Carbon dioxide cured prefabricated water-permeable concrete and preparation method thereof

A technology of permeable concrete and carbon dioxide, applied in the field of building material preparation, can solve the problems of uneven distribution of voids, slow growth of permeable concrete strength, low production efficiency, etc. Effect

Active Publication Date: 2019-05-31
SOUTHEAST UNIV
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention firstly solves the problems of slow growth of permeable concrete strength, low production efficiency, and uneven distribution of voids. Secondly, the invention solves the problems of industrial tail gas emission, industrial solid waste and Construction waste disposal problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon dioxide cured prefabricated water-permeable concrete and preparation method thereof
  • Carbon dioxide cured prefabricated water-permeable concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] The preparation method of the carbon dioxide curing prefabricated permeable concrete comprises the following steps:

[0039] 1) The recycled aggregate absorbs water until saturated surface dry;

[0040] 2) Add the recycled aggregate, nickel slag sand and 40-60% water into the mixer according to the proportion, and stir for 0.5-1 minute;

[0041] 3) Add cement and stir for 1 to 2 minutes;

[0042] 4) Add the remaining water, water reducer, cellulose ether and Wenlun glue, and stir for 1 to 5 minutes;

[0043] 5) Pour the concrete in step 3) into the mold, use a low-frequency plate vibrator to vibrate in layers, and transfer the mold to a closed curing box or curing room;

[0044] 6) Inflate carbon dioxide gas into the airtight curing box or curing room, control the relative humidity of the curing box or curing room to 40-70%, the mass fraction of carbon dioxide to 20-100%, and perform carbon dioxide curing on concrete products for 6-24 hours;

[0045] 7) Demoulding afte...

Embodiment 1

[0047] Prefabricated permeable concrete using carbon dioxide curing is composed of the following components by mass: 60 parts of recycled concrete aggregate, 30 parts of nickel slag sand, 14 parts of ordinary Portland cement, 2 parts of fly ash, 4 parts of steel slag, 1.2 parts of lime, 0.1 It consists of 1 part of nano-calcium carbonate, 6 parts of water, 0.4 part of naphthalene-based water reducer, 0.003 part of cellulose ether, and 0.001 part of Wenlun glue.

[0048] The preparation of carbon dioxide cured prefabricated pervious concrete prepared from nickel slag, steel slag and recycled aggregate includes the following steps:

[0049] Contains the following steps:

[0050] 1) The recycled aggregate absorbs water until saturated surface dry;

[0051] 2) Add the recycled aggregate, nickel slag sand and 40% water into the mixer according to the proportion, and stir for 0.5 minutes;

[0052] 3) Add cement and stir for 1 minute;

[0053] 4) Add the remaining water, water red...

Embodiment 2

[0058] Carbon dioxide cured prefabricated permeable concrete prepared by using nickel slag, steel slag and recycled aggregate consists of the following components by mass: 70 parts of recycled concrete aggregate, 20 parts of nickel slag sand, 24 parts of ordinary Portland cement, and 1.5 parts of fly ash , 4.5 parts of steel slag, 1 part of lime, 0.14 parts of nano-calcium carbonate, 10 parts of water, 0.55 parts of naphthalene-based water reducer, 0.005 parts of cellulose ether, and 0.002 parts of Wenlun glue.

[0059] The preparation of carbon dioxide cured prefabricated pervious concrete prepared from nickel slag, steel slag and recycled aggregate includes the following steps:

[0060] Contains the following steps:

[0061] 1) The recycled aggregate absorbs water until saturated surface dry;

[0062] 2) Add the recycled aggregate, nickel slag sand and 50% water into the mixer according to the proportion, and stir for 1 minute;

[0063] 3) Add cement and stir for 2 minutes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a carbon dioxide cured prefabricated water-permeable concrete and a preparation method thereof. The water-permeable concrete is composed of following components in parts by weight: 55 to 80 parts of regenerated aggregate, 7 to 30 parts of nickel slag sand, 18 to 40 parts of cementing material, 5 to 25 parts of water, 0.01 to 2 parts of naphthalene water reducer, 0 to 0.02 part of cellulose ether, and 0 to 0.01 part of welan gum. The cementing material is composed of following components in parts by weight: 70 to 90 parts of common silicate cement, 5 to 15 parts of fly ash, 10 to 30 parts of steel slag, 5 to 15 parts of lime or lime slag, and 0.02 to 1 part of nano calcium carbonate. The technology is simple, the structure advantage of water-permeable concrete and the properties of industrial byproducts such as nickel slag, steel slag, fly ash, and the like are fully utilized; carbon dioxide curing is utilized to realize rapid, efficient and environmentally friendly production; high strength, durable and water permeable concrete is obtained, the energy consumption is reduced, the industrial tail gas, metallurgy slag, and building waste are effectively utilized, and good economic benefits, social benefits, and environmental benefits are generated.

Description

technical field [0001] The invention relates to a carbon dioxide curing prefabricated permeable concrete and a preparation method thereof, belonging to the technical field of building material preparation. Background technique [0002] In recent years, my country has vigorously promoted the construction of "sponge city", and permeable concrete pavement is an excellent sponge city technical method to increase rainwater infiltration, which can improve surface runoff conditions very well. [0003] Permeable concrete is a skeleton-void structure, often with single-grained coarse aggregates as the skeleton, often with low strength, and it is prone to problems such as slurry sinking to block the voids during construction and water loss during maintenance to affect strength growth. How to improve strength and reduce clogging is the key issue in the current research on the preparation technology of pervious concrete. [0004] Some scholars in my country have extensively studied the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B40/02
Inventor 张亚梅王申李保亮潘子云
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com