Treatment process for wear-resistant material of liquid wear-resistant paper

A technology of liquid wear-resistant paper and wear-resistant material, applied in the field of wear-resistant materials, can solve the problems of unstable wear resistance, unstable coupling agent, white spot of liquid wear-resistant paper, etc. Reduce small white spots, strong binding effect

Active Publication Date: 2019-02-15
山东爱格装饰材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this method, due to the instability of the coupling agent during the treatment process, it is easy to cause white spots on the liquid wear-resistant paper, and the wear resistance is unstable, which eventually leads to a high scrap rate of the finished product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The process for treating wear-resistant materials for liquid wear-resistant paper includes the following steps:

[0024] (1) Configuration of treatment liquid:

[0025] Add ethanol to the silane coupling agent KH570, stir evenly to obtain a silane coupling agent alcohol solution with a mass fraction of 18-25%, and continue to add 0.5-1% of the total mass of the silane coupling agent alcohol solution to this solution. melamine formaldehyde prepolymer with a content of 10-15%, after stirring for 20-40 minutes, adjust the pH of the solution to 7-8 with an oxalic acid solution with a mass fraction of 10%;

[0026] (2) Treatment liquid treatment of wear-resistant materials:

[0027] Put the 180-mesh corundum powder into the mixing tank, spray the treatment liquid into the corundum powder while stirring, continue stirring for 15-30 minutes after the treatment liquid is sprayed, and then dry it into the corundum powder at no higher than 100°C The water content is between 3% ...

Embodiment 2

[0029] The process for treating wear-resistant materials for liquid wear-resistant paper includes the following steps:

[0030] (1) Configuration of treatment liquid:

[0031] Add ethanol to the silane coupling agent KH550, stir evenly to obtain a silane coupling agent alcohol solution with a mass fraction of 18-25%, and continue to add 0.5-1% of the total mass of the silane coupling agent alcohol solution to this solution. melamine formaldehyde prepolymer with a content of 10-15%, after stirring for 20-40 minutes, adjust the pH of the solution to 7-8 with an oxalic acid solution with a mass fraction of 10%;

[0032] (2) Treatment liquid treatment of wear-resistant materials:

[0033] Put 220 mesh corundum powder into the mixing tank, spray the treatment liquid into the corundum powder while stirring, continue stirring for 15-30 minutes after the treatment liquid is sprayed, and then dry it into the corundum powder at no higher than 100°C The water content is between 3% and ...

Embodiment 3

[0035] The process for treating wear-resistant materials for liquid wear-resistant paper includes the following steps:

[0036] (1) Configuration of treatment liquid:

[0037] Add ethanol to the silane coupling agent KH590, stir evenly to obtain a silane coupling agent alcohol solution with a mass fraction of 18-25%, and continue to add 0.5-1% of the total mass of the silane coupling agent alcohol solution to this solution. melamine formaldehyde prepolymer with a content of 10-15%, after stirring for 20-40 minutes, adjust the pH of the solution to 7-8 with an oxalic acid solution with a mass fraction of 10%;

[0038] (2) Treatment liquid treatment of wear-resistant materials:

[0039] Put 240 mesh corundum powder into the mixing tank, spray the treatment liquid into the corundum powder while stirring, continue stirring for 15-30 minutes after the treatment liquid is sprayed, and then dry it into the corundum powder at no higher than 100°C The water content is between 3% and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a treatment process for a wear-resistant material of liquid wear-resistant paper, belongs to the technical field of wear-resistant materials, and solves the problems that the wear-resistant material treated by the existing treatment process is unstable in wear resistance and white points are easily produced in a production process. The treatment process comprises the following steps: (1) preparing a treatment liquid, namely, adding ethyl alcohol into a silane coupling agent, stirring uniformly to obtain a silane coupling agent alcohol solution, continuing adding a melamine formaldehyde prepolymer with the solid content of 10 to 15 percent into the solution, stirring for 20 to 40 minutes, and regulating the PH to be neutral with an oxalic acid solution; and (2) treating the wear-resistant material with the treatment liquid, namely, adding alundum powder into a stirring tank, spraying the treatment liquid into the alundum powder while stirring, continuing stirringfor 15 to 30 minutes after the treatment liquid is sprayed, and drying the alundum powder at the temperature of not lower than 100 DEG C until the water content in the alundum powder is between 3 to5 percent. The treatment process can be used for treating the wear-resistant material of the liquid wear-resistant paper.

Description

technical field [0001] The invention relates to a treatment process for wear-resistant materials used in liquid wear-resistant paper, and belongs to the technical field of wear-resistant materials. Background technique [0002] The wear-resistant paper is impregnated with melamine and additives, and the board is hot-pressed by the steel plate of the hot press to become a veneer board, which is widely used in the veneer of cabinets, wardrobes, and Bell laminate flooring. [0003] Due to the poor compatibility between inorganic corundum powder and melamine resin, wear-resistant materials generally need to be treated before use. The existing technology is to directly spray silane coupling agent on the filler and stir in a mixer for 10-30 minutes. Dry after filling treatment. In this method, due to the instability of the coupling agent during the treatment process, it is easy to cause white spots on the liquid wear-resistant paper, and the wear resistance is unstable, which eve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/00D21H19/14D21H17/69
CPCD21H17/69D21H19/14D21H27/00
Inventor 吉军梁付明钟欢云李支栋邹波刘高峰
Owner 山东爱格装饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com