Shell activated carbon descaling ceramic material and preparation method thereof

A technology of ceramic materials and activated carbon, applied in the field of ceramic materials, can solve the problems of inability to adsorb harmful substances for a long time, easy scaling of the inner liner, poor adsorption of impurities in water, etc., and achieve the effect of protecting the health of family members and long service life.

Inactive Publication Date: 2019-03-26
杭州钰山津环保科技有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The liner made of existing ceramic materials has poor adsorption to impurities in water and cannot absorb harmful substances for a long time, and the liner is easy to scale when heated, and long-term use is not conducive to health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A ceramic material for descaling by shell activated carbon, the raw materials of which are as follows in parts by weight: 10 parts of shell powder, 7 parts of phosphate rock, 10 parts of zeolite, 20 parts of pottery clay, 8 parts of silicon ore, 6 parts of meteorite, and 10 parts of activated carbon , 9 parts of selenium mineral earth, 8 parts of diatomaceous earth.

[0022] Specifically, the preparation method of the shell powder is as follows: wash the shells and soak them in 0.1% hydrochloric acid solution for 40 minutes, take them out and drain them, then calcinate them at 1000°C for 1 hour, wash them with deionized water, dry them, and use planetary Grinding and pulverizing with a type ball mill, and finally sifting to obtain shell powder.

[0023] Specifically, the shell powder is any one of pearl shell, abalone shell or oyster shell, the shell powder.

[0024] Specifically, the mesh size of the sieve used for sieving is 200.

[0025] A preparation method of a s...

Embodiment 2

[0030] A ceramic material for descaling by shell activated carbon, the raw materials are as follows by weight: 15 parts of shell powder, 12 parts of phosphate rock, 15 parts of zeolite, 25 parts of pottery clay, 12 parts of silicon ore, 15 parts of meteorite, and 15 parts of activated carbon , 12 parts of selenium mineral earth, 15 parts of diatomaceous earth.

[0031] Specifically, the preparation method of the shell powder is as follows: wash the shells and soak them in 0.3% hydrochloric acid solution for 30 minutes, take them out and drain them, then calcinate them at 1000°C for 2 hours, wash them with deionized water, dry them, and use planetary Grinding and pulverizing with a type ball mill, and finally sifting to obtain shell powder.

[0032] Specifically, the shell powder is any one of pearl shell, abalone shell or oyster shell, the shell powder.

[0033] Specifically, the mesh size of the sieve used for sieving is 180.

[0034] A preparation method of a shell activat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a shell activated carbon descaling ceramic material which comprises the following raw materials in parts by weight: 10-15 parts of shell powder, 7-12 parts of phosphate ore, 10-15 parts of zeolite, 20-25 parts of argil, 8-12 parts of silicon ore, 6-15 parts of stone needle, 10-15 parts of activated carbon, 9-12 parts of selenium ore and 8-15 parts of kieselguhr. According to the invention, shell powder and activated carbon are added; smashed shell powder and activated carbon are added as raw materials into a ceramic liner, so that the shell powder has an absorbing function, is free from saturability, is long in service life, can absorb hazardous substances for a long time and can protect health of families; the added phosphate ore and silicon ore can stabilize various carbonates in water, can convert water-insoluble calcium carbonate into water-soluble calcium hydrophosphate and can keep the water-soluble calcium hydrophosphate stable under heating state, so asto achieve the purpose of controlling scaling; a liner made from the ceramic material has the functions of healthcare, sterilization, absorption, water purification and scaling prevention.

Description

technical field [0001] The invention relates to the technical field of ceramic materials, in particular to a ceramic material for shell activated carbon descaling and a preparation method thereof. Background technique [0002] Common ceramic materials are clay, alumina, kaolin and so on. Ceramic materials generally have higher hardness, but poor plasticity. Ceramic materials are mostly used in tableware and decoration. [0003] The liner made of existing ceramic materials has poor adsorption to impurities in water, cannot absorb harmful substances for a long time, and the liner is easy to scale when heated, and long-term use is not conducive to health. Contents of the invention [0004] The object of the present invention is to solve the shortcomings in the prior art, and propose a ceramic material for descaling shell activated carbon and a preparation method thereof. [0005] In order to achieve the above object, the present invention adopts the following technical sol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/626C04B33/04C04B33/13C04B33/132
CPCC04B33/04C04B33/13C04B33/131C04B33/132C04B35/62675C04B2235/5436C04B2235/5427Y02P40/60
Inventor 陈旭亚
Owner 杭州钰山津环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More