A kind of anti-corrosion mirror back protective coating and preparation method thereof

A protective coating and anti-corrosion technology, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problem of blurred mirror surface, etc., and achieve the effect of large surface tension coefficient, easy operation, excellent waterproof and oil-proof performance

Active Publication Date: 2020-10-23
广东鑫皇冠新材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after using the mirror for a period of time, or even a few months, some light green or black spots will appear on the surface, which can make the entire mirror blurred in severe cases.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-corrosion mirror back protective coating and preparation method thereof
  • A kind of anti-corrosion mirror back protective coating and preparation method thereof
  • A kind of anti-corrosion mirror back protective coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present invention provides a kind of mirror back protective paint with anticorrosion, and by weight percentage, described paint comprises following raw material:

[0022]

[0023] The fluorine-containing acrylic resin is a polymer of perfluoroethylene and fluorine-containing acrylic monomers, wherein the fluorine-containing acrylic monomers are not less than 60% of the total weight of the monomers.

[0024] The modified acrylic resin is a polymer of trifluoropropylene oxide and fluorine-containing acrylic monomer, wherein the fluorine-containing acrylic monomer is not less than 60% of the total weight of the monomers.

[0025] The fluorine-containing acrylic monomer is one or more of trifluoroethyl acrylate and trifluoroethyl methacrylate, that is, the fluorine-containing acrylic monomer is trifluoroethyl acrylate, or trifluoroethyl methacrylate Ethyl ester, or a mixture of trifluoroethyl acrylate and trifluoroethyl methacrylate in any proportion.

[0026] The f...

Embodiment 2

[0033] On the basis of embodiment 1, present embodiment 2 is as a preferred embodiment of the present invention, and a kind of mirror back protection coating with corrosion resistance, by weight percentage, comprises following raw material:

[0034]

[0035]

[0036] Wherein, the filler is prepared from aluminum tripolyphosphate, glass flakes, mica powder and wollastonite in a weight ratio of 12:10:7:6; , N-methylpyrrolidone and ethanol are prepared by mixing in a weight ratio of 20:21:22:29; the preparation method of the mirror back protective coating is the same as in Example 1.

Embodiment 3

[0038] On the basis of embodiment 2, present embodiment 3 is as a preferred embodiment of the present invention, and a kind of mirror back protection paint with corrosion resistance, by weight percentage, comprises following raw material:

[0039]

[0040] Wherein, the preparation method of the mirror back protective coating is the same as that in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anticorrosive mirror back protecting coating and a preparation method thereof, and relates to the field of mirror back protecting coatings. The coating comprises the following raw materials in percent by weight: 15-25% of fluorine-containing acrylic resin, 10-25% of modified acrylic resin, 0-15% of fillers, 2-15% of a pigment, 0-10% of an auxiliary agent and 15-45 % of asolvent. Through the use of the fluorine-containing acrylic resin and the modified acrylic resin as main film-forming substances, the anticorrosive mirror back protecting coating has a high film-forming speed, excellent corrosion resistance, acid and alkali resistance and water resistance, can be applied to shower coating, spray coating or roll coating, adopts a simple and easily operated coatingprocess, and has a good coating effect.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to an anti-corrosion mirror back protection coating and a preparation method thereof. Background technique [0002] Mirrors used in daily life, such as mirrors on furniture, mirrors hung in shops and living rooms, people always hope to use them for a long time to keep the mirror surface bright and clear forever. However, when the mirror is used for a period of time, or even a few months, some light green or black spots will appear on the surface, and in severe cases, the entire mirror surface will be blurred. [0003] Mirrors are divided into silver mirrors and aluminum mirrors, which are composed of three parts: flat glass, metal reflective layer (silver layer or aluminum layer) and mirror back paint. The blurred mirror surface of the mirror is mainly the result of the hot and humid environment in the rainy season first destroying the mirror back coating and then destroying the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/16C09D5/08C09D7/61
CPCC08K2003/327C08K2201/014C08L2205/025C09D5/08C09D133/16C09D7/61C08L33/16C08K3/00C08K3/32C08K3/40C08K3/34
Inventor 谭贺洵汪洋张明远