Ceramic material for dissolving-out of minerals, ceramic device and preparation method thereof

A technology for ceramic materials and minerals, applied in the field of materials, can solve the problems of human body damage, low dissolution rate, loss of trace elements of minerals, etc.

Inactive Publication Date: 2018-12-11
奈曼旗中华麦饭石开发有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although RO technology can effectively solve the pollution problem, it also causes the loss of minerals and trace elements in the water. Long-term drinking will cause certain damage to the human body. Under the concept of health, people often have more demand for minerals. In addition, In the prior art, the dissolution rate of materials that can provide minerals is low, and usually requires a soaking time of more than 24 hours or even longer to have a dissolution effect. Therefore, it is necessary to find a material that can quickly dissolve a variety of minerals to meet people's needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic material for dissolving-out of minerals, ceramic device and preparation method thereof
  • Ceramic material for dissolving-out of minerals, ceramic device and preparation method thereof
  • Ceramic material for dissolving-out of minerals, ceramic device and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Get the Chinese medical stone of 65 mass parts, the hexacyclite of 15 mass parts, the diatomite of 8 mass parts, the feldspar of 9 mass parts and the lepidolite of 3 mass parts mix and obtain ceramic main material, according to the table 1 shown Components and Addition A ceramic material is obtained by adding a ceramic additive to the main ceramic material, wherein the content of the ceramic additive is a percentage of the weight of the main ceramic material, and the particle size of polymethyl methacrylate in this embodiment is ≤13 μm .

[0026] Table 1 ceramic additive components and addition (additional wt%)

[0027]

[0028] Take the ceramic material obtained above, mix it according to the mass ratio of ceramic material: deionized water: ZrO2 grinding ball 1:2:3, ball mill on PMQ2L omnidirectional planetary ball mill for 18 hours, and place it in DHG-9053A drying box Drying, making balls by hand after refining the mud, using SXL-1400 box-type resistance furnace ...

Embodiment 2

[0032] Take the ceramic balls a-g prepared in Example 1, soak them in the ratio of ceramic balls: pure water=1:20, and use the TDS-3 type TDS pen to measure the salinity of the sample, the results are as follows Figure 4 As shown, the amount of dissolved elements determines the level of mineralized water TDS (total soluble solids), wherein K+, Na+ have the most obvious effect, as can be seen from the figure, the ceramic ball made by the ceramic material formula of the present invention can Minerals are dissolved rapidly in a short period of time.

[0033] The above-mentioned ceramic balls a-g soaked for 5h and 30h were respectively tested for mineralized water elements. The results are shown in Table 2-3. In the table, only some of the mineral elements detected this time are listed, and the measured heavy metal ions are far lower than the national Standard, where N.D. means that the content is lower than the detection limit. It can be seen from the table that the ceramic bal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic material for dissolving-out of minerals, a ceramic device and a preparation method thereof. The ceramic material for dissolving-out of the minerals is prepared from aceramic main material and ceramic additives, wherein the ceramic main material comprises 60 to 70wt% of medical stone, 10 to 20wt% of Liuhuanshi, 5 to 11wt% of diatomite, 4 to 14wt% of feldspar and 1to 5wt% of lithium mica; the ceramic additives comprise polymethyl methacrylate and sodium carboxymethylcellulose. The ceramic device made of the ceramic material has the advantages that multiple types of minerals can be quickly dissolved out, and the better application prospect is realized in the field of healthy drinking water.

Description

technical field [0001] The invention relates to the field of materials, in particular to a ceramic material for dissolving minerals, a ceramic device and a preparation method thereof. Background technique [0002] With the continuous progress of society, the water pollution caused by the development of industry and agriculture is becoming more and more serious. For the safety of drinking water, RO (reverse osmosis) means is used in the field of water treatment to treat water, to eliminate the pollution caused by biology (microbes, viruses, etc.), physics (mud, etc.) Sand, rust, etc.), chemical (organic matter, residual chlorine, etc.) threats. Although RO technology can effectively solve the pollution problem, it also causes the loss of minerals and trace elements in the water. Long-term drinking will cause certain damage to the human body. Under the concept of health, people often have more demand for minerals. In addition, The dissolution rate of materials that can provid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/16C04B35/634C04B35/636
CPCC04B35/16C04B35/63424C04B35/6365C04B2235/3208C04B2235/3427C04B2235/3463C04B2235/3472
Inventor 冯雷柯世文
Owner 奈曼旗中华麦饭石开发有限公司