Polyimide film

A polyimide film, polyimide technology, applied in synthetic resin layered products, chemical instruments and methods, layered products, etc., can solve the problems of easy cracking and difficult to use as a flexible display, and achieve visual recognition. Excellent effect

Active Publication Date: 2018-08-07
SUMITOMO CHEM CO LTD
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, glass that has been used as a front panel material for image display devices has high transparency and can exhibit high hardness depending on the type of glass, but on the other hand, it is very rigid and easy to break, so it is difficult to use as Front panel materials for flexible displays

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyimide film
  • Polyimide film
  • Polyimide film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0188] Hereinafter, the present invention will be described in more detail in conjunction with examples. Unless otherwise specified, "%" and "part" in an example represent mass % and a mass part. First, the evaluation method will be described.

[0189]

[0190] Based on JIS K7105:1981, the total light transmittance of the sample was measured using a fully automatic direct-reading haze computer HGM-2DP manufactured by Suga Test Instruments.

[0191]

[0192] Gel Permeation Chromatography (GPC) Determination

[0193] (1) Pretreatment method

[0194] The sample was dissolved in γ-butyrolactone (GBL) to obtain a 20% by mass solution, diluted to 100 times with a DMF eluent, filtered through a 0.45 μm membrane filter, and the obtained solution was used as a measurement solution.

[0195] (2) Measurement conditions

[0196] Chromatographic column: TSKgel SuperAWM-H×2+SuperAW2500×1 (6.0mm I.D.×150mm×3 pieces)

[0197] Eluent: DMF (added with 10mM lithium bromide)

[0198] Fl...

manufacture example 1

[0213] [Production Example 1] Production of polyimide varnish (1) containing polyimide polymer (1)

[0214] In a nitrogen atmosphere, 1.25 g of isoquinoline was charged into a reaction vessel equipped with a solvent trap and a filter and connected to a vacuum pump. Next, 375.00 g of γ-butyrolactone (GBL) and 104.12 g of 2,2'-bis(trifluoromethyl)-4,4'-diaminobiphenyl (TFMB) were charged into the reaction vessel, and the mixture was subjected to Stir to dissolve. Further, after adding 145.88 g of 4,4'-(hexafluoroisopropylidene)diphthalic dianhydride (6FDA) to the reaction vessel, the temperature was started to rise in an oil bath while stirring the mixture.

[0215] The molar ratio of TFMB to 6FDA added was 1.00:0.99, and the monomer concentration in the mixture was 40% by mass. When the internal temperature of the reaction container reached 80°C, the pressure was reduced to 650 mmHg, and then the internal temperature was raised to 180°C. After the internal temperature reache...

manufacture example 2

[0216][Production example 2] Polyimide varnish (2) containing polyimide polymer (2)

[0217] As the polyimide varnish (2), "Neopulim (registered trademark) C6A20" manufactured by Mitsubishi Gas Chemical Co., Ltd. was used. "Neopulim C6A20" contains 22 mass % of polyimide polymers (2) in γ-butyrolactone solvent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a polyimide film and is to provide an optic-film which can be used as a front panel of a flexible display and has excellent visuognosis of white color on frames. The polyimidefilm includes at least one polyimide high-molecular substance, yellow index (YI) being 0 < YI < 1.0.

Description

technical field [0001] The present invention relates to polyimide films. Background technique [0002] Currently, image display devices such as liquid crystal display devices and organic EL display devices are widely and effectively used not only in televisions but also in mobile phones and smart watches. With the expansion of such applications, image display devices (flexible displays) having flexible characteristics are required, and flexibility of each member thereof is required. [0003] The configuration of an image display device includes, in addition to display elements such as a liquid crystal display element or an organic EL display element, a polarizing plate, a retardation plate, a front panel, and the like. In order to realize a flexible display, all the above-mentioned members need to have a flexible characteristic. When the components of an image display device are made of a flexible polymer material (for example, Patent Document 1), since the components are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J5/18C08L79/08C08K3/36C08K5/18
CPCC08J5/18C08K5/18C08K3/36C08J2379/08B32B27/281C08L79/08C08K5/17C08L2201/10
Inventor 安井未央片波岚樱井孝至
Owner SUMITOMO CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com