4140 plastic die steel plate with delivery in annealed state and production method of 4140 plastic die steel plate
A technology of plastic mold and production method, applied in the field of plastic mold steel, can solve the problems of long process time, high energy consumption, not suitable for the production of medium and heavy plate products, etc. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0019] Example 1
[0020] The thickness of the 4140 plastic mold steel plate delivered in the annealed state of this embodiment is 10mm, and its chemical composition and mass percentage are: C: 0.38%, Mn: 0.75%, Si: 0.15%, S: 0.015%, P: 0.020 %, Cr: 0.80%, Mo: 0.15%, Al: 0.005%, the rest is iron and unavoidable impurities.
[0021] The production method of the 4140 plastic mold steel plate delivered in the annealed state of this embodiment includes converter smelting, LF furnace refining, RH vacuum refining, continuous casting slab, controlled rolling and cold rolling, and high temperature tempering heat treatment. The specific process steps are as follows Description:
[0022] (1) Converter smelting process: the molten iron into the converter has a sulfur content of 0.050%, and the ferromolybdenum is added to the converter at 3.5kg / t steel and scrap; the final carbon of the converter smelting is 0.10%, and the converter starts at 1 / 4 when the converter is tapped. Add steel grit al...
Example Embodiment
[0029] Example 2
[0030] The thickness of the 4140 plastic mold steel plate delivered in the annealed state of this embodiment is 150mm, and its chemical composition and mass percentage are: C: 0.43%, Mn: 1.00%, Si: 0.35%, S: 0.015%, P: 0.020 %, Cr: 1.10%, Mo: 0.25%, Al: 0.025%, the rest is iron and unavoidable impurities.
[0031] The production method of the 4140 plastic mold steel plate delivered in the annealed state of this embodiment includes converter smelting, LF furnace refining, RH vacuum refining, continuous casting slab, controlled rolling and cold rolling, and high temperature tempering heat treatment. The specific process steps are as follows Description:
[0032] (1) Converter smelting process: the molten iron into the converter, the sulfur content is 0.060%, the molten iron is pretreated and then loaded into the converter, the ferromolybdenum is added to the converter at 3.8kg / t steel and scrap; the final carbon of the converter smelting is 0.20%, the converter At ...
Example Embodiment
[0039] Example 3
[0040] The thickness of the 4140 plastic mold steel plate delivered in the annealed state of this embodiment is 100mm, and its chemical composition and mass percentage are: C: 0.41%, Mn: 0.90%, Si: 0.30%, S: 0.015%, P: 0.020 %, Cr: 1.00%, Mo: 0.20%, Al: 0.020%, the rest is iron and unavoidable impurities.
[0041] The production method of the 4140 plastic mold steel plate delivered in the annealed state of this embodiment includes converter smelting, LF furnace refining, RH vacuum refining, continuous casting slab, controlled rolling and cold rolling, and high temperature tempering heat treatment. The specific process steps are as follows Description:
[0042] (1) Converter smelting process: The molten iron into the converter has a sulfur content of 0.040%, and ferromolybdenum is added to the converter at 3.8kg / t steel and scrap; the final carbon of the converter smelting is 0.15%, and the converter starts at 1 / 4 of the time when the converter is tapped. Add stee...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap