Manganese zinc ferrite material with wide temperature, low power consumption and high magnetic permeability and preparation method thereof

A technology of manganese-zinc ferrite and high magnetic permeability, which is applied in the manufacture of inductors/transformers/magnets, the magnetism of inorganic materials, electrical components, etc., can solve the problems of operating temperature, magnetic permeability and power consumption limitations, and broaden the scope of work Effects of temperature range, cost reduction, and power loss improvement

Active Publication Date: 2020-11-03
南通三佳磁业有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing magnetic materials cannot meet the needs of industry development due to the limitations of operating temperature, magnetic permeability, power consumption, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The invention discloses a manganese-zinc ferrite material with low power consumption, wide temperature range and high magnetic permeability, comprising: a main component and a doping component; the doping component accounts for 3% of the total mass of the main component ; The main component includes the following composition in mass percentage: Fe 2 o 3 55.8%, ZnO 9.8%, MnO 34.4; the doping components include CaCO 3 , SiO 2 , NiO, Nb 2 o 5 , SnO 2 、Co 2 o 3 , La 2 o 3 and Li 2 CO 3 , and the mass ratio of each component in the doping component is: CaCO 3 : SiO 2 :NiO:Nb 2 o 5 : SnO 2 :Co 2 o 3 : La 2 o 3 : Li 2 CO 3 3:2:1:1:0.8:0.5:0. 3:0.5.

[0024] Wherein, the purity of the ZnO is greater than 99.9%, and the specific surface area is 4.5-4.8m 2 / g; the Mn 3 o 4 The purity is greater than 99.8%, and the specific surface area is 6.0-10.0m 2 / g; the Fe 2 o 3 The purity is greater than 99.8%, and the specific surface area is 4.2-4.5m 2 / g. By...

Embodiment 2

[0033] The invention discloses a manganese-zinc ferrite material with low power consumption, wide temperature range and high magnetic permeability, comprising: a main component and a doping component; the doping component accounts for 5% of the total mass of the main component ; The main component includes the following composition in mass percentage: Fe 2 o 3 58.7%, ZnO 11.2%, MnO 30.1; the doping components include CaCO 3 , SiO 2 , NiO, Nb 2 o 5 , SnO 2 、Co 2 o 3 , La 2 o 3 and Li 2 CO 3 , and the mass ratio of each component in the doping component is: CaCO 3 : SiO 2 :NiO:Nb 2 o 5 : SnO 2 :Co 2 o 3 : La 2 o 3 : Li 2 CO 3 is 4:3:2:1.5:1.2:0.8:0.5:1.

[0034] Wherein, the purity of the ZnO is greater than 99.9%, and the specific surface area is 4.5-4.8m 2 / g; the Mn 3 o 4 The purity is greater than 99.8%, and the specific surface area is 6.0-10.0m 2 / g; the Fe 2 o 3 The purity is greater than 99.8%, and the specific surface area is 4.2-4.5m 2 / g. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a wide temperature, low power consumption and high permeability manganese zinc ferrite material and a preparation method thereof. The material comprises a main component and adoping component, wherein the main component comprises the following components in percentage by mass: 55.8 to 58.7 percent of Fe2O3, 9.8 to 11.2 percent of ZnO, the balance of MnO, and the total amount is 100 percent. The material ensures that grains are sufficiently refined by relatively reducing the content of Fe2O3 in the main component and through a special doping technology, reduces the probability of irregular large grains, effectively improves the power consumption, meanwhile broadens the operating temperature range, has excellent properties of wide temperature, low power consumption and high permeability, is beneficial to the miniaturization of transformer devices, reduces the industrial scale production cost, and improves the operating efficiency.

Description

technical field [0001] The invention relates to the field of manganese-zinc ferrite materials, in particular to a manganese-zinc ferrite material with wide temperature, low power consumption and high magnetic permeability and a preparation method thereof. Background technique [0002] Due to the rapid development of the electronic information industry, the upgrading of electronic products is accelerating, and the products are developing towards environmental protection, energy saving and miniaturization. This has led to an unprecedented development of the basic material of electronic products - magnetic material. A large number of applications in the communication industry, IT industry, automobile industry, etc., promote the rapid development of high-performance ferrite products. [0003] At present, the size of household electronic products is gradually reduced, and energy saving and consumption reduction are required. The structure of power transformers has been miniaturi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/38C04B35/622C04B35/626C04B35/64H01F1/01H01F41/00
CPCC04B35/2633C04B35/622C04B35/62615C04B35/62645C04B35/64C04B2235/3203C04B2235/3208C04B2235/3227C04B2235/3251C04B2235/3262C04B2235/3275C04B2235/3279C04B2235/3284C04B2235/3293C04B2235/3418C04B2235/6562C04B2235/6583C04B2235/661H01F1/01H01F41/00
Inventor 黄有东李申华
Owner 南通三佳磁业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap