Production method of lost foam casting anode steel claw head and anode steel claw head lost module

A technology of lost foam casting and anode steel claw, which is applied in casting molding equipment, casting molds, casting mold components, etc., can solve the problems of increased pressure drop and power loss, easy to be corroded, oxidized, and high production and maintenance costs. The effect of improving grain morphology, improving corrosion resistance and oxidation resistance, and reducing production and maintenance costs

Pending Publication Date: 2018-09-28
百色皓海碳素有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the use of existing anode steel claws, the part above the joint between the claw head and the phosphorus iron ring in the carbon electrode is easily corroded and oxidized, resulting in bending and thin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of lost foam casting anode steel claw head and anode steel claw head lost module
  • Production method of lost foam casting anode steel claw head and anode steel claw head lost module
  • Production method of lost foam casting anode steel claw head and anode steel claw head lost module

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Such as Figure 1-3 As shown, the present invention provides a kind of production method of lost foam casting anode steel claw head, comprising:

[0039] Step 1, preparing molten steel, the content of chromium in the molten steel is 3%, the content of manganese is 0.6%, the content of carbon is 0.45%, the content of silicon is 0.4%, the content of molybdenum is 0.2%, the content of sulfur is less than 0.04%, and the content of phosphorus is less than 0.04% %, the balance is Fe, and the molten steel is made by directly melting low-carbon steel and alloy materials according to the formula quantity;

[0040] Step 2: Using the lost foam casting process, pour molten steel into the lost die set of the anode steel claw head, cool and form it, and the finished product is obtained.

[0041] Wherein said anode steel claw head disappearing module includes, claw head white mold 1, which is a vertically arranged cylindrical structure, and the opposite sides near the top of the uppe...

Embodiment 2

[0044] The present invention provides a kind of production method of lost foam casting anode steel claw head, comprising:

[0045] Step 1, preparing molten steel, the content of chromium in the molten steel is 4.5%, the content of manganese is 0.9%, the content of carbon is 0.6%, the content of silicon is 0.6%, the content of molybdenum is 0.25%, the content of sulfur is less than 0.04%, and the content of phosphorus is less than 0.04% %, the balance is Fe, and the molten steel is made by directly melting low-carbon steel and alloy materials according to the formula quantity;

[0046] Step 2: Using the lost foam casting process, pour molten steel into the lost die set of the anode steel claw head, cool and form it, and the finished product is obtained. All the other operating conditions are the same as in Example 1.

[0047] After the prepared anode steel claw head was welded to the anode steel claw beam, it was used for performance testing in actual aluminum production, and ...

Embodiment 3

[0049] The present invention provides a kind of production method of lost foam casting anode steel claw head, comprising:

[0050] Step 1, preparing molten steel, the content of chromium in the molten steel is 6%, the content of manganese is 1.2%, the content of carbon is 0.8%, the content of silicon is 0.8%, the content of molybdenum is 0.3%, the content of sulfur is less than 0.04%, and the content of phosphorus is less than 0.04% %, the balance is Fe, and the molten steel is made by directly melting low-carbon steel and alloy materials according to the formula quantity;

[0051] Step 2: Using the lost foam casting process, pour molten steel into the lost die set of the anode steel claw head, cool and form it, and the finished product is obtained. All the other operating conditions are the same as in Example 1.

[0052] The prepared anodized steel claw head was welded to the anode steel claw beam, and then used for performance testing in actual aluminum production. The aver...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production method of a lost foam casting anode steel claw head. The production method comprises the following steps of: preparing molten steel, wherein the molten steel comprises the following components in proportion: 3-6% of chromium, 0.6-1.2% of manganese, 0.45-0.8% of carbon, 0.4-0.8% of silicon, 0.2-0.3% of molybdenum, less than 0.04% of Sulphur, less than 0.04% of phosphorus and the balance of Fe; and pouring the molten steel into an anode steel claw head lost module by adoption of a lost foam casting process, so as to obtain the lost foam casting anode steel claw head. The invention furthermore discloses the anode steel claw head lost module. The anode steel claw head is good in comprehensive quality and long in service, so that the production and maintenance cost can be remarkably reduced.

Description

technical field [0001] The invention relates to the field of anode steel claw preparation. More specifically, the present invention relates to a method of lost foam casting anodic steel claw head and the lost mold group of anodic steel claw head. Background technique [0002] The era of low-carbon economy is the need of today's scientific and technological progress and development, and energy saving and consumption reduction is also the need of today's national policy and sustainable economic development. The electrolytic aluminum anode steel claw is the connection component between the anode carbon block on the electrolytic cell and the busbar wire. It loads a large current during the aluminum electrolysis process. It is one of the most important consumable parts for electrolytic aluminum production enterprises. The quality of the steel claw is good. Bad directly affects production efficiency and production cost. During the use of existing anode steel claws, the part abov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/22C25C3/12B22C9/04B22C9/22C09D1/00C09D5/10C09D7/61
CPCC22C38/002C22C38/02C22C38/04C22C38/22C25C3/12C09D1/00C09D5/10C09D7/61B22C9/04B22C9/22Y02P10/20
Inventor 邓家宏黄三财徐赋曹建富陈朝永黄丽梅
Owner 百色皓海碳素有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap