hands of operators will be exposed to ultraviolet rays, but the PVC gloves

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0068] Example 1

[0069] An anti-ultraviolet PVC glove is made of the following raw materials in weight fraction:

[0070] PVC powder 100 parts

[0071] DOP 80 servings

[0072] TXIB 10 copies

[0073] D70 10 copies

[0074] Stabilizer 2 parts

[0075] 2 parts epoxy soybean oil

[0076] 8 parts of anti-ultraviolet auxiliary agent,

[0077] Among them, the anti-ultraviolet auxiliary agent is made of the following raw materials in weight fractions: 12 parts of fluorocarbon emulsion, 2-(2'-hydroxy-3'-tert-butyl-5'-methylphenyl)-5-chloro-benzene 5 parts of triazole, 6 parts of 2-hydroxy-4-methoxybenzophenone, and 3 parts of ceramic powder.

[0078] The manufacturing method of PVC gloves is as follows:

[0079] (1) Primary ingredients: DOP, epoxidized soybean oil and anti-ultraviolet additives are mixed and then stirred, then PVC powder, stabilizer, TXIB viscosity reducer are added in turn and stirred to obtain primary ingredients;

[0080] (2) standing defoaming: the pri...

Example Embodiment

[0089] Example 2

[0090] An anti-ultraviolet PVC glove is made of the following raw materials in weight fraction:

[0091] PVC powder 100 parts

[0092] DOP 80 servings

[0093] TXIB 15 copies

[0094] D70 15 copies

[0095] Stabilizer 2.5 parts

[0096] Epoxidized soybean oil 2.5 parts

[0097] Anti-ultraviolet auxiliary agent 10 parts

[0098] Among them, the anti-ultraviolet auxiliary agent is made of the following raw materials in weight fractions: 12 parts of fluorocarbon emulsion, 2-(2'-hydroxy-3'-tert-butyl-5'-methylphenyl)-5-chloro-benzene 2 parts of triazole, 5 parts of 2-hydroxy-4-methoxybenzophenone, 4 parts of ceramic powder.

[0099] The manufacturing method of PVC gloves is as follows:

[0100] (1) Primary ingredients: DOP, epoxidized soybean oil and anti-ultraviolet additives are mixed and then stirred, then PVC powder, stabilizer, TXIB viscosity reducer are added in turn and stirred to obtain primary ingredients;

[0101] (2) standing defoaming: the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses anti-ultraviolet PVC (Polyvinyl Chloride) gloves and a preparation method thereof. The anti-ultraviolet PVC gloves are prepared from the following raw materials in parts by weight: 100 parts of PVC, 78 to 82 parts of DOP, 10 to 15 parts of TXIB, 10 to 15 parts of D70, 2 to 2.5 parts of stabilizer, 2 to 2.5 parts of epoxidized soybean oil and 5 to 10 parts of anti-ultraviolet aid, wherein the anti-ultraviolet aid is prepared from the following raw materials in parts by weight: 12 to 15 parts of a fluorocarbon emulsion, 2 to 5 parts of 2-(2'-hydroxy-3'-tert-butyl-5'-methyl phenyl)-5-chloro-benzotriazole, 5 to 8 parts of 2-hydroxyl-4-methoxybenzophenone and 3 to 4 parts of a ceramic powder. The anti-ultraviolet PVC gloves disclosed by the invention have the advantagesof good anti-ultraviolet performance, long duration time, comfortableness in wearing and low cost; the adopted anti-ultraviolet agent does not affect the transparency of a product and also has no effects on the initial coloring of the PVC gloves; the production process of the anti-ultraviolet PVC gloves is simple and easy to operate.

Description

technical field [0001] The invention relates to an anti-ultraviolet PVC glove and a manufacturing method thereof, belonging to the technical field of plastic gloves. . Background technique [0002] Due to its relatively simple production process, low material cost, convenient wearing, comfortable hand feeling, acid and alkali resistance, good isolation effect, no skin allergies, and low price, PVC gloves have developed rapidly and are widely used in Medical, electronic processing, food processing, scientific research, fast food and other fields. In some processing plants, the hands of operators will be exposed to ultraviolet rays, but the PVC gloves currently on the market have a single function and do not have the characteristic of anti-ultraviolet rays. Therefore, aiming at the deficiencies in the prior art, it is meaningful to design a kind of anti-ultraviolet PVC glove. Contents of the invention [0003] The purpose of the present invention is to solve the above-men...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L91/00C08L27/12C08K13/02C08K5/3475C08K5/132C08K5/098C08K5/12A41D19/015
CPCA41D19/0055C08L27/06C08L2201/08C08L2201/10C08L2205/03C08L91/00C08L27/12C08K13/02C08K5/3475C08K5/132C08K5/098C08K5/12
Inventor 李金才王花梅赵艳凤冯盛华张艳艳
Owner JIANGSU HUAYUAN GLOVE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap