Processing method for preventing metal layer on surface of plastic product from falling off

A surface metal layer and plastic product technology, applied in the field of plastic products, can solve the problems of low bonding strength, weak, restricted use, etc., and achieve the effect of enhancing surface performance, stable metal layer, and not easy to fall off

Inactive Publication Date: 2019-01-18
嘉兴松尚电器有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these methods all have the disadvantage of insufficient bonding force between the metal layer and the substrate, because the bonding force between the plastic and its surface covering metal layer is very weak, and the bonding strength with the metal covering layer is low. It is easy to peel off, which affects the use effect and seriously restricts its wide use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A processing method for preventing the metal layer on the surface of a plastic product from falling off, comprising the following steps:

[0020] S1, annealing the plastic products;

[0021] S2, degreasing the annealed plastic product;

[0022] S3, destaticizing and dust-removing the degreasing-treated plastic products;

[0023] S4, treating the surface of the plastic product treated in step 3 so that its surface flatness is 1-5mm;

[0024] S5, coating the mixture of bisphenol A epoxy resin and curing agent on the surface of the plastic product treated in step 4 to form a coating layer;

[0025] S6, thermally spraying a metal wire on the surface of the coating layer of the plastic product treated in step 5 to form a metal coating;

[0026] S7, drying the plastic product treated in step 6 to obtain the final product.

[0027] In the step 1, the plastic product is heated to 60°C and kept for 1.5h.

[0028] In the step 2, the plastic product is cleaned with gasoline o...

Embodiment 2

[0031] A processing method for preventing the metal layer on the surface of a plastic product from falling off, comprising the following steps:

[0032] S1, annealing the plastic products;

[0033] S2, degreasing the annealed plastic product;

[0034] S3, destaticizing and dust-removing the degreasing-treated plastic products;

[0035] S4, treating the surface of the plastic product treated in step 3 so that its surface flatness is 1-5 mm;

[0036] S5, coating the mixture of bisphenol A epoxy resin and curing agent on the surface of the plastic product treated in step 4 to form a coating layer;

[0037] S6, thermally spraying a metal wire on the surface of the coating layer of the plastic product treated in step 5 to form a metal coating;

[0038] S7, drying the plastic product treated in step 6 to obtain the final product.

[0039] In the step 1, the plastic product is heated to 70° C. and kept for 3 hours.

[0040] In the step 2, the plastic product is cleaned with gaso...

Embodiment 3

[0043] A processing method for preventing the metal layer on the surface of a plastic product from falling off, comprising the following steps:

[0044] S1, annealing the plastic products;

[0045] S2, degreasing the annealed plastic product;

[0046] S3, destaticizing and dust-removing the degreasing-treated plastic products;

[0047] S4, treating the surface of the plastic product treated in step 3 so that its surface flatness is 1-5 mm;

[0048] S5, coating the mixture of bisphenol A epoxy resin and curing agent on the surface of the plastic product treated in step 4 to form a coating layer;

[0049] S6, thermally spraying a metal wire on the surface of the coating layer of the plastic product treated in step 5 to form a metal coating;

[0050] S7, drying the plastic product treated in step 6 to obtain the final product.

[0051] In the step 1, the plastic product is heated to 65° C. and kept for 2 hours.

[0052] In the step 2, the plastic product is cleaned with gaso...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a processing method for preventing a metal layer on the surface of a plastic product from falling off, belongs to the technical field of plastic products, and in particular relates to a processing method of preventing the metal layer on the surface of the plastic product from falling off. The method comprises the following steps: annealing the plastic product; oiling the annealed plastic product; removing electricity and dust of the deoiled plastic product; treating the surface of the plastic product treated in the step 3, wherein the surface smoothness is 1-5 mm; coating the surface of the plastic product treated in the step 4 with a mixture of bisphenol A epoxy resin and a curing agent to form a coating layer; thermally spraying a metal wire to the surface of thecoating layer of the plastic product treated in the step 5 to form a metal coating; and drying the plastic product treated in the step 6. After treatment, the surface performance, for example, wear resistance, heat resistance, weather resistance, corrosion resistance and the like, of the plastic product is improved greatly.

Description

technical field [0001] The present invention relates to the technical field of plastic products, in particular to a method for surface processing of plastic products. Background technique [0002] Plastic is a class of plastic synthetic polymer materials. Together with synthetic rubber and synthetic fibers, it forms the three major synthetic materials that are indispensable in today's daily life. Specifically, plastic is a material with natural or synthetic resin as the main component, adding various additives, which can be molded into a certain shape under certain temperature and pressure conditions, and maintains the same shape at room temperature. The plastic products industry is the pillar industry of my country's light industry. At present, my country's plastic products industry is facing opportunities for development, but it will also encounter many challenges. This needs to be led by the market and enterprises, and the government is providing policy guidance to move...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C71/00B29C71/02
CPCB29C71/00B29C71/0009B29C71/02B29C2071/022
Inventor 董和英
Owner 嘉兴松尚电器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com