Method for producing threaded connector from plasticized super-strength gypsum powder or plasticized quick-drying cement

A quick-drying cement and connector technology, applied in the field of chemical casting, can solve the problems of high cost, troublesome processing, high price, etc., and achieve the effect of low price, simple installation and good product quality.

Inactive Publication Date: 2018-11-30
夏璐
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to overcome the disadvantages of existing connectors such as high cost and high price caused by expensive raw materials and troublesome processing, the present invention provides a method for producing wire-tooth connectors with plasticized super-strong gypsum powder or plasticized quick-drying cement. to reduce the price of certain connectors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: the method for producing silk tooth connector with plasticized super strong gypsum powder, this method comprises the steps:

[0018] a Prepare materials, prepare by weighing the plasticized super strong gypsum powder according to the size ratio of the mold;

[0019] b Mold manufacturing, according to the required product connection method to make a connector, this connector is composed of a shell and a rotating body, the shell is a boss-shaped shell with a flat front and a convex back, and a center of the boss body is designed The front and rear through holes are designed with radial grooves on the middle wall of the through hole. The rotating body is a component with a convex key designed on the outer wall of the middle part and a front and rear through hole designed in the center. When installing, the rotating body The convex key snaps into the groove on the inner wall of the housing, so that the rotating body can rotate freely in the housing by its own ...

Embodiment 2

[0024] Embodiment 2, the method for producing wire-tooth connector with plasticized quick-drying cement, this method comprises the following steps: 1. Make model: According to the size of wire-tooth connector and the tooth pitch processing model,

[0025] 2. Mold making: use the silica gel circulating in the market to make complex molds and process them into complete molds;

[0026] 3. Purchasing raw materials: the main raw material is plasticized quick-drying cement, and the auxiliary raw material is sandstone. The main raw material should be a product produced by a regular manufacturer with a compression resistance of 100 MPa or more, and the sandstone is 60-80 mesh. Quartz sand;

[0027] 4. Slurry processing: Pour 25-30 parts of clean water into the container: add 100 parts of plasticized quick-drying cement and 125 parts of quartz sand, first soak in the water container for 1-5 minutes, and then stir with a beater Uniform, become a linear flow material for standby;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for producing a threaded connector from plasticized super-strength gypsum powder or plasticized quick-drying cement comprises the following steps: making a model mold, making a mold, purchasing a raw material, processing a slurry, grouting the mold, performing demolding after a product in the mold is cooled to normal temperature, taking out the product, repairing and curing the product, and packaging the product after the product is completely dried in order to form the finished product. The raw material in the invention is the highly-hard and fast-setting plasticized super-strength gypsum powder or plasticized quick-drying cement, so the raw material can be used to substitute a metal or plastic material in order to make the threaded connector, so the product has a good quality, along service life, no pollution and a low price; and the method has the advantages of simple process, simplicity in operation, and easy availability of the material, and the produced product has theadvantages of easiness in mounting, low price, good quality, long service life, no large devices, facilities or places, fastness in processing, high efficiency, lowest investment, and convenience in enforcement, promotion and application.

Description

technical field [0001] The invention relates to a method for producing wire-tooth connectors by using plasticized super-strength gypsum powder or plasticized quick-drying cement, which belongs to the technical field of chemical casting. Background technique [0002] At present, most of the threaded connectors sold on the market, such as elbows, straight-throughs, tees, internal thread joints, and external thread joints, are made of plastic, cast iron, or stainless steel. Connectors made of gypsum or cement non-metallic materials, the reason is that the connector products of these non-metallic materials are unreliable, mismatched, uncoordinated, polluted, and wear quickly, resulting in high cost of existing connectors. Expensive. Contents of the invention [0003] In order to overcome the disadvantages of existing connectors such as high cost and high price caused by expensive raw materials and troublesome processing, the present invention provides a method for producing w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B28/00B28B1/14
CPCB28B1/14C04B28/00C04B28/14C04B14/06
Inventor 夏璐夏国华
Owner 夏璐