A cement-based tile adhesive and a composition for preparing the adhesive

A ceramic tile adhesive and cement-based technology, applied in the field of building materials, can solve the problem that cement-based tile adhesive cannot be thickly applied, and achieve the effects of reducing transportation costs, improving shrinkage resistance, and high early strength.

Active Publication Date: 2021-09-07
KESHUN WATERPROOF TECH CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem that the current cement-based tile adhesive cannot be applied thickly, the present invention provides a quick-drying, thickly applied tile adhesive and a composition for preparing the tile adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A cement-based tile adhesive and a composition for preparing the adhesive
  • A cement-based tile adhesive and a composition for preparing the adhesive
  • A cement-based tile adhesive and a composition for preparing the adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of composition that is used to prepare cement-based tile adhesive, the specific weight (KG) proportioning of each component is as follows:

[0020]

[0021] Take the above-mentioned composition and the medium sand on the construction site, and mix the mass ratio of composition: sand = 1:4. After mixing evenly, add water accounting for 10% to 15% of the total mass, and stir it into a paste to obtain cement base tile adhesive.

Embodiment 2

[0023] A kind of composition that is used to prepare cement-based tile adhesive, the specific weight (KG) proportioning of each component is as follows:

[0024]

[0025] Take the above-mentioned composition and the medium sand on the construction site, and mix the mass ratio of composition: sand = 1:4. After mixing evenly, add water accounting for 10% to 15% of the total mass, and stir it into a paste to obtain cement base tile adhesive.

Embodiment 3

[0027] A kind of composition that is used to prepare cement-based tile adhesive, the specific weight (KG) proportioning of each component is as follows:

[0028]

[0029]

[0030] Take the above-mentioned composition and the medium sand on the construction site, and mix the mass ratio of composition: sand = 1:4. After mixing evenly, add water accounting for 10% to 15% of the total mass, and stir it into a paste to obtain cement base tile adhesive.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a cement-based tile adhesive, which comprises a composition, and the composition is composed of the following raw materials in mass percentage: 80.00%-90.00% of ordinary Portland cement; 5.00%-10.00% of low-alkalinity sulphoaluminate cement %; redispersible latex powder 2.00%~10.00%; cellulose ether 1.25%~2.00%; guar gum powder 0.25%~0.50%; early strength agent 1.00%~6.00%; also includes sand and water, among which, The mass ratio of the composition to sand is: composition:sand=1:4, water accounts for 10%-15% of the total mass. Compared with the prior art, the cement-based tile adhesive provided by the present invention increases the amount of aggregate (sand) in the formula to more than 65%, which can well reduce the shrinkage rate of the system, so that the tile adhesive can be thickly pasted, At the same time, the production cost is greatly reduced.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a cement-based ceramic tile adhesive and a composition used for preparing the adhesive. Background technique [0002] At present, the floors of buildings on the market mostly use marble or ceramic tiles, mainly because marble and ceramic tiles are easy to clean, stain-resistant, waterproof, anti-corrosion, and wear-resistant, so they are widely used in civil buildings, large shopping malls, and office buildings. And the ground decoration of public places such as hospitals, and in the construction of marble or ceramic tiles, ceramic paste materials are used to bond the marble or ceramic tiles to the ground. [0003] At present, tile paste materials mainly promote the use of cement-based tile adhesives, which use the occlusal force and van der Waals molecular force to paste tiles, which is very suitable for the current trend of low water absorption of tiles. However, the populari...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/06
CPCC04B28/06C04B2111/00646C04B2201/50C04B7/02C04B2103/0057C04B24/383C04B24/38C04B24/04C04B14/06
Inventor 梁志豪龚兴宇黄莉恒吴家伟
Owner KESHUN WATERPROOF TECH CO LTD