Graphene/bacterial cellulose composite material with gradient structure and preparation method

A technology of bacterial cellulose and composite materials, which is applied in the field of graphene/bacterial cellulose composite materials and its preparation, can solve the problems of inability to prepare graphene composite materials with gradient structure and single structure, and achieve the purpose of inhibiting graphene agglomeration, The effect of simple preparation process and easy operation

Active Publication Date: 2022-02-18
EAST CHINA JIAOTONG UNIVERSITY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Considering that the structure of the existing graphene composite materials is relatively simple, which has limitations in simulating complex biological tissues and the development of bionics, the existing technology cannot prepare graphene composite materials with gradient structures.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene/bacterial cellulose composite material with gradient structure and preparation method
  • Graphene/bacterial cellulose composite material with gradient structure and preparation method
  • Graphene/bacterial cellulose composite material with gradient structure and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Example 1. Using graphene dispersion and bacterial cellulose as raw materials, a graphene / bacterial cellulose composite material with a gradient structure was prepared by using a membrane-liquid interface culture method. Specific steps are as follows:

[0027] Step 1. Preparation of medium: Add glucose (25g / L), yeast powder (7.5g / L), peptone (10g / L) and disodium hydrogen phosphate (10g / L) to a beaker containing 1000ml ultrapure water in sequence Stir until it is completely dissolved; use glacial acetic acid to adjust the pH value of the system to 4-5 to prepare a medium, put it in a sterilizer and sterilize it at 115°C and 0.1MPa for 30min to obtain the uninoculated Culture medium, spare;

[0028] Step 2, prepare three kinds of mixed media with different volume ratios:

[0029] Preparation of graphene dispersion: prepare a graphene dispersion with a mass volume concentration of 1 mg / ml in deionized water, sonicate for 15 minutes, and sterilize with ultraviolet light; ...

Embodiment 2

[0034] Example 2. Using graphene dispersion and bacterial cellulose as raw materials, a graphene / bacterial cellulose composite material with a gradient structure was prepared by using a membrane-liquid interface culture method. Specific steps are as follows:

[0035] Step 1, preparation culture medium: with embodiment 1;

[0036] Step 2, prepare three kinds of mixed culture mediums with different volume ratios: the preparation process is basically the same as in Example 1, the difference is only: the graphene dispersion and the culture medium volume ratios prepared in this Example 2 are respectively 1:7, 1: 3 and 2:1 (that is, the concentration of graphene is 0.125mg / ml, 0.25mg / ml, 0.67mg / ml respectively) three kinds of mixed medium; ultrasonic 15min, make the graphene flake particles evenly dispersed in in culture medium;

[0037] Step 3, preparation of basement membrane: same as Example 1;

[0038] Step 4, spray the above-mentioned three kinds of mixed culture mediums wit...

Embodiment 3

[0040] Example 3. Using graphene oxide dispersion liquid and bacterial cellulose as raw materials, a graphene oxide / bacterial cellulose composite material with a gradient structure was prepared by using a membrane-liquid interface culture method. Specific steps are as follows:

[0041] Step 1, preparation culture medium: with embodiment 1;

[0042] Step 2, prepare three kinds of mixed media with different volume ratios: the preparation process is basically the same as in Example 1, the difference is only: the graphene dispersion wherein is a graphene oxide dispersion whose mass volume concentration is 2mg / ml; this implementation In Example 3, the volume ratios of the graphene oxide dispersion to the culture medium were 1:39, 1:7, and 1:3 (that is, the graphene oxide concentrations were 0.05mg / ml, 0.25mg / ml, and 0.5mg / ml, respectively). Mixed medium with three ratios; ultrasonic for 15 minutes, so that the graphene oxide flake particles are evenly dispersed in the medium;

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
breaking strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a graphene / bacterial cellulose composite material with a gradient structure, which adopts a membrane-liquid interface culture method, mainly including preparing a culture medium and preparing a basement membrane used as a membrane-liquid interface for culturing graphene / bacterial cellulose ; Prepare the mixed medium of graphene / uninoculated medium of various volume ratios (concentrations); the concentration of graphene in the mixed medium according to the order of spraying varies from low to high, and the different concentrations are mixed in the form of mist The mixed culture medium of graphene is sprayed on the basement membrane for many times to realize the contact of membrane liquid. Graphene / bacterial cellulose composites with gradient cellulose ratio. The composite material of the invention can provide materials for the preparation of new advanced materials such as bionic biological materials, electromagnetic gradient materials, conductive gradient functional materials and the like.

Description

technical field [0001] The invention relates to a graphene / bacterial cellulose composite material with a gradient structure and a preparation method thereof. Background technique [0002] During long-term evolution and selection, organisms have subtly evolved functional gradients and heterogeneity under the conditions of rather limited elements and compounds to choose from, thus creating high-performance biomaterials. Gradients play an integral role in the survival and development of organisms. For example, natural (bio)materials are often composites with spatial gradients and tunable properties. Natural (bio)materials utilize their gradients to enhance a range of properties and functions, including load-bearing and support capabilities, interfacial strengthening, toughening, and non-mechanical functions. Inspired by biological materials in nature, it is recognized that the introduction of spatial gradients can effectively improve the mechanical and functional properties o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C12P19/04C08L1/04C08K3/04C08K7/24C08K3/38C08K7/00C08J5/18C12R1/02
CPCC12P19/04C08J5/18C08K3/046C08K3/041C08K3/042C08J2301/04C08K7/00C08K2201/011C08K2003/387C08K3/04
Inventor 万怡灶刘金枝张全超杨志伟敖海勇胡剑罗红林崔腾
Owner EAST CHINA JIAOTONG UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com