Tree moss soft pseudo-carbonized fermented granules and preparation method and application thereof

A particle and tree moss technology is applied in the field of cigarette material preparation, which can solve the problems of inability to directly flavor cigarettes with harmonization of aroma, poor adsorption effect, and insignificant adsorption effect of adsorbing material particles, achieves good application value, improves aroma and reduces coke, the effect of convenient industrial production

Inactive Publication Date: 2019-03-12
CHINA TOBACCO YUNNAN IND
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the disadvantages of the existing plant particles, such as the insignificant adsorption effect of harmful substances in smoke, the inability to directly add fragrance to the adsorption material particles, and the poor coordination of cigarette aroma, the present invention provides a method that can enhance Moss soft pseudo-carbonized fermented granules that can reduce harm and reduce tar, reduce the irritation of cigarette smoke, enhance the aroma effect, and significantly improve the sweetness, and the preparation method thereof, and use the granules in cigarette tip sticks, The special burnt aroma of the moss itself can still be retained

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tree moss soft pseudo-carbonized fermented granules and preparation method and application thereof
  • Tree moss soft pseudo-carbonized fermented granules and preparation method and application thereof
  • Tree moss soft pseudo-carbonized fermented granules and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] 1. Soft carbonization of tree moss

[0036] Put the moss into the carbonization furnace, gradually raise the furnace temperature to about 80°C, and keep it for 40 minutes. After the moss is dry, quickly raise the temperature to 120°C, and keep it for 3 hours. Turn off the heat source, and take out the soft carbonized sample of the moss for use. Generally, the raw material turns taupe, and the carbonization is completed when the weight is 50-80% of that before the carbonization.

[0037] 2. Cultivation of Bacillus subtilis Van3 (B.subtilisVan3)

[0038] A. Test tube slant culture

[0039]A Luria-Bertani (LB) medium was used, and the formula was: 10 g of peptone, 10 g of sodium chloride, 5 g of yeast extract, 20 g of agar, and distilled water to a volume of 1000 ml. Sterilize at 121°C for 25 minutes and place on a slope. Inoculate Van35, incubate at 28°C for 24 hours to obtain test tube seeds, transfer the liquid strains to 1L of LB liquid medium according to the inocu...

Embodiment 2

[0045] 1. Soft carbonization of tree moss

[0046] Put the moss into the carbonization furnace, gradually raise the furnace temperature to 80°C, and keep it for 30 minutes. After the moss is dry, quickly raise the temperature to 140°C, and keep it for 2.5 hours.

[0047] 2. Cultivation of Bacillus subtilis Van3

[0048] B. Seed culture

[0049] A Luria-Bertani (LB) medium was used, and the formula was: 10 g of peptone, 10 g of sodium chloride, 5 g of yeast extract, and distilled water to a volume of 1000 ml. Sterilize at 121°C for 25 minutes. Inoculate Van35 test tube species, cultivate at 28°C for 24h to obtain liquid strains, transfer the liquid strains to 1L of LB liquid medium at 5% (volume percentage of liquid strains, v / v), 37°C, 150r Centrifuge the culture solution at 3500 r / min for 10 min, wash the precipitate with sterile water, centrifuge, and finally shake evenly with 20 mL of sterile water, and dilute it 10 times before use, which is the Bacillus subtilis Van3. ...

Embodiment 3

[0054] Example 3: Moss Soft Pseudo-Carbonization Fermentation Granules Applied in Cigarette Filter Sticks

[0055] The moss flexible pseudo-carbonization fermentation granules obtained in Example 1 are applied to cigarette composite cigarette filter sticks, and 1.5 mg of granular material is added per millimeter of standard cigarette filter sticks to prepare experimental cigarettes, which are named No. 1 cigarettes; Cigarettes without the above-mentioned particles were used as the control sample, and the moisture content of the cigarette samples was adjusted to 12wt% according to the national standard "GB / T16447-1996 Atmospheric Environment for the Regulation and Testing of Tobacco and Tobacco Products", and the smoking expert group was evaluated according to "GB5606.4- 1996 Cigarette Sensory Technical Requirements" to carry out sensory evaluation of cigarettes and detection of harmful components in smoke. See Table 1 for the evaluation results; see Table 2 and Table 3 for spe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses tree moss soft pseudo-carbonized fermented granules. The granules are obtained by adopting tree moss as a raw material, performing heating soft pseudo-carbonization treatment on the raw material, fermenting the raw material through bacillus subtilis Van3, pulverizing an intermediate product after fermentation into powder with the particle size of 100-180 mesh, and adoptingan adhesive for bonding the power into the granules, namely the tree moss soft pseudo-carbonized fermented granules, with the particle size of 20-60 mesh. The invention also discloses a preparation method of the tree moss soft pseudo-carbonized fermented granules and application of the granules in cigarette filter tips. The tree moss soft pseudo-carbonized fermented granules can selectively adsorbharmful substances of cigarette smoke while retaining a special coke aroma of the tree moss.

Description

technical field [0001] The invention relates to the technical field of cigarette material preparation, in particular to a soft pseudo-carbonized fermented granule of tree moss, a preparation method thereof and an application for cigarette tip rods. Background technique [0002] Low coking has become an inevitable trend in the development of the tobacco industry. Low coking brings about a reduction in the taste of cigarettes, and insufficient aroma has gradually become a prominent problem in the development of tobacco. How to overcome the key technologies that affect the aroma and aroma of tobacco leaves has become the core of improving the competitiveness of cigarette production. Adding tobacco flavors and fragrances to shredded cigarettes is a conventional and necessary technical means to add aroma, but the space for improving the quality of cigarettes is relatively limited. It has become a new development trend to improve the aroma and aroma of cigarettes and reduce the i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A24B15/28A24B3/12
CPCA24B15/28A24B3/12
Inventor 张玲张伟杨建云韦克毅汤丹瑜张天栋段焰青赵英良李娟蔡波李源栋唐石云
Owner CHINA TOBACCO YUNNAN IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com