High-adhesion modified asphalt and preparation method thereof

A modified asphalt, high-viscosity technology, applied in building components, building insulation materials, buildings, etc., can solve the problems of poor temperature stability of asphalt materials, restricting the use of asphalt pavement, and brittleness, etc., to improve thermal stability and resistance Low temperature performance, improved tensile strength, enhanced grip and cohesion effects

Inactive Publication Date: 2019-06-07
河北长大交通科技有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, asphalt materials have poor temperature stability, are prone to brittle cracks in winter, and are easy to soften at high temperatures in summer. These shortcomings seriously restrict the use of asphalt pavement.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-adhesion modified asphalt and preparation method thereof
  • High-adhesion modified asphalt and preparation method thereof
  • High-adhesion modified asphalt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The modified asphalt formula of this embodiment is as follows: matrix asphalt 5kg, composite reinforcing fiber is formed by compounding 100g basalt fiber and 100g polyester fiber, additives include 50g compatibilizer, 80gSBS, 35gEVA, 1.5g sulfur powder, 120g rubber powder, 50g terpene resin, 60g thermoplastic rubber and 5g Roadmate A series of asphalt anti-stripping agents; the rubber powder includes 49.0wt% rubber hydrocarbon, 11.5wt% acetone extract, 32.0wt% carbon black and 7.5wt% ash.

[0034] The preparation method is as follows:

[0035] (1) Dry the base asphalt to 135°C, and convert the base asphalt into liquid asphalt;

[0036] (2) Spread the basalt fiber and polyester fiber evenly, spray liquid asphalt on the surface and cool it down to below -10°C quickly, so that the fiber surface is evenly wrapped with asphalt film, and flip it quickly during the cooling process to prevent composite reinforcement fibers Adhesion; then the composite fiber wrapped with asph...

Embodiment 2

[0045]The modified asphalt formula of this embodiment is as follows: matrix asphalt 5kg, composite reinforcing fiber is formed by compounding 50g basalt fiber and 100g polyester fiber, additives include 100g compatibilizer, 50gSBS, 60gEVA, 3.5g sulfur powder, 100g rubber powder, 20g terpene resin, 50g thermoplastic rubber and 2g anti-peeling agent; the rubber powder includes 49.0wt% rubber hydrocarbon, 11.5wt% acetone extract, 32.0wt% carbon black and 7.5wt% ash.

[0046] The preparation method is the same as in Example 1. The modified resin prepared in this example was subjected to a performance test, and the test results are shown in Table 2.

[0047] Table 2

[0048]

[0049]

Embodiment 3

[0051] The modified asphalt formula of this embodiment is as follows: matrix asphalt 5kg, composite reinforcing fiber is formed by compounding 50g basalt fiber and 50g polyester fiber, additives include 80g compatibilizer, 80gSBS, 20gEVA, 0.6g sulfur powder, 150g rubber powder, 100g of terpene resin, 40g of thermoplastic rubber and 8g of anti-peeling agent; the rubber powder includes 49.0wt% rubber hydrocarbon, 11.5wt% acetone extract, 32.0wt% carbon black and 7.5wt% ash.

[0052] The preparation method is the same as in Example 1. The modified resin prepared in this example was subjected to a performance test, and the test results are shown in Table 3.

[0053] table 3

[0054]

[0055] The thermal stability test was carried out on Examples 1-3, and the thermal stability test was evaluated by the dynamic stability (rutting test) test. Take the modified asphalt without adding composite reinforcing fiber, and the other components and preparation method are the same as thos...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
voidageaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-adhesion modified asphalt and a preparation method thereof, and belongs to the technical field of road engineering materials. The raw materials of the high-adhesion modified asphalt comprises 500 parts of base asphalt, 300-400 parts of an additive and 10-20 parts of composite reinforcing fibers, and the composite reinforcing fibers are prepared by compounding basalt fibers and polyester fibers and then being coated with base asphalt thin films. When preparing the high-adhesion modified asphalt, the composite reinforcing fibers are added, so that the adhesion, high-temperature stability, fatigue durability of asphalt pavements are greatly improved, and the asphalt has the properties of low-temperature crack prevention and reflection crack prevention. The tensile, shear, compressive and impact strength are effectively improved, and the thermal stability and low temperature resistance of the asphalt are improved.

Description

technical field [0001] The invention relates to the technical field of road engineering materials, in particular to a high-viscosity modified asphalt and a preparation method thereof. Background technique [0002] Asphalt pavement refers to various types of pavement paved with asphalt materials mixed with mineral materials. Asphalt binder improves the ability of paving aggregates to resist road damage from driving and natural factors, making the road smooth, less dusty, impermeable and durable. Therefore, asphalt pavement is the most widely used high-grade pavement in road construction. [0003] With the development of China's highway transportation, my country's highway construction is entering a period of rapid development. New conditions such as high speed, heavy load and bearing complex stress have put forward higher requirements for high-grade road surfaces. The traditional densely graded asphalt concrete pavement is prone to problems such as slipping, water drift, sp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L53/02C08L23/08C08L45/00C08L21/00C08L67/00C08L91/00C08K13/04C08K7/10C08K3/06C08K3/04C08J5/04
Inventor 颜立景饶奇范明霞周晓雨杨杰
Owner 河北长大交通科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com