New energy vehicle charging gun shell material and preparation method thereof

A new energy vehicle and shell material technology, applied in the field of new energy vehicle charging gun shell material and its preparation, can solve the problems of not meeting the comprehensive performance index, not meeting the use requirements, not being scratch-resistant, etc., and achieving mechanical Good performance, good low temperature notched impact performance, effect of improving scratch resistance

Inactive Publication Date: 2019-03-22
中广核高新核材科技(苏州)有限公司
View PDF11 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The material has good low-temperature notched impact strength and flame retardancy, but the material is not scratch-resistant, and it is easy to be scratched and replaced during the trial process. It cannot meet the requirements for the use of charging gun shell materials in harsh environments.
[0008] However, the modified polycarbonate involved in the prior art can only meet part of the use requirements of the charging gun shell, but fails to meet the performance indicators comprehensively. How to overcome the above technical problems has become the direction of efforts of ordinary technicians in the art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1~4

[0034] Examples 1 to 4: a tear-resistant oil-resistant halogen-free flame retardant sheath material for charging pile cables, the new energy vehicle charging gun shell material is composed of the following components by weight, as shown in Table 1 :

[0035]

[0036] ;

Embodiment 1

[0037] The compatibilizer of Example 1 is selected from maleic anhydride grafted polyolefin elastomer (POE-G-MAH); the antioxidant is tetrakis[beta-(3,5-di-tert-butyl-4-hydroxybenzene) base) propionic acid] pentaerythritol ester; the light stabilizer is a salicylic acid ester; the flame retardant is a phosphorus-based flame retardant.

Embodiment 2

[0038] The compatibilizer of Example 2 is maleic anhydride grafted SEBS (SEBS-G-MAH); the antioxidant is tris(2,4-di-tert-butylphenyl) phosphite; the light stabilizer It is a mixture of salicylates and benzoates; the flame retardant is selected from aromatic sulfonates.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
oxygen indexaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to view more

Abstract

The invention relates to a new energy vehicle charging gun shell material and a preparation method thereof. The new energy vehicle charging gun shell material consists of the following components in parts by weight: 60 to 90 parts of a polycarbonate resin base material, 10 to 80 parts of silicified polycarbonate resin, 5 to 12 parts of an acrylic ester impact modifier, 6 to 25 parts of a methyl methacrylate-styrene copolymer, 4 to 8 parts of nano-silica, 1 to 5 parts of a compatilizer, 0.2 to 2 parts of pentaerythritol tetraisostearate, 0.2 to 2 parts of silicone powder, 0.5 to 2 parts of an antioxidant, 0.2 to 0.6 part of a light stabilizer, 0.3 to 1 part of bis(2,dimethylaminoethyl)ether, 0.1 to 0.5 part of n-octyltrichlorosilane, 0.2 to 0.4 part of a flame retardant and 0.5 to 2 parts of polytetrafluoroethylene powder. The charging gun shell material disclosed by the invention has high impact resistance, high wear and scratch resistance (pencil hardness grade 3H), heat and ultraviolet light resistance, flame retardance UL94-V0 (1.5 mm), glow wire test (850 DEG C, 1 mm) and the oxygen index of 38 at a normal temperature (23 DEG C) and low temperatures (negative 30 DEG C and negative 50 DEG C).

Description

technical field [0001] The invention relates to the field of car charging gun shell materials, in particular to a new energy car charging gun shell material and a preparation method thereof. Background technique [0002] As an important part of electric vehicle charging facilities, the performance of the charging gun has an important impact on the entire charging process. However, as a new type of charging facility, the use environment of the charging gun is different from the traditional charging environment. It not only needs to have the reliability and safety of the charging gun that will not be affected by various harsh natural environments for a long time, but also need to have the ability to prevent the charging gun from being damaged by frequent man-made fading, scratches, dragging and even car rolling. It will cause mechanical and electrical damage, which will bring safety hazards to users, and will not be reduced due to the long charging and discharging process tim...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L27/18C08L33/12C08K13/02C08K3/36C08K5/103C08K5/5419C08K5/17
CPCC08K2201/011C08L69/00C08L2201/02C08L2201/08C08L2203/20C08L2205/025C08L2205/035C08L27/18C08L33/12C08K13/02C08K3/36C08K5/103C08K5/5419C08K5/17
Inventor 廖永江何晓东单永东翁伟
Owner 中广核高新核材科技(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products