Preparation method of waterborne epoxy emulsion
A water-based epoxy emulsion and epoxy resin technology, which is applied in epoxy resin coatings, coatings, anti-corrosion coatings, etc., can solve the problems of short construction time, poor wettability, adhesion and salt spray resistance of self-emulsifying epoxy emulsion and other problems, to achieve the effect of good film density and improved adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0018] The present invention provides a method for preparing an aqueous epoxy emulsion, which includes the following steps:
[0019] (1) Put an appropriate amount of epoxy resin into the reaction vessel, and then sequentially add polyether and catalyst to the reaction vessel, stir evenly, heat to 30-150°C and keep for 1-7 hours. Preferably, the heating temperature in step (1) is 40-120°C, and the holding time is 2-5 hours. In specific implementation, the epoxy resin in the formula can be divided into two parts and added to the reaction vessel. The weight of each part can be determined according to the actual situation. For example, you can first take 6-45 parts of epoxy resin from the formula and put it in the reaction vessel. Into the reaction vessel and react with other raw materials. Through step (1), a hydrophilic group is provided, so that the epoxy resin is water-based and the flexibility of the epoxy resin is improved.
[0020] (2) Add the remaining epoxy resin to the abov...
Example Embodiment
[0028] Example 1
[0029] (1) Accurately weigh 6 grams of E51 epoxy resin in the formula and add it to a three-necked bottle, and then add 5 grams of polyethylene glycol ether and 0.01g of triphenylphosphine to the three-necked bottle in turn, stir well and heat to 30℃ to keep warm 7 hour;
[0030] (2) Continue to add the remaining 44 grams of E51 epoxy resin in the formula, stir evenly, add 0.1 grams of phosphoric acid at 30°C, stir again, and keep it warm for 6 hours;
[0031] (3) Cool down to 25°C, add 20 grams of water to emulsify to obtain a water-based epoxy emulsion.
Example Embodiment
[0032] Example 2
[0033] (1) Accurately weigh the mixture of 45 grams of E51 epoxy resin and bisphenol F epoxy resin (NPEF170) in the formula and add it to the three-necked bottle, and then add 20 grams of polyglycol ether ether and 5 grams to the three-necked bottle. Stannous octoate, stir well and heat to 120°C for 5 hours;
[0034] (2) Continue to add the remaining mixture of 20 grams of E51 epoxy resin and bisphenol F epoxy resin (NPEF170) in the formula, stir evenly, add 10 grams of phosphoric acid at 120°C, stir again, and keep it warm for 5 hours;
[0035] (3) Cool down to 80℃, add 25g of water to emulsify to obtain waterborne epoxy emulsion
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap