Surface polishing process for metal part

A technology for surface polishing and metal parts, applied in the field of metal polishing, can solve the problems of residual harmful substances on the surface, environmental pollution, and low gloss, and achieve the effects of reducing microscopic roughness, low operating costs, and improving gloss

Inactive Publication Date: 2018-12-18
宗江伟
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing polishing process also has many problems, such as low gloss after polishing, residu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A metal surface polishing process, specifically implemented according to the following steps:

[0041] Step 1, pre-cleaning: wash the surface of the metal parts with high pressure, and the washing time is 15 minutes;

[0042] Step 2, degreasing: place the surface of the metal part obtained after step 1 in a cleaning solution for degreasing treatment, and then dry the surface of the metal part;

[0043] The cleaning solution is composed of triethanolamine oleate, sodium bicarbonate, sodium silicate, sodium tripolyphosphate and polyether 2010 with a mass ratio of 2:3:1:0.5:0.5;

[0044] The drying temperature is 50°C, and the drying time is 40 minutes;

[0045] Step 3, ultrasonic cleaning: put the surface of the metal parts obtained after step 2 into clean water for ultrasonic cleaning, and air-dry;

[0046] Among them, the ultrasonic cleaning time is 15 minutes;

[0047] Step 4, polishing: put the surface of the metal piece obtained after step 3 in the polishing solut...

Embodiment 2

[0055] A metal surface polishing process of the present invention is specifically implemented according to the following steps:

[0056] Step 1, pre-cleaning: wash the surface of the metal parts with high pressure, and the washing time is 15 minutes;

[0057] Step 2, degreasing: place the surface of the metal part obtained after step 1 in a cleaning solution for degreasing treatment, and then dry the surface of the metal part;

[0058] The cleaning solution is composed of triethanolamine oleate, sodium bicarbonate, sodium silicate, sodium tripolyphosphate and polyether 2010 with a mass ratio of 3:3:2:0.8:0.5;

[0059] The drying temperature is 55°C, and the drying time is 35 minutes;

[0060] Step 3, ultrasonic cleaning: put the surface of the metal parts obtained after step 2 into clean water for ultrasonic cleaning, and air-dry;

[0061] Among them, the ultrasonic cleaning time is 20min;

[0062] Step 4, polishing: the surface of the metal piece obtained after step 3 is p...

Embodiment 3

[0070] A metal surface polishing process of the present invention is specifically implemented according to the following steps:

[0071] Step 1, pre-cleaning: wash the surface of the metal parts with high pressure, and the washing time is 15 minutes;

[0072] Step 2, degreasing: place the surface of the metal part obtained after step 1 in a cleaning solution for degreasing treatment, and then dry the surface of the metal part;

[0073] The cleaning solution is composed of triethanolamine oleate, sodium bicarbonate, sodium silicate, sodium tripolyphosphate and polyether 2010 with a mass ratio of 4:3:1.5:0.5:0.6;

[0074] The drying temperature is 65°C, and the drying time is 35 minutes;

[0075] Step 3, ultrasonic cleaning: put the surface of the metal parts obtained after step 2 into clean water for ultrasonic cleaning, and air-dry;

[0076] Among them, the ultrasonic cleaning time is 20 minutes;

[0077] Step 4, polishing: put the surface of the metal piece obtained after st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a surface polishing process for a metal part. The surface polishing process is specifically carried out according to the following steps that firstly, the surface of the metalpart is subjected to high pressure washing, is placed in cleaning liquid for degreasing treatment, is dried and is then ultrasonically cleaned; the metal part is then placed into a polishing solutionfor polishing, and pickling, neutralization, rinsing and drying are carried out; and finally, metal anti-rust wax is applied to the surface of the metal part. According to the surface polishing process, an environment-friendly polishing process is adopted, the operation is simple, running cost is low, safety and environmental protection are achieved, the micro-geometry shape of the metal surface can be can improved after polishing, the micro-roughness of the metal surface is reduced, and the gloss of the metal surface is improved.

Description

technical field [0001] The invention belongs to the technical field of metal polishing, and in particular relates to a surface polishing process of a metal piece. Background technique [0002] Metal polishing refers to the use of mechanical, chemical or electrochemical action to reduce the surface roughness of metal workpieces to obtain a bright and smooth surface. Metal polishing is the modification of the surface of metal workpieces using polishing tools and abrasive particles or other polishing media. [0003] Chemical polishing is to achieve a bright and smooth metal surface through regular dissolution. During the chemical polishing process, the passivation oxide film and the oxide film are continuously dissolved on the surface of the metal parts, and the former is stronger than the latter. Due to the microcosmic inconsistency of the surface of the part, the microscopic convex part on the surface dissolves preferentially, and the dissolution rate is greater than that o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23G1/24C23F3/00
CPCC23F3/00C23G1/24
Inventor 宗江伟
Owner 宗江伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap