Long-service-life iron runner castable for hot repair

A iron channel castable and hot repair technology, which is applied in the field of iron channel castables, can solve the problems of gas mismatch of metal aluminum powder, etc., achieve excellent high-temperature performance, increase density, and ensure high-temperature performance

Active Publication Date: 2019-03-15
中冶武汉冶金建筑研究院有限公司
View PDF7 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a long-life iron channel castable for hot repair, which solves the problem of possible mismatch between cement solidification and metal aluminum powder gas generation, and effectively improves the service life of the iron channel castable for hot repair by comprehensively optimizing the ratio

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Long-service-life iron runner castable for hot repair
  • Long-service-life iron runner castable for hot repair
  • Long-service-life iron runner castable for hot repair

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A long-life heat repair castable for iron ditch, the components and their mass percentages are: brown corundum 56%; silicon carbide 13%; ball pitch 2.4%; pure calcium aluminate cement 2.5%; alumina micropowder 10.905%; silicon dioxide powder 1.5%; silicon carbide powder 11%; composite antioxidant 2%; metal aluminum powder 0.3%, explosion-proof fiber 0.075; dispersant 0.3%; The raw materials were weighed according to the above proportions and fully mixed; then water was added (the mass of water was 4.1% of the total mass of each raw material) and stirred evenly, and then vibrated and formed; The heat treatment was carried out for 24 hours, and the iron trough castable sample for long-life hot repair was prepared.

[0040] The performance test of the iron channel castable sample for long-life hot repair prepared in this embodiment is performed, and the results are shown in Table 1. The performance testing method adopted is carried out in accordance with the current natio...

Embodiment 2

[0044]A castable for long-life hot repairing iron trench, the components and their mass percentages are: brown corundum 64%; silicon carbide 5%; ball asphalt 2%; pure calcium aluminate cement 1.5%; alumina micropowder 12%; silicon dioxide powder 1.77%; silicon carbide powder 12%; composite antioxidant 1%; metal aluminum powder 0.2%, explosion-proof fiber 0.05%; dispersant 0.4%; coagulant 0.08%. The raw materials were weighed according to the above proportions and fully mixed; then water was added (the mass of water was 3.9% of the total mass of each raw material) and stirred evenly, and then vibrated and formed; after forming, the obtained samples were dried naturally for 24 hours and then reheated at 110°C. The heat treatment was carried out for 24 hours, and the iron trough castable sample for long-life hot repair was prepared.

[0045] The performance test of the iron channel castable sample for long-life hot repair prepared in this embodiment is performed, and the results ...

Embodiment 3

[0049] A long-life heat repair castable for iron ditch, the components and their mass percentages are: brown corundum 60%; silicon carbide 0-1mm: 9%; ball pitch 2.5%; pure calcium aluminate cement 2% 10% of alumina micropowder; 2% of silica micropowder; 13% of silicon carbide powder; 1.06% of composite antioxidant; 0.1% of metal aluminum powder, 0.1% of explosion-proof fiber; Weigh and mix each raw material according to the above ratio; then add water (the mass of water is 4% of the total mass of each raw material) and stir evenly, then vibrate and shape; after forming, the sample obtained is dried naturally for 24 hours and then reheated at 110°C. The heat treatment was carried out for 24 hours, and the iron trough castable sample for long-life hot repair was prepared.

[0050] The performance test of the iron channel castable sample for long-life hot repair prepared in this embodiment is performed, and the results are shown in Table 3. The performance testing method adopted...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a long-service-life iron runner castable for hot repair. The long-service-life iron runner castable for hot repair comprises the following components in percentage by mass: 56%-64% of brown fused alumina, 5%-13% of silicon carbide, 2%-3% of ball pitch, 1.5%-2.5% of calcium aluminate cement, 8%-12% of alumina micro-powder, 1.5%-2.5% of silicon dioxide micro-powder, 11%-13% of silicon carbide powder, 1%-2% of a composite antioxidant, 0.1%-0.3% of metal aluminum powder, less than 0.1% of explosion-proof fibers, 0.2%-0.4% of a dispersing agent and 0.08% of a coagulant. Thenovel coagulant is used for the iron runner castable, thus, the metal aluminum powder in the iron runner castable produces hydrogen ahead of time, the gas is generated to open an exhaust hole when thecastable is not cured, then, the castable is matched with the suitable metal aluminum powder and the low-melting-point explosion-proof fibers, and it ensures that the castable has excellent high-temperature usability while meeting the condition of construction.

Description

technical field [0001] The invention belongs to the technical field of composite materials, and in particular relates to an iron ditch castable. Background technique [0002] In the past two years, with the continuous rise of steel prices, various iron and steel enterprises have emphasized high production and smooth production in order to seize production and strengthen smelting. Iron trenches are an important part of the ironmaking process. The extension of the fixed repair cycle of iron trenches is extremely important to steel companies. meaning. How to ensure the service life of the iron trench materials and prolong the regular repair cycle of the blast furnace under the premise of ensuring safe use is one of the primary survival conditions for the iron trench contracting enterprises. Especially for a large number of single taphole blast furnaces and 1000 cubic blast furnaces in China, the time available for pouring construction of iron trenches is seriously insufficient...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/103C04B35/63C04B38/02
CPCC04B35/103C04B35/6303C04B38/02C04B2235/3208C04B2235/3222C04B2235/3418C04B2235/3821C04B2235/3826C04B2235/402C04B2235/428C04B2235/5212C04B2235/5427C04B2235/5436
Inventor 魏建修邵荣丹
Owner 中冶武汉冶金建筑研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap