Light-permeable green brick and manufacturing method thereof

A production method and technology for light-transmitting bricks, which are applied in the field of building ceramic materials and processes, can solve the problems of low strength, poor powder plasticity, and difficulty in forming blanks, and achieve the effect of improving hardness

Active Publication Date: 2019-03-01
GUANGDONG BODE FINE IND CONSTR MATERIAL
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are also some manufacturers who have developed formulas for light-transmitting ceramic tiles. These formulas have good performance in terms of light transmission, but some of these formulas have poor powder plasticity, difficulty in forming green bodies and low strength.
Therefore, light-transmitting bricks have not been mass-produced so far

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] Example 1 A light-transmitting brick body

[0063] The light-transmitting brick body is prepared from the following raw materials calculated by mass percentage: 80% light-transmitting blank clinker, 19% clay, 0.1% binder, 0.9% colorant, and the sum of the mass percentages of the above components is 100%; the binder is carboxymethyl cellulose, and the colorant is ceramic pigment yellow; the light-transmitting blank frit is prepared from the following raw materials in parts by weight: 35 parts of potassium feldspar, albite 26 parts, 12 parts of dolomite, 2 parts of alumina, 1 part of barium carbonate, 3 parts of soda ash.

Embodiment 2

[0064] Example 2 A light-transmitting brick body

[0065] The light-transmitting brick body is prepared from the following raw materials calculated by mass percentage: 82% light-transmitting blank clinker, 16% clay, 1% binder, 1% colorant, and the mass percentage of the above components The sum is 100%; the binder is polyvinyl alcohol, and the colorant is ceramic pigment red; the light-transmitting blank frit is prepared from the following raw materials in parts by weight: 40 parts of potassium feldspar, 30 parts of albite 16 parts of dolomite, 5 parts of alumina, 3 parts of barium carbonate, and 6 parts of soda ash.

Embodiment 3

[0066] Example 3 A light-transmitting brick body

[0067] The light-transmitting brick body is prepared from the following raw materials calculated by mass percentage: 85% light-transmitting blank clinker, 12% clay, 1.5% binder, 1.5% colorant, and the sum of the mass percentages of the above components is 100%; the binder is carboxymethyl cellulose, and the colorant is ceramic pigment blue; the light-transmitting blank frit is prepared from the following raw materials in parts by weight: 39 parts of potassium feldspar, sodium feldspar 30 parts of limestone, 16 parts of dolomite, 6 parts of alumina, 3 parts of barium carbonate, and 6 parts of soda ash.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a light-permeable green brick and a manufacturing method thereof. The light-permeable green brick is prepared from the following raw materials by weight percent: 80-90% of light-permeable blank frit, 8-20% of clay, 0.1-3% of binder and 0-4% of colorant; the sum of weight percent of the raw materials is 100%; the light-permeable blank frit is prepared from the following rawmaterials in parts by weight: 35-45 parts of potassium feldspar, 26-34 parts of albite, 12-18 parts of dolomite, 2-8 parts of aluminum oxide, 1-7 parts of barium carbonate and 3-9 parts of sodium carbonate. Through the improvement for the formula of light-permeable green brick according to the invention, the light-permeable green brick has a transparent texture and a light-transmitting function; after the light-permeable green brick is combined with clay and binder, hardness and abrasion resistance of the light-permeable green brick are greatly promoted; the hardness of light-permeable green brick can reach up to Moh's hardness at level 5.5.

Description

technical field [0001] The invention relates to a building ceramic material and technology, in particular to a light-transmitting brick body and a manufacturing method thereof. Background technique [0002] As a kind of building decoration material, ceramic tile has the characteristics of wear-resistant waterproof and beautiful surface pattern, and is deeply loved by people. It is widely used in home decoration, office decoration and commercial decoration. With the development of people's needs and markets, people continue to put forward new requirements for the functions of ceramic tiles. [0003] In order to meet the needs of the market and improve the decorative effect of ceramic tiles, ceramic tiles with a certain degree of light transmission (hereinafter referred to as light-transmitting tiles) can produce transparent and changing effects under the action of light, which has become a hot spot for research and development by major ceramic manufacturers. . There are als...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/19C04B35/622C04B35/626
CPCC04B35/19C04B35/622C04B35/62665C04B2235/3201C04B2235/321C04B2235/3215C04B2235/3217C04B2235/349C04B2235/656C04B2235/6567C04B2235/9653
Inventor 叶竞通
Owner GUANGDONG BODE FINE IND CONSTR MATERIAL
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com