A kind of high-strength slow-setting plant-growing concrete and its preparation method

A planting concrete and slow-setting technology, which is applied to ceramic products, other household appliances, household appliances, etc., can solve problems such as difficulty in ensuring construction quality, insignificant effect of setting adjustment materials, and affecting concrete strength and durability. Achieve the effect of improving the ability of water and fertilizer retention, improving the compressive strength and high construction quality

Active Publication Date: 2021-02-09
SHENZHEN GANGCHUANG BUILDING MATERIAL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Soil-retaining slope protection requires planting concrete to have a certain strength and durability, but the strength and porosity of planting concrete are almost a contradiction, and it is difficult to balance the two
It is suitable for plant growth and requires the use of cementitious materials with low alkalinity in the process of preparing concrete. At present, the rapid hardening and early strength sulphoaluminate cement can meet the requirements of low alkalinity, but at the same time, the cement has the characteristics of rapid hardening and early strength. Generally, the initial setting time is usually within ten minutes. In order to ensure normal construction, setting-adjusting materials will be added in the process of preparing concrete. However, the currently-applied setting-adjusting materials have no significant setting-adjusting effect and will affect the strength and durability of concrete. It is difficult to guarantee the construction quality in practical engineering applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] In the embodiment of the present invention, a kind of high-strength slow-setting type plant-growing concrete, the raw materials used include 71 parts by weight of stones, 10 parts of rapid-hardening and early-strength sulphoaluminate cement, 1.1 parts of pumice powder, and 2.15 parts of water. 0.15 parts of polycarboxylate superplasticizer, 0.005 parts of graphene oxide powder, 10 parts of concentrated sulfuric acid, and 0.01 part of sodium lignosulfonate.

[0026] (1) Put 0.005 parts of graphene oxide powder into a 250ml flask, slowly add 10 parts of concentrated sulfuric acid into the flask, place the flask in a water bath, control the temperature at 40°C, and stir for 70 hours to obtain sulfonated graphite oxide Alkene (S-GO), the S-GO was suction filtered and washed to a pH of 5.

[0027] (2) Add 0.01 parts of sodium lignosulfonate and 0.15 parts of polycarboxylate superplasticizer into the S-GO washing liquid, heat and stir in a water bath for 60 minutes, the condi...

Embodiment 2

[0033] In the embodiment of the present invention, a kind of high-strength slow-setting type plant-growing concrete, the raw materials used include 85 parts by weight of stones, 18 parts of rapid-hardening and early-strength sulphoaluminate cement, 2.4 parts of pumice powder, and 4.45 parts of water. 0.24 parts of polycarboxylate superplasticizer, 0.04 parts of graphene oxide powder, 15 parts of concentrated sulfuric acid, and 0.03 parts of sodium lignosulfonate.

[0034] (1) Put 0.04 parts of graphene oxide powder into a 250ml flask, slowly add 15 parts of concentrated sulfuric acid into the flask, place the flask in a water bath, control the temperature at 50°C, and stir for 80 hours to obtain sulfonated graphite oxide Alkene (S-GO), the S-GO was suction filtered and washed to a pH of 6.

[0035] (2) Add 0.03 parts of sodium lignosulfonate and 0.24 parts of polycarboxylate superplasticizer into the S-GO washing liquid, heat and stir in a water bath for 90 minutes, the condit...

Embodiment 3

[0041] In the embodiment of the present invention, a kind of high-strength slow-setting type plant-growing concrete, the raw materials used in it include 75 parts by weight of stones, 14 parts of rapid-hardening and early-strength sulphoaluminate cement, 1.6 parts of pumice powder, and 3.45 parts of water. 0.19 parts of polycarboxylate superplasticizer, 0.02 parts of graphene oxide powder, 12 parts of concentrated sulfuric acid, and 0.02 parts of sodium lignosulfonate.

[0042] (1) Put 0.02 parts of graphene oxide powder into a 250ml flask, slowly add 12 parts of concentrated sulfuric acid into the flask, place the flask in a water bath, control the temperature at 40-50°C, and stir for 70-80h to obtain sulfonic acid groups The Graphene Oxide (S-GO) was obtained, and the S-GO was suction-filtered and washed to a pH value of 6.

[0043] (2) Add 0.02 parts of sodium lignosulfonate and 0.19 parts of polycarboxylate superplasticizer into the S-GO washing liquid, heat and stir in a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-strength slow-setting type plant-growing concrete. The raw materials used in the concrete include: 71-85 parts of gravel, 10-18 parts of cement, 1.1-2.4 parts of pumice powder, 2.15-4.45 parts of water, and a water reducer 0.15-0.24 parts, 0.005-0.04 parts of graphene oxide powder, 10-15 parts of concentrated sulfuric acid, 0.01-0.03 parts of sodium lignosulfonate. In the present invention, graphene oxide can significantly improve the strength of the fast-hardening and early-strength type sulphoaluminate cement matrix, which can ensure that the planting concrete has enough pores for plant growth; in the present invention, the S-GO polycarboxylic acid admixture can improve the fast-hardening and early-strength sulfoaluminate cement matrix. The fluidity of hard early-strength type sulphoaluminate cement and the effect of prolonging the setting time of fast-hardening and early-strength type sulphoaluminate cement; the pozzolanic effect of pumice powder in the present invention can improve the intensity of planting concrete, and more consumption of concrete Alkaline substances, thereby reducing the alkalinity of plant-growing concrete is conducive to plant growth.

Description

technical field [0001] The invention relates to the technical field of plant-growing concrete, in particular to a high-strength slow-setting plant-growing concrete and a preparation method thereof. Background technique [0002] The construction of infrastructure and the irrational development of natural resources have caused more and more environmental damage, resulting in the generation of a large number of secondary bare slopes. After being washed away by rainwater, a large amount of water and soil resources are lost, and even natural disasters such as landslides and mudslides are caused. endanger human survival and development. With the progress of society and the support of national policies, people's investment in environmental protection has gradually increased. In this environment, planting concrete slope protection technology came into being. [0003] Plant-growing concrete is an environmentally friendly material with a porous structure. Plants are planted on the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/06C04B38/08C04B111/40
CPCC04B28/06C04B38/08C04B2111/40C04B2201/50C04B14/02C04B14/04C04B2103/302C04B14/024C04B22/141C04B24/18
Inventor 刘裕辛继宝候双双孙文刘明乐王凯黄亚林张奔
Owner SHENZHEN GANGCHUANG BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products