Antibacterial waterproof inner wall putty

An interior wall putty and white cement technology, applied in the direction of filling slurry, etc., can solve the problems of application performance limitation, lack of ability to improve indoor environment, and insufficient functionality, and achieve good antibacterial and mildew resistance, reduce radiation hazards, adjust strong wet performance

Inactive Publication Date: 2018-11-23
HEFEI GUANGMIN BUILDING MATERIAL CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of interior wall putty has good physical properties, good flexibility and adhesion to the wall, but its functionali

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial waterproof inner wall putty
  • Antibacterial waterproof inner wall putty
  • Antibacterial waterproof inner wall putty

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0077] This embodiment relates to an antibacterial and waterproof interior wall putty and a preparation method thereof, the putty is composed of the following raw materials in parts by weight:

[0078] 24 parts of 325 white cement;

[0079] 20 parts of perovskite tailings powder;

[0080] Coumarone resin 14 parts;

[0081] 10 servings of banana juice;

[0082] 8 parts of bismuth vitrinate powder;

[0083] 16 parts of sea pumice powder;

[0084] 15 parts of mordenite powder;

[0085] 1.5 parts of 2-ethyl-4 methylimidazole;

[0086] 2 parts of tributoxyethyl phosphate;

[0087] 4 parts toughening agent;

[0088] 2 parts of compound coupling agent;

[0089] 1.5 parts of compound water repellent;

[0090] 12 parts of compound rubber powder;

[0091] 30 parts of magnetized water.

[0092] The selection and preparation of the toughening agent, compounded coupling agent, compounded hydrophobic agent and compounded rubber powder in this example are shown in Table 1 below: ...

Embodiment 2

[0101] This embodiment relates to an antibacterial and waterproof interior wall putty and a preparation method thereof, the putty is composed of the following raw materials in parts by weight:

[0102] Label 325 white cement 26 parts;

[0103] 22 parts of perovskite tailings powder;

[0104] Coumarone resin 16 parts;

[0105] 12 parts of plantain juice;

[0106] 9 parts of bismuth vitrinate powder;

[0107] 18 parts of sea pumice powder;

[0108] 19 parts of mordenite powder;

[0109] 2 parts of 2-ethyl-4 methylimidazole;

[0110] 2.4 parts of tributoxyethyl phosphate;

[0111] 4.5 parts of toughening agent;

[0112] 2.5 parts of compound coupling agent;

[0113] 1.8 parts of compound water repellent;

[0114] 13 parts of compound rubber powder;

[0115] 32 parts of magnetized water.

[0116] The selection and preparation of the toughening agent, compounded coupling agent, compounded hydrophobic agent and compounded rubber powder in this example are shown in Table 2...

Embodiment 3

[0126] This embodiment relates to an antibacterial and waterproof interior wall putty and a preparation method thereof, the putty is composed of the following raw materials in parts by weight:

[0127] Label 325 white cement 28 parts;

[0128] 23 parts of perovskite tailings powder;

[0129] Coumarone resin 18 parts;

[0130] 13 servings of plantain juice;

[0131] 10 parts of bismuth vitrinate powder;

[0132] 20 parts of sea pumice powder;

[0133] 21 parts of mordenite powder;

[0134] 2.2 parts of 2-ethyl-4 methylimidazole;

[0135] 2.5 parts of tributoxyethyl phosphate;

[0136] 5 parts of toughening agent;

[0137] 2.7 parts of compound coupling agent;

[0138] 2 parts of compound water repellent;

[0139] 14 parts of compound rubber powder;

[0140] 34 parts of magnetized water.

[0141] The selection and preparation of the toughening agent, compounded coupling agent, compounded hydrophobic agent and compounded rubber powder in this example are shown in Table...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thermal conductivityaaaaaaaaaa
Thermal conductivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antibacterial waterproof inner wall putty, and relates to the technical field of putty materials. The antibacterial waterproof inner wall putty is prepared from the following raw materials of 325 white cement, coumarone resin, perovskite tailing powder, bismuth vandate powder, bryozoatum powder, mererized zeolite powder, plantain juice, 2-ethyl-4-methyl imidazole, tributoxy ethyl phosphate, a toughening agent, a compound coupling agent, a compound hydrophobic agent, a compound rubber powder and magnetized water. The antibacterial waterproof inner wall putty has the advantages that the mechanical property, hydrophobicity, flexibility, purification and humidity control ability, antibacterial property, heat-insulation property, electromagnetic radiation absorption property and the like are obviously improved; the whole property is more excellent, the application property is better, and the service life is guaranteed.

Description

technical field [0001] The invention relates to the technical field of interior wall putty, in particular to an antibacterial and waterproof interior wall putty. Background technique [0002] Putty is the most commonly used kind of building decoration materials. The main components of traditional putty are talcum powder and glue. Putty, to take a step further, is a kind of base material for leveling the wall, which lays a good foundation for future decoration (painting and wallpaper). Putty is divided into two kinds: putty inside wall and putty on exterior wall. External wall putty can resist wind and sun, so it has good gelation, high strength and low environmental index. The comprehensive index of putty in the inner wall is good, and it is hygienic and environmentally friendly. Therefore, the inner wall is not for external use and the outer wall is not for internal use. Putties are usually based on gypsum or cement, so rough surfaces are easier to bond firmly. However, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 黄洋
Owner HEFEI GUANGMIN BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap