A kind of pickleball rotational molding polyethylene-polyolefin elastomer composite material and preparation method thereof

A technology of polyolefin elastomer and rotomolding, which is applied in the field of pickleball rotomolding polyethylene-polyolefin elastomer composite materials, which can solve the problems of deformation, pickleball's poor impact resistance and inability to rebound, etc. Achieve the effects of simple preparation method, industrialized operation and good elasticity

Active Publication Date: 2022-01-18
ZHEJIANG ROTOUN PLASTIC TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The impact resistance of the pickleball on the market has not been very good. It begins to deform after being hit less than 2000 times and cannot bounce back.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Take polyethylene (density 0.917g / cm 3 , melt flow rate [190°C, 2.16Kg] is 1.82g / 10min), polyolefin elastomer elastomer (density 0.902g / cm 3 , melt flow rate is 23.06g / 10min), antioxidant AT10, antioxidant AT168, ultraviolet absorber UV-531, according to the total mass parts is 100 parts, the mass ratio of each raw material component is polyethylene: polyolefin Elastomer Elastomer: Antioxidant AT10: Antioxidant AT168: Ultraviolet Absorber UV-531=89.68:9.97:0.05:0.10:0.20.

[0030] Add polyethylene, polyolefin elastomer elasticity, antioxidant AT10, antioxidant AT168, and ultraviolet absorber UV-531 into the mixer, and the mixing time is 4 minutes; melt and blend the mixed materials with a twin-screw extruder, extrude Pelletization and extrusion process parameters: melt temperature is 185°C, screw speed is 280rpm; finally, the granulated particles are ground with a plastic mill, milling process parameters: grinding plate temperature is 75°C, grinding plate speed is 2800...

Embodiment 2

[0033] Take polyethylene (density 0.917g / cm 3 , melt flow rate [190°C, 2.16Kg] is 1.82g / 10min), polyolefin elastomer elastomer (density 0.902g / cm 3 , melt flow rate is 23.06g / 10min), antioxidant AT10, antioxidant AT168, ultraviolet absorber UV-531, according to the total mass parts is 100 parts, the mass ratio of each raw material component is polyethylene: polyolefin Elastomer Elastomer: Antioxidant AT10: Antioxidant AT168: Ultraviolet Absorber UV-531=79.72:19.93:0.05:0.10:0.20.

[0034] Add polyethylene, polyolefin elastomer elasticity, antioxidant AT10, antioxidant AT168, and ultraviolet absorber UV-531 into the mixer, and the mixing time is 3 minutes; melt and blend the mixed materials with a twin-screw extruder, extrude Pelletization and extrusion process parameters: melt temperature is 200°C, screw speed is 350rpm; finally, the granulated particles are ground with a plastic mill, milling process parameters: grinding plate temperature is 75°C, grinding plate speed is 280...

Embodiment 3

[0037] Take polyethylene (density 0.917g / cm 3 , melt flow rate [190°C, 2.16Kg] is 1.82g / 10min), polyolefin elastomer elastomer (density 0.902g / cm 3 , melt flow rate is 23.06g / 10min), antioxidant AT10, antioxidant AT168, ultraviolet absorber UV-531, according to the total mass parts is 100 parts, the mass ratio of each raw material component is polyethylene: polyolefin Elastomer Elastomer: Antioxidant AT10: Antioxidant AT168: Ultraviolet Absorber UV-531=69.76:29.90:0.05:0.10:0.28.

[0038] Add polyethylene, polyolefin elastomer elasticity, antioxidant AT10, antioxidant AT168, and ultraviolet absorber UV-531 into the mixer, and the mixing time is 5 minutes; melt and blend the mixed materials with a twin-screw extruder, extrude Granulation and extrusion process parameters: melt temperature is 205°C, screw speed is 420rpm; finally, the granulated particles are ground with a plastic mill, milling process parameters: grinding plate temperature is 75°C, grinding plate speed is 2800r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a pickleball rotationally molded polyethylene composite material and a preparation method thereof, in particular to a pickleball rotationally molded polyethylene composite material. The raw material formula is: 38.34‑93.5% polyethylene, 6.28‑93.5% polyolefin elastomer 60.4%, 0.12-0.66% of antioxidant and 0.10-0.60% of anti-ultraviolet agent, and then through mixing, melt blending, extrusion granulation and milling to obtain the pickle ball rotationally molded polyethylene composite material. A method for preparing the material is also provided. The polyethylene composite material for rotational molding of the pickleball obtained by the invention can be used for rotational molding of the pickleball, and the pickleball can resist hitting for 3000 times.

Description

technical field [0001] The invention relates to a polyethylene-polyolefin elastomer composite material for rotomolding a pickleball, in particular to a polyethylene material which is resistant to hitting a pickleball for 3000 times and is suitable for a rotomolding production process and a preparation method thereof. [0002] technical background [0003] Rotational molding is a plastic processing method that uses a rotating mold for processing. The processing process is to put plastic powder or slurry into the mold, and the closed mold is rotated or shaken on the equipment, and the mold is heated by an open flame or hot air. External heating, the plastic powder or slurry is turned and flowed inside the mold under the heated state. After the temperature reaches the softening point, it is gradually coated on the inner surface of the mold, melted and condensed. The mold is placed in the natural environment or passed through water, After cooling by media such as fog and wind, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L23/02C08K5/134C08K5/526C08K5/132
Inventor 陈叶茹唐宇航温原
Owner ZHEJIANG ROTOUN PLASTIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products