Composite piezoelectric catalyst as well as preparation method and application thereof

A catalyst and composite technology, which is applied in composite piezoelectric catalyst and its preparation, and its application in sonocatalytic cracking of water for hydrogen production. To meet the needs of energy conversion technology development and other issues, the preparation method is simple, the practical application is broadened, and the effect of broad application prospects is achieved.

Inactive Publication Date: 2018-10-19
FUZHOU UNIV
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are few studies on the use of the piezoelectric effect of catalysts to split pure water and generate hydrogen reported at home and abroad, only involving hexagonal ZnO fibrous microcrystals, tetragonal BaTiO 3 Dendritic crystallites ( J. Phys. Chem. Lett . 2010 , 1 , 997–1002), the sound-driven hydrogen production catalyst used is a single piezoelectric semiconductor, and its hydrogen production efficiency needs to be improved, which cannot meet the development needs of mechanical energy-hydrogen energy conversion technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite piezoelectric catalyst as well as preparation method and application thereof
  • Composite piezoelectric catalyst as well as preparation method and application thereof
  • Composite piezoelectric catalyst as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Example 1 Alcothermal Synthesis of ZnO Nanorods with Excellent Piezoelectric Properties

[0025] Weigh 0.330 g of (C 4 h 6 NO 4 ) 2 Zn (1 mmol) and 0.56 g of KOH (10 mmol) were dissolved in 10 mL and 20 mL of n-propanol, respectively; then the alcoholic solutions of the two reactants were slowly mixed and stirred for 30 min to make the precursors uniformly mixed, Afterwards, the reaction kettle was covered and sealed, put into a stainless steel sleeve and locked, placed in a programmed temperature-raising blast oven, and raised from room temperature to 150 °C over 60 minutes, and then naturally dropped to room temperature after 24 hours of heat preservation; the obtained precipitation was deionized with After washing with water for 6 times until the ion concentration of the mother solution dropped below 10 ppm, it was then transferred to a vacuum oven at 60 °C for 24 h to obtain a white powder, namely ZnO nanorods with excellent piezoelectric properties.

Embodiment 2

[0026] Example 2 Synthesis of ZnO-Au Composite Piezoelectric Catalyst by Defect Reduction Method

[0027] Weigh 50 mg of the zinc oxide nanorods obtained in Example 1, and disperse it in 50 mL of deionized water, then add 2.5 mL of 0.02 g / mL HAuCl 4 4H 2 O, and stirred for 4 h under dark conditions, the oxygen vacancy defects on the surface of ZnO were used to reduce gold ions to simple gold, which was loaded on the surface of nanorods. After the reduction, the sample was washed 4 times with deionized water until the ion concentration of the mother solution dropped below 10 ppm, and then transferred to a vacuum oven at 60 °C for 24 h to obtain a purple powder, which is the ZnO-Au composite piezoelectric catalyst.

Embodiment 3

[0028] Example 3 Structural Characterization

[0029] The sample that embodiment 1, 2 is made is scanned by X-ray diffractometer, and the results are shown in figure 1 . Depend on figure 1 It can be determined that the obtained samples are hexagonal wurtzite crystal ZnO and ZnO-Au composites, respectively.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a composite piezoelectric catalyst as well as a preparation method and application thereof in sound catalytic cracking hydrogen production from water. The preparation method comprises the following step: by virtue of an oxygen vacancy defect on the surface of zinc oxide, performing in-situ reduction on the zinc oxide on the surfaces of nano rods to form an elementary substance of gold, thereby obtaining a ZnO-Au composite piezoelectric catalyst, wherein the zinc oxide nanorods with special orientation generate positive and negative charges on the surfaces by enriching sound wave energy in an environment through a piezoelectric effect, then pure water decomposition can be promoted, and hydrogen can be generated; in addition, after the elementary substance of gold isloaded, the hydrogen production capability of the ZnO-Au composite piezoelectric catalyst can be greatly improved, the hydrogen generation velocity of the ZnO-Au composite piezoelectric catalyst undersound wave driving is 4 times that of non-loaded zinc oxide nanorods, limits of a single piezoelectric material as a sound catalyst are broken through, efficient utilization of sound energy is achieved, a novel way is provided for water cracking hydrogen production under the piezoelectric effect, and the composite piezoelectric catalyst has wide application prospects in the field of mechanical energy-hydrogen energy conversion, and is simple in preparation method and applicable to industrial production.

Description

technical field [0001] The technical field of catalytic materials of the present invention particularly relates to a composite piezoelectric catalyst and its preparation and application in hydrogen production by sonocatalytic cracking of water. Background technique [0002] The rapid expansion of population, the rapid development of economy, and the excessive exploitation and consumption of fossil energy have caused the worldwide problem of energy shortage. At present, many countries around the world have formulated corresponding policies to address the energy shortage problem, so as to promote the sustainable development of social economy. As a clean and pollution-free renewable energy, hydrogen energy is particularly important for the development of industrial production and national economy. [0003] Using the abundant renewable energy in nature to directly drive the water splitting reaction with the assistance of energy conversion materials can convert low-density energ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/52C01B3/04
CPCB01J23/52B01J35/0033C01B3/042C01B2203/0277Y02E60/36
Inventor 刘平王凯强叶云黄学烟赵燕雷瑞高帆
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap