PVC modified material used for automobile charging pile and preparation method thereof

A modified material and car charging technology, which is applied in the field of PVC materials, can solve problems such as poor thermal stability, poor fluidity, and poor antistatic, and achieve good compatibility, improved thermal stability, and improved impact resistance.

Inactive Publication Date: 2018-11-20
广东祺龙科技有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polyvinyl chloride (PVC) is one of the earliest industrialized and widely used general-purpose thermoplastics. It has the advantages of light weight, high strength, insulation, flame retardancy, corrosion resistance, excellent comprehensive performance, low price and wide source of raw materials; but also There are the following disadvantages: 1. The toughness is poor, and it is easy to be brittle when impacted, so it cannot be used as a structural material. In addition, the brittleness of polyvinyl chloride is greatly affected by temperature. The lower limit of general PVC products is -15°C. The lower limit of use of PVC is -30°C; 2. Poor thermal stability, it begins to decompose HCl at 100°C, and decomposes more rapidly when it is higher than 150°C, and the melting temperature of PVC is about 210°C; 3. The viscosity of PVC Extremely high, extremely poor fluidity, which limits its use to a certain extent
[0003] However, the existing PVC materials for car charging piles have defects such as poor anti-static, which limits their use to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC modified material used for automobile charging pile and preparation method thereof
  • PVC modified material used for automobile charging pile and preparation method thereof
  • PVC modified material used for automobile charging pile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A PVC modified material for a car charging pile, comprising the following raw materials in parts by weight:

[0044]

[0045]

[0046] The PVC resin is a high degree of polymerization ethylene-based PVC resin with an average degree of polymerization of 1750.

[0047] The preparation method of the gasoline-resistant plasticizer is as follows: weigh 20 parts of cage-type organosilicon hybrid star polyester, 15 parts of 2-hydroxystearic acid triglyceride, diethylene glycol dibenzoate 15 parts, 10 parts of epoxy fatty acid methyl ester, 20 parts of polyhydroxyvaleric acid, 15 parts of terephthalic acid, 10 parts of ricinoleic acid, 20 parts of diethylene glycol, 15 parts of polyvinyl alcohol, 10 parts of xylitol, Prepared by mixing 5 parts of chitin, 8 parts of epoxidized soybean oil and 3 parts of carbonamide, and stirring at 250°C for 60 minutes.

[0048] The filler is light calcium carbonate with a particle size of 1 μm and modified by silane coupling agent and ma...

Embodiment 2

[0058] A PVC modified material for a car charging pile, comprising the following raw materials in parts by weight:

[0059]

[0060] The PVC resin is a high degree of polymerization ethylene-based PVC resin with an average degree of polymerization of 1780.

[0061] The preparation method of the gasoline-resistant plasticizer is as follows: weigh 25 parts of cage-type organosilicon hybrid star polyester, 18 parts of 2-hydroxystearic acid triglyceride, diethylene glycol dibenzoate 18 parts, 12 parts of epoxy fatty acid methyl ester, 22 parts of polyhydroxyvaleric acid, 18 parts of terephthalic acid, 12 parts of ricinoleic acid, 22 parts of diethylene glycol, 18 parts of polyvinyl alcohol, 12 parts of xylitol, Prepared by mixing 8 parts of chitin, 9 parts of epoxidized soybean oil and 3.5 parts of carboxamide, and stirring at 280°C for 50 minutes.

[0062] The filler is light calcium carbonate with a particle size of 3 μm and modified by silane coupling agent and maleic anhyd...

Embodiment 3

[0072] A PVC modified material for a car charging pile, comprising the following raw materials in parts by weight:

[0073]

[0074] The PVC resin is a high degree of polymerization ethylene-based PVC resin with an average degree of polymerization of 1800.

[0075] The preparation method of the gasoline-resistant plasticizer is as follows: weigh 30 parts of cage-type organosilicon hybrid star polyester, 20 parts of 2-hydroxystearic acid triglyceride, diethylene glycol dibenzoate 20 parts, 15 parts of epoxy fatty acid methyl ester, 25 parts of polyhydroxyvaleric acid, 20 parts of terephthalic acid, 15 parts of ricinoleic acid, 25 parts of diethylene glycol, 20 parts of polyvinyl alcohol, 15 parts of xylitol, Prepared by mixing 10 parts of chitin, 10 parts of epoxidized soybean oil and 4 parts of carboxamide, and stirring at 300°C for 45 minutes.

[0076] The filler is light calcium carbonate with a particle size of 5 μm and modified by silane coupling agent and maleic anhyd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of PVC materials, and specially relates to a PVC modified material used for an automobile charging pile and a preparation method thereof. The PVC modifiedmaterial includes, by weight, the following raw materials: 80-120 parts of PVC resin, 40-70 parts of a gasoline resistance plasticizer, 10-15 parts of a filler, 7-11 parts of a high temperature resistance stabilizer, 8-16 parts of a cold resistance modifier, 1-3 parts of an anti-aging agent, 1-3 parts of an antistatic agent, 3-7 parts of a fire retardant, 0.6-1.0 part of an antioxidant, and 0.6-1.0 part of a lubricant. The PVC modified material has the characteristics of good antistatic effect, environmental protection, excellent performance of high temperature resistance and low temperature resistance, good effects of gasoline resistance, antioxidation and fire prevention, and good processing properties; and the PVC modified material is suitable for the automobile charging pile.

Description

technical field [0001] The invention relates to the technical field of PVC materials, in particular to a PVC modified material for automobile charging piles and a preparation method thereof. Background technique [0002] Polyvinyl chloride (PVC) is one of the earliest industrialized and widely used general-purpose thermoplastics. It has the advantages of light weight, high strength, insulation, flame retardancy, corrosion resistance, excellent comprehensive performance, low price and wide source of raw materials; but also There are the following disadvantages: 1. The toughness is poor, and it is easy to be brittle when impacted, so it cannot be used as a structural material. In addition, the brittleness of polyvinyl chloride is greatly affected by temperature. The lower limit of general PVC products is -15°C. The lower limit of use of PVC is -30°C; 2. Poor thermal stability, it begins to decompose HCl at 100°C, and decomposes more rapidly when it is higher than 150°C, and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L67/00C08L67/04C08L29/04C08L5/08C08K13/06C08K3/32C08K3/26C08K3/34C08K5/098C08K9/06
CPCC08L27/06C08K2003/265C08K2003/325C08K2201/011C08K2201/014C08L2201/02C08L2201/04C08L2201/08C08L2205/035C08L67/00C08L67/04C08L29/04C08L5/08C08K13/06C08K3/32C08K3/26C08K3/34C08K5/098C08K9/06
Inventor 宁建华
Owner 广东祺龙科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap