Kiln Transformation Jianzhan Firing Technology

A kiln transformation and process technology, which is applied in the field of Jianzhan firing technology, can solve the problems of unclear formula selection and temperature control, difficulty in producing beautiful rabbit hair or oil droplets, and difficulty in preparing other patterns, so as to achieve clear and beautiful patterns, High yield and easy-to-control effects

Active Publication Date: 2021-06-04
王清霞
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The main types of built-in cups are rabbit hair cups and oil drop cups. The yield rate of the preparation process of rabbit hair cups and oil drop cups reported so far is low, and there are the following limitations: First, the selection of formula and temperature control are not clear, and it is difficult to It is difficult to produce beautiful rabbit hair or oil droplets; second, generally only rabbit hair and oil droplets can be prepared, and it is difficult to prepare other patterns

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Kiln Transformation Jianzhan Firing Technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The kiln-to-build burning process includes the following steps:

[0033] (1) providing the raw material of the green body, the first glaze slurry, the second glaze slurry and the third glaze slurry, wherein,

[0034] The green body raw material is prepared by the following method: 8 parts by weight of kaolin, 2 parts by weight of red soil and 1 part by weight of field soil are mixed, pulverized, washed, passed through an 80-mesh sieve, precipitated, packed in a cloth bag to filter water, smelted mud, Stale, to obtain green body raw materials;

[0035] The first glaze slurry is prepared by the following method: 8 parts by weight of glaze ore, 2 parts by weight of plant ash, 0.03 part by weight of iron red, 1 part by weight of potassium feldspar, and 0.05 part by weight of Yixing glaze soil are mixed, and 2.5 times by weight of water is added. Grinding in a ball mill for 6h, and then passing through a 90-mesh sieve to obtain the first glaze slurry, the first glaze slurry...

Embodiment 2

[0048] The kiln-to-build burning process includes the following steps:

[0049] (1) providing the raw material of the green body, the first glaze slurry, the second glaze slurry and the third glaze slurry, wherein,

[0050] The green body raw material is prepared by the following method: 9 parts by weight of kaolin, 2.2 parts by weight of red soil and 1 part by weight of field soil are mixed, pulverized, washed, passed through an 85-mesh sieve, precipitated, bagged to filter water, smelted, Stale, to obtain green body raw materials;

[0051] The first glaze slurry is prepared by the following method: mixing 9 parts by weight of glaze ore, 1.8 parts by weight of plant ash, 0.04 part by weight of iron red, 1.1 part by weight of potassium feldspar and 0.04 part by weight of Yixing glaze clay, adding 3 times by weight of water to put Grinding in a ball mill for 6.5h, and then passing through an 80-mesh sieve to obtain the first glaze slurry, the first glaze slurry was stale for 1...

Embodiment 3

[0063] The kiln-to-build burning process includes the following steps:

[0064] (1) providing the raw material of the green body, the first glaze slurry, the second glaze slurry and the third glaze slurry, wherein,

[0065] The green body raw material is prepared by the following method: 8.5 parts by weight of kaolin, 2.5 parts by weight of red soil and 1.2 parts by weight of field soil are mixed, pulverized, washed, passed through an 85-mesh sieve, precipitated, packed in a cloth bag to filter water, smelted mud, Stale, to obtain green body raw materials;

[0066] The first glaze slurry is prepared by the following method: 8 parts by weight of glaze ore, 2 parts by weight of plant ash, 0.05 part by weight of iron red, 1.2 part by weight of potassium feldspar and 0.03 part by weight of Yixing glaze clay are mixed, and 2.8 times by weight of water is added. Grinding in a ball mill for 7h, and then passing through a 100-mesh sieve to obtain the first glaze slurry, the first gla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a firing process for kiln transformation and building a lamp. The process includes the following steps: providing body raw materials, first glaze slurry, second glaze slurry and third glaze slurry; drawing and trimming the aging body raw materials , biscuit firing, and then dipping the first glaze slurry on the green body; after the first glaze slurry on the green body dries, apply the second glaze slurry with a brush according to the expected pattern; the second glaze slurry on the green body After drying, apply the third glaze slurry with a brush according to the expected pattern; put the glazed body into the electric kiln for roasting, stop the furnace, and leave the kiln after cooling. The Jianzhan prepared by the present invention has few and small air holes, clear and beautiful patterns, and can present artistic conception patterns such as landscapes or insects and birds according to prior assumptions, and the overall appearance is beautiful and exquisite.

Description

technical field [0001] The present invention relates to the technical field of porcelain, in particular to a firing process for building a lamp. Background technique [0002] Jianzhan was once a tea set used by the royal family in the Song Dynasty, and it was also a treasure for scholars and officials to fight tea. In the middle and late Yuan Dynasty, with the war and social fashion changes, Jianyao and Jianzhan tended to decline. In the following hundreds of years, the Jianyao Jianzhan firing skills were on the verge of being lost. [0003] The main types of building cups are rabbit hair cups and oil drop cups. The reported process yield of rabbit hair cups and oil drop cups is low, and there are the following limitations: first, the selection of formula and the control of temperature are not clear, and it is very It is difficult to produce beautiful rabbit hair or oil droplets; second, generally only rabbit hair and oil droplets can be prepared, and it is difficult to pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/34C04B33/04C03C8/00C04B41/89C03C1/00
CPCC03C1/00C03C8/00C04B33/04C04B33/34C04B41/009C04B41/52C04B41/89C04B2235/6562C04B2235/661C04B41/5022C04B41/4539
Inventor 王清霞
Owner 王清霞