Photocatalytic antibacterial ecological tile and preparation method thereof

A photocatalyst antibacterial and ecological brick technology, applied in the field of building materials, can solve problems such as inability to effectively remove and kill bacteria on the surface of ceramic tiles, and achieve the effect of beautifying the home and purifying the air.

Inactive Publication Date: 2018-09-28
佛山市鸿都陶瓷有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] One of the purposes of the present invention is to provide a photocatalyst antibacterial ecological brick and its preparation method to solve the problem that traditional ceramic tiles cannot effectively remove and kill bacteria on the surface of ceramic tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0019] Photocatalyst antibacterial ecological brick, in terms of mass percentage, is composed of the following components: 32% diopside, 18% super clay, 28% burnt gemstone, 7% white clay, 12% porcelain stone, 1% debonding agent, nano-titanium dioxide 2%.

[0020] The preparation method of the described photocatalyst antibacterial ecological brick comprises the following preparation steps:

[0021] Step 1: Prepare diopside, super clay, burnt gemstone, white clay, porcelain stone, debonding agent and nano-titanium dioxide according to the mass percentage, add water and ball mill for 9 hours, and prepare mud.

[0022] Step 2, after sieving and removing iron from the mud obtained in step 1, put it into the mud pool and homogenize for 6-12 hours;

[0023] Step 3, the stale homogenized mud in step 2 is deironed again by the electromagnetic iron remover, then sent to the drying tower for drying and making powder, and then the obtained powder is sent to the silo to stale for more tha...

specific Embodiment 2

[0026] Photocatalyst antibacterial ecological brick, in terms of mass percentage, is composed of the following components: 30% diopside, 21% super clay, 26% burnt gemstone, 7% white clay, 11% porcelain stone, 1.5% debonding agent, nano-titanium dioxide 3.5%.

[0027] The preparation method of the described photocatalyst antibacterial ecological brick comprises the following preparation steps:

[0028] Step 1: Prepare diopside, super clay, burnt gemstone, white clay, porcelain stone, debonding agent and nano-titanium dioxide according to the mass percentage, add water and ball mill for 9 hours, and prepare mud.

[0029] Step 2, after sieving and removing iron from the mud obtained in step 1, put it into the mud pool and homogenize for 6-12 hours;

[0030] Step 3, the stale homogenized mud in step 2 is deironed again by the electromagnetic iron remover, then sent to the drying tower for drying and making powder, and then the obtained powder is sent to the silo to stale for more...

specific Embodiment 3

[0033] Photocatalyst antibacterial ecological brick, in terms of mass percentage, is composed of the following components: 30% diopside, 18.7% super clay, 26% burnt gemstone, 8% white clay, 12% porcelain stone, 1.3% debonding agent, nano-titanium dioxide 4%.

[0034] The preparation method of the described photocatalyst antibacterial ecological brick comprises the following preparation steps:

[0035] Step 1: Prepare diopside, super clay, burnt gemstone, white clay, porcelain stone, debonding agent and nano-titanium dioxide according to the mass percentage, add water and ball mill for 9 hours, and prepare mud.

[0036] Step 2, after sieving and removing iron from the mud obtained in step 1, put it into the mud pool and homogenize for 6-12 hours;

[0037] Step 3, the stale homogenized mud in step 2 is deironed again by the electromagnetic iron remover, then sent to the drying tower for drying and making powder, and then the obtained powder is sent to the silo to stale for more...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of building materials and in particular relates to a photocatalytic antibacterial ecological tile and a preparation method thereof. The tile is composed of the following components in percentage by mass: 30-32% of diopside, 18-21% of special grade clay, 26-28% of flint clay, 7-9% of white mud, 11-13% of chinastone, 1-1.5% of a dispergator and 2-5% of nanometer titania. The preparation method of the tile comprises the following steps: 1, taking various components in percentage by mass, adding and ball-milling to form mud; 2, screening the mud, removing iron, and performing decay homogenization; 3, removing iron from the mud subjected to decay homogenization, drying the prepared powder, and decaying the powder; 4, performing press molding on the powder, andperforming primary firing to obtain a biscuit; 5, glazing and printing the biscuit, and performing secondary firing, thereby obtaining the finished product. The tile is capable of killing bacteria under sunlight or ultraviolet light.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a photocatalyst antibacterial ecological brick and a preparation method thereof. Background technique [0002] In family kitchens, bathrooms, especially hospitals, public toilets, etc., it is easy to breed and reproduce bacteria, such as candida and streptococcus. These bacteria can affect people's health and induce diseases such as pneumonia. [0003] As a decoration material, traditional tiles are widely used in home kitchens and bathrooms. However, in addition to the use function and decorative effect, traditional tiles cannot effectively remove and kill the bacteria that adhere to, breed and multiply on the surface of the tiles, and cannot meet people's needs for environmental sanitation. Contents of the invention [0004] One of the purposes of the present invention is to provide a photocatalyst antibacterial ecological brick and its preparation method to solve the prob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/10C04B33/34
CPCC04B33/10C04B33/13C04B33/131C04B33/34C04B2235/3427C04B2235/3445C04B2235/3232C04B2235/96
Inventor 林赟
Owner 佛山市鸿都陶瓷有限公司