Formula of diatomite bottom plate

A technology of diatom mud and bottom plate, which is applied in the field of diatom mud, can solve the problems of impurities on the surface of the board, heavy weight, and easy breaking of the board.

Inactive Publication Date: 2019-05-31
湖北天然居科技有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 2. The plate is easy to break;
[0005] 3. Foaming does not meet the requirements, and it is too heavy;
[0008] 6. There are impurities on the surface of the plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Reclaiming material: 2000g polyvinyl chloride resin, 3000g diatomaceous earth, 2000g calcium carbonate, 132g stabilizer, 24g polyethylene wax, 28g stearic acid, 240g foaming regulator, foaming ADC64g, 100g chlorinated polyethylene, iron oxide Yellow 12g, wood flour 200g, small tube material 2200g;

[0026] Ingredients: After the raw materials are prepared according to the formula ratio, they are put into the hot mixer and stirred. The temperature reaches 130℃. When the temperature reaches 130℃, the materials are put into the cold mixing pot and stirred. The temperature drops to 40℃ and is discharged. After the extruder barrel mold is heated up to a certain temperature, it will be put into production. After the product is produced, the weight is weighed and the width, thickness and flatness are measured.

Embodiment 2

[0028] Reclaiming material: 2000g polyvinyl chloride resin, 3000g diatomaceous earth, 2000g calcium carbonate, 132g stabilizer, 24g polyethylene wax, 28g stearic acid, 240g foaming regulator, foaming ADC64g, 100g chlorinated polyethylene, iron oxide Yellow 12g, wood flour 200g, small tube material 2200g;

[0029] Ingredients: After preparing the raw materials according to the formula ratio, put them into the hot mixer and stir until the temperature reaches 126°C. When the temperature reaches 126°C, put the materials into the cold mixing pot and stir. The temperature drops to 40°C and discharges. Wait for continuous cooling. After the extruder barrel mold is heated up to a certain temperature, it will be put into production. After the product is produced, the weight is weighed and the width, thickness and flatness are measured.

Embodiment 3

[0031] Reclaiming material: 2000g polyvinyl chloride resin, 3000g diatomaceous earth, 2000g calcium carbonate, 132g stabilizer, 24g polyethylene wax, 28g stearic acid, 240g foaming regulator, foaming ADC64g, 100g chlorinated polyethylene, iron oxide Yellow 12g, wood flour 200g, small tube material 2200g;

[0032] Ingredients: After the raw materials are prepared according to the formula ratio, they are put into the hot mixer and stirred. The temperature reaches 127℃. When the temperature reaches 127℃, the materials are put into the cold mixing pot and stirred. The temperature drops to 40℃ and is discharged. Then start production after the extruder barrel mold heats up to a certain temperature, and weigh the weight after the product is produced, and measure the width, thickness, and flatness;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a formula of a diatomite bottom plate. The bottom plate comprises, by mass percentage, 18-21% of polyvinyl chloride resin, 28-32% of diatomite, 19.5-21% of calcium carbonate,1.30-1.35% of stabilizer, 0.20-0.29% of polyethylene wax, 0.25-0.30% of stearic acid, 2-3% of foaming regulator, 0.6-0.7% of foaming ADC, 0.9-1.1% of chlorinated polyethylene, 0.115-0.13% of iron oxide yellow, 1.5-2.2% of wood flour and 21-22.5% of small tube material. The diatomite bottom plate is capable of removing formaldehyde, purifying air, preventing dampness and mildew and achieving breathability and humidity regulation, good in toughness and less prone to deformation.

Description

Technical field [0001] The invention relates to the field of diatom mud, in particular to a formula for a diatom mud floor. Background technique [0002] At present, in the process of house decoration, most of the materials that need to be used for the floor are used for decoration. However, most of the traditional floor plates have the following problems: [0003] 1. The surface of the board shows leucorrhea, dark band, bright band, light gray band, etc.; [0004] 2. The sheet is easy to break; [0005] 3. The foaming fails to meet the requirements and is too heavy; [0006] 4. Distortion of the board surface; [0007] 5. The surface of the board presents wavy, horizontal, collapse, and vertical lines; [0008] 6. There are impurities on the surface of the board. [0009] In view of the above shortcomings, a material is urgently needed to solve the existing problems. Summary of the invention [0010] In order to solve the above technical problems, the purpose of the present invention is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/28C08L97/02C08L23/06C08K13/02C08K3/34C08K3/26C08K5/09C08K3/22C08J9/10
Inventor 沈炜豪
Owner 湖北天然居科技有限公司