High-purity corundum powder and preparation method thereof

A technology of corundum and powder, which is applied in the field of high-purity corundum powder and its preparation, which can solve the problems that impurities cannot be removed, impurity cannot be removed, and the time for dissolving impurities is long, so as to achieve low cost, good impurity removal effect and short production cycle.

Inactive Publication Date: 2018-12-28
WUHAN UNIV OF SCI & TECH
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since corundum is difficult to dissolve, impurities embedded in the crystal lattice cannot be removed
[0005] The problems of the above method are: 1. It takes a long time to dissolve impurities; 2. Adding acid, alkali and other solutions to introduce new impurities requires secondary removal; 3. Impurities embedded in the crystal lattice cannot be removed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A high-purity corundum powder and a preparation method thereof. The steps of the technical solution adopted in this embodiment are:

[0029] Step 1: Crushing the corundum block material to a particle size of <50mm, sieving and classifying, to obtain fine crushed material with a particle size of <30mm and a corundum block ball with a particle size of ≥30mm and <50mm.

[0030] Step 2, crushing the finely divided material to a particle size of <8 mm, sieving and classifying, to obtain a primary fine powder with a particle size of <0.09 mm and a granular material I with a particle size of ≥0.09 mm and <8 mm.

[0031] Step 3: Perform magnetic separation for iron removal of the granular material I, and then crush the iron-removed granular material I to a particle size of <3 mm, sieve and classify, and obtain secondary fine powder with a particle size of <0.09 mm and a particle size of ≥ 0.09mm and <3mm pellets II.

[0032] Step 4. Perform magnetic separation on the granules...

Embodiment 2

[0042] A high-purity corundum powder and a preparation method thereof. Except the following situation, all the other are the same as embodiment 1:

[0043] The corundum is white corundum;

[0044] The crushing is pair-roll crushing;

[0045] The classification described in step 4 is hydraulic classification.

Embodiment 3

[0047] A high-purity corundum powder and a preparation method thereof. Except the following situation, all the other are the same as embodiment 1:

[0048] Described corundum is a kind of in plate corundum, sub-white corundum, bauxite corundum and brown corundum;

[0049] The crushing is rolling crushing;

[0050] The classification described in step 4 is wind classification.

[0051] Compared with the prior art, this specific embodiment has the following positive effects:

[0052] 1. In this specific embodiment, it is found through experiments that after the same batch of corundum blocks is broken and ground, the impurities are concentrated in the fine powder, and the fine powder with higher impurity content is directly removed. The impurity effect is good, and the purity of the prepared high-purity corundum powder is greater than 99.8%.

[0053] 2. In this specific embodiment, the homogeneous corundum ball is used as the grinding medium, new impurities will not be introd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-purity corundum powder and a preparation method thereof. According to the technical scheme, a corundum block material is subjected to crushing to obtain corundum blockballs with the particle size of 30-50mm and disentegrated particles with the particle size smaller than 30mm; the disentegrated particles are subjected to crushing, and screening and grading to obtaingranular materials I with the particle size larger than or equal to 0.09mm and smaller than 8mm; the granular materials I are subjected to magnetic separation, iron removal, crushing, screening and grading to obtain granular materials II with the particle size larger than or equal to 0.09mm and smaller than 3mm; the granular materials II are subjected to magnetic separation, iron removal, crushing, screening and grading to obtain granular materials III with the particle size larger than or equal to 0.09mm and smaller than 1mm; the granular materials III and the corundum block balls are subjected to magnetic separation and iron removal correspondingly; the granular materials III after iron removal are mill-grinded by the corundum block balls after iron removal and then subjected to hydraulic grading to obtain one-time purified fine powder with the particle size larger than or equal to 0.04mm and smaller than 0.09mm; and the corundum block balls after magnetic separation and iron removal are used as a grinding medium, grinding and pure-water washing are carried out to obtain the high-purity corundum powder. According to the high-purity corundum powder and the preparation method thereof, the production cycle is short, the cost is low, introduction of new impurities is avoided, and produced products are of high purity.

Description

technical field [0001] The invention belongs to the technical field of corundum powder. Specifically, it relates to a high-purity corundum powder and a preparation method thereof. Background technique [0002] There are two main methods for producing corundum: one is the direct method, that is, the natural bauxite is directly fused or sintered into brown corundum, bauxite, sub-white corundum, etc.; the other is the indirect method, that is, bauxite is used first Mine produces industrial alumina, and then fused or sintered alumina is produced into white corundum, dense corundum, tabular corundum, sintered corundum, etc. Therefore, bauxite is an important raw material for the production of corundum. [0003] The impurities in bauxite are SiO 2 , TiO 2 , Fe 2 O 3 , CaO, MgO, K 2 O and Na 2 O et al. Obviously, the total amount of impurities in the corundum produced by the direct method is higher, and the Na in the corundum produced by the indirect method is relatively h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B02C21/00B02C23/14B02C23/16B03B7/00C01F7/46
CPCB02C21/00B02C23/14B02C23/16B02C2023/165B03B7/00C01F7/46
Inventor 徐建平周双清
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products