Processing method of ceramic product with good stability

The technology of a ceramic product and a processing method, which is applied to the processing field of ceramic products, can solve the problems of easy damage and fall off of the glaze layer, low overall strength and low quality, etc., and achieve the effects of not easy to peel off, reasonable matching and stable glaze layer.

Inactive Publication Date: 2018-11-23
界首市伟盛古窑彩陶制作发展有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ceramic products are mainly composed of clay and other raw materials, plus a glaze layer fixed on the outer layer. Most of the existing ceramic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing method of ceramic product with good stability

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A method for processing ceramic products with good stability, comprising the steps of:

[0034] (1) Preparation of functional fillers:

[0035] a. Mix formaldehyde and cyanuric acid amide according to the mass ratio of 1:1.2 and put them into the reaction kettle, then add 1.8% of the total mass of boric acid and 0.35% of ferrocene to obtain mixture A, and then mix the mixture A Adjust the pH value to 8.0, heat to keep the temperature in the reactor at 37°C, and stir at a speed of 260 rpm for 30 minutes before standby;

[0036] b. Add 4% polyvinyl alcohol, 1.5% phenol, 2% natron, and 0.7% manganese sulfate to the total mass of mixture A in the reaction kettle treated in operation a, then raise the temperature to 46°C to Take it out after stirring at a speed of 400 rpm for 45 minutes, and then mix it evenly with deionized water 90 times its total mass to obtain mixture B for later use;

[0037] c. Put the montmorillonite into the acid solution for soaking for 3 minutes,...

Embodiment 2

[0057] A method for processing ceramic products with good stability, comprising the steps of:

[0058] (1) Preparation of functional fillers:

[0059] a. Mix formaldehyde and cyanuric diamide according to the mass ratio of 1:1.4 and put them into the reaction kettle, then add 2.1% of the total mass of boric acid and 0.4% of ferrocene to obtain mixture A, and then mix the mixture A Adjust the pH value to 8.3, heat to keep the temperature in the reactor at 40°C, and stir at a speed of 270 rpm for 32 minutes before standby;

[0060] b. Add 5% polyvinyl alcohol, 1.7% phenol, 2.5% natron, and 1.1 manganese sulfate to the reaction kettle of the total mass of mixture A, then raise the temperature to 48° C. Take it out after 47 minutes of stirring at the speed of rotation per minute, and then mix it uniformly with deionized water with a total mass of 93 times to obtain mixture B for subsequent use;

[0061] c. Put the montmorillonite into the acid solution for soaking for 4 minutes,...

Embodiment 3

[0081] A method for processing ceramic products with good stability, comprising the steps of:

[0082] (1) Preparation of functional fillers:

[0083] a. Formaldehyde and cyanuric acid amide are mixed according to the mass ratio of 1:1.5 and then put into the reaction kettle, and then 2.4% of the total mass of boric acid and 0.45% of ferrocene are added to obtain the mixture A, and then the mixture A is mixed Adjust the pH value to 8.5, heat to keep the temperature in the reactor at 41°C, and stir at a speed of 280 rpm for 35 minutes before standby;

[0084] b. Add 6% polyvinyl alcohol, 2% phenol, 3% natron, and 1.2% manganese sulfate of the total mass of mixture A to the reaction kettle after operation a, and then raise the temperature to 50°C to Take it out after stirring at a speed of 450 rpm for 50 minutes, and then mix it evenly with deionized water with a total mass of 95 times to obtain mixture B for later use;

[0085] c. Put the montmorillonite into the acid solutio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a processing method of a ceramic product with good stability. The processing method comprises the following steps: (1) preparing function filler; (2) preparing a clay material;(3) preparing a blank, and printing; (4) firing; and (5) cooling. The processing method of the ceramic product is reasonable in matching various steps, simple and standard in process, and convenientin popularization and application; and the prepared ceramic product is good in characteristics such as strength, wear resistance, water resistance and the like, stable in glaze layer, unlikely to strip, good in comprehensive application quality, long in service life, and high in market competence.

Description

technical field [0001] The invention belongs to the technical field of ceramic processing, and in particular relates to a processing method for ceramic products with good stability. Background technique [0002] China is an ancient country of ceramics. When talking about ceramics, foreigners think of China. Chinese ancestors used soil as a material, dug holes as kilns, and chiseled them on top of chalk clay pottery blanks to produce exquisite low-temperature pottery. Jieshou has a long history of firing pottery in vertical kilns, and there are still many workshops or factories producing pottery. Ceramic products are mainly composed of clay and other raw materials, plus a glaze layer fixed on the outer layer. Most of the existing ceramic products have problems such as low overall strength and easy damage to the glaze layer, resulting in low quality and long life. low downside. In order to promote the healthy development of the ceramic products industry, it is necessary to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/04C04B33/13C04B35/626C04B35/63C04B41/86C03C8/00
CPCC03C8/00C04B33/04C04B33/13C04B35/62685C04B35/63C04B41/009C04B41/5022C04B41/86C04B2235/612C04B2235/656C04B2235/6567C04B2235/96C04B41/4535
Inventor 邢淑芹
Owner 界首市伟盛古窑彩陶制作发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap