Phosphorus-free and nitrogen-free scouring agent as well as preparation method and use method thereof

A technology of scouring agent and fat, which is applied in the field of scouring agent, can solve the problems of not meeting the requirements of environmental protection, etc., and achieve the effects of good market application and promotion prospects, good whiteness, and high scouring efficiency

Inactive Publication Date: 2018-10-02
苏州联胜化学有限公司
7 Cites 4 Cited by

AI-Extracted Technical Summary

Problems solved by technology

[0006] In addition, among the scouring agents used in the industry, some scouring agents still use non-environmentally friendly raw materials such as alkylphenol polyoxye...
View more

Method used

A kind of non-phosphorous and nitrogen-free scouring agent that the present invention relates to and its preparation and use method, wherein said non-phosphorous and nitrogen-free scouring agent adopts the environmental protection formula that does no...
View more

Abstract

The invention provides a phosphorus-free and nitrogen-free scouring agent as well as a preparation method and a use method thereof. The phosphorus-free and nitrogen-free scouring agent comprises the following preparation components: isomeric fatty alcohol polyoxyethylene ether, fatty alcohol polyoxyethylene polyoxypropylene ether, rosin polyoxyethylene ether carboxylate, sodium secondary alkyl sulfonate and water. The invention provides the phosphorus-free and nitrogen-free scouring agent which is free from phosphorus, nitrogen and APEO and biodegradable, is an environment-friendly scouring agent, and has a high gross scouring effect and good whiteness in use.

Application Domain

Fibre treatment

Technology Topic

ChemistryRosin +10

Examples

  • Experimental program(1)

Example Embodiment

[0030] In the following, in conjunction with examples, the technical solutions of a phosphorus- and nitrogen-free scouring agent and its preparation and use methods related to the present invention will be further described in detail.
[0031] In the present invention, all the raw materials used are conventionally used and can be purchased from the market. In the present invention, unless otherwise specified, all amounts, percentages and parts are weight units.
[0032] An embodiment of the present invention provides a phosphorus- and nitrogen-free scouring agent, which is composed as follows in weight percentage:
[0033] Isomerized fatty alcohol polyoxyethylene ether 8.2%;
[0034] Fatty alcohol polyoxyethylene polyoxypropylene ether 14.8%;
[0035] Rosin polyoxyethylene ether carboxylate 26.6%;
[0036] Sodium secondary alkyl sulfonate 15.4%;
[0037] Water 35.0%.
[0038] Further, the preparation method of the phosphorus- and nitrogen-free scouring agent includes the following steps:
[0039] Add the melted isomeric fatty alcohol polyoxyethylene ether and fatty alcohol polyoxyethylene polyoxypropylene ether in order in the reaction kettle according to weight percentage, turn on the stirrer, and fully stir for 30-50 minutes;
[0040] Then add the rosin polyoxyethylene ether carboxylate and sodium secondary alkyl sulfonate in sequence, and heat to 50-60°C while stirring;
[0041] Slowly add the measured pure water (the addition will be completed within 30-60 minutes), and continue to keep stirring at 50-60°C for 1-2 hours;
[0042] After fully stirring and uniformly, the temperature is lowered to 30-40° C. and the material is filtered out to obtain the phosphorus- and nitrogen-free scouring agent.
[0043] In an implementation of the use of the phosphorus- and nitrogen-free scouring agent, the fabric involved is a pure cotton yarn card 20X16 fabric, the process is a cold pile process, and the materials involved include:
[0044] Caustic soda 50g/L;
[0045] The phosphorus- and nitrogen-free scouring agent 15g/L;
[0046] Hydrogen peroxide (100%) 30g/L;
[0047] Oxygen bleaching stabilizer 15g/L;
[0048] Among them, two dip and two rolling at room temperature, the rolling reduction rate is 100%.
[0049] Further, it also includes the following steps:
[0050] Stack at room temperature for 16~24 hours-----wash with hot water (95℃) for 3 times----wash with cold water for 2 times----dry to regain moisture.
[0051] Test the gross effect and whiteness: gross effect (cm/30min): 14.8; whiteness: 80.5%.
[0052] The present invention relates to a phosphorus- and nitrogen-free scouring agent and a preparation and use method thereof. The phosphorus- and nitrogen-free scouring agent adopts an environmentally friendly formula that does not contain nitrogen, phosphorus and APEO, and has high scouring efficiency during use. , The whiteness is good, making it an environmentally friendly scouring agent with high processing efficiency, and has a good market application prospect.
[0053] The technical scope of the present invention is not limited to the content in the above description. Those skilled in the art can make various deformations and modifications to the above embodiments without departing from the technical idea of ​​the present invention, and these deformations and modifications should belong to Within the scope of the present invention.

PUM

no PUM

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.

Similar technology patents

High-silicon daily reinforced porcelain and preparation method thereof

PendingCN114380571Agood whitenessGood sintering performance
Owner:GUANGDONG SITONG GROUP

Five-in-one low-temperature quickly-smelting agent

InactiveCN101418514Agood whitenessImprove gross effect
Owner:SHANDONG JINLU CHEM

Intelligent assembly line for cleaning garbage cans

ActiveCN106494849AImprove processing efficiencySimple and reasonable configuration
Owner:YANGZHOU JINWEI ENVIRONMENTAL PROTECTION TECH CO LTD

Method for producing tetrabromobisphemol A with high whiteness degree

InactiveCN101429101Aenvironmentally friendlygood whiteness
Owner:CHINA UNIV OF PETROLEUM (EAST CHINA)

Classification and recommendation of technical efficacy words

  • good whiteness

Five-in-one low-temperature quickly-smelting agent

InactiveCN101418514Agood whitenessImprove gross effect
Owner:SHANDONG JINLU CHEM

Method for producing tetrabromobisphemol A with high whiteness degree

InactiveCN101429101Aenvironmentally friendlygood whiteness
Owner:CHINA UNIV OF PETROLEUM (EAST CHINA)

High-silicon daily reinforced porcelain and preparation method thereof

PendingCN114380571Agood whitenessGood sintering performance
Owner:GUANGDONG SITONG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products