Multi-doping pomegranate-shaped solid electrolyte material and preparation method thereof

A solid electrolyte and garnet-type technology, which is applied in the field of multi-doped garnet-type solid electrolyte materials and their preparation, can solve the problems of harsh preparation conditions of solid electrolytes, and achieve reduced energy consumption, improved ion conductivity, and good electrical conductivity. The effect of chemical properties

Inactive Publication Date: 2019-06-14
SOUTH CHINA UNIV OF TECH
View PDF5 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the preparation conditions of such solid electrolytes are rel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi-doping pomegranate-shaped solid electrolyte material and preparation method thereof
  • Multi-doping pomegranate-shaped solid electrolyte material and preparation method thereof
  • Multi-doping pomegranate-shaped solid electrolyte material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1 (comparative example)

[0028] Preparation of Al 2 o 3 -Li 7 La 3 Zr 2 o 12 Solid electrolyte material:

[0029] Weigh 2.33gLiOH·H according to the molar ratio of Li, La, Zr 7:3:2 2 O, 2.91gLa 2 o 3 , 1.46gZrO 2 , adding isopropanol as a dispersant for ball milling, material: zirconium balls: dispersant = 1:3:1 (mass ratio), ball milling at a speed of 500r / min for 6h, and then placed in a blast drying oven to dry at 60°C, A mixed powder is obtained. Put the mixed powder in a muffle furnace, raise the temperature to 800°C at a rate of 3°C / min, keep it at 800°C for 6 hours, take out the sample after cooling to room temperature with the furnace, add 0.005gAl 2 o 3Secondary ball milling for 6 hours to reduce the particle size of the solid powder to the micron level. After drying again, obtain the mother powder; take 5g of the mother powder, press the mother powder at a pressure of 250MPa, hold the pressure for 20min, and obtain LLZO tablets with a t...

Embodiment 2

[0032] Preparation of Al 2 o 3 -Li 6.8 La 3 Zr 1.9 Te 0.1 o 12 (Te is +6 valence in this embodiment) solid electrolyte material:

[0033] Choose LiOH·H 2 O, La 2 o 3 , ZrO 2 , TeO 2 、Al 2 o 3 As a raw material, weigh 2.24g LiOH·H according to the stoichiometric ratio 2 O, 2.88gLa 2 o 3 , 1.38g ZrO 2 , 0.09g TeO 2 , adding isopropanol as a dispersant for ball milling, material: zirconium balls: dispersant = 1:3:1, ball milling at a speed of 400r / min for 6h, and then placed in a blast drying oven at 60°C to obtain a mixed powder. Pre-fire the mixed powder in a muffle furnace at 600°C for 2h, add 0.007g Al 2 o 3 Secondary ball milling for 6 hours to reduce the particle size of the solid powder to the nanometer level. After drying again, 5 g of the mother powder was obtained. The mother powder was pressed into tablets with a pressure of 250 MPa to a thickness of 1 mm, and then placed in a muffle furnace at 3 ° C. Raise the temperature to 700°C at a rate of 1 / mi...

Embodiment 3

[0035] Preparation of Al 2 o 3 -Li 6.8 La 3 Zr 1.9 Te 0.1 o 12 The solid electrolyte material:

[0036] Weigh 4.48gLiOH·H according to the stoichiometric ratio 2 O, 5.76gLa 2 o 3 , 2.76gZrO 2 , 0.18gTeO 2 , adding isopropanol as a dispersant for ball milling, material: zirconium balls: dispersant = 1:6:1, ball milled at a speed of 500r / min for 12h, and then dried in a blast drying oven at 60°C to obtain a mixed powder. Put the mixed powder in a muffle furnace, pre-fire at 600°C for 2 hours, add 0.014g Al 2 o 3 Secondary ball milling for 12 hours to reduce the particle size of the solid powder to the micron level, and then dry again to obtain 10g of the mother powder, then press the mother powder into tablets with a pressure of 200MPa and a thickness of 1mm, and sinter in a muffle furnace at 700°C for 12 hours , making Al 2 o 3 -Li 6.8 La 3 Zr 1.9 Te 0.1 o 12 Cubic garnet type solid electrolyte sheet.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Ionic conductivityaaaaaaaaaa
Ionic conductivityaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of a solid electrolyte, and discloses a multi-doping pomegranate-shaped solid electrolyte material and a preparation method thereof. The constituent of themulti-doping pomegranate-shaped solid electrolyte material is A-Li<7-bX>La<3>Zr<2-x>M<x>O<12>, wherein M is more than one of Te, Ta, Ti, Nb, Ge, Ga, Gd and Bi, x is more than or equal to 0.1 but lessthan or equal to 1.5, the numerical value b is changed with the valence state of the M, and A is one or more of Al2O3, Al(NO3)3, aluminum carbonate, ZnO and MgO. The invention also discloses the preparation method of the solid electrolyte material. With the mode of multiple doping, the sintering temperature is reduced, the energy consumption is reduced, and the obtained pomegranate-shaped solid electrolyte material has relatively good electrochemical performance.

Description

technical field [0001] The invention belongs to the field of solid electrolyte materials, and in particular relates to a multi-doped garnet-type solid electrolyte material and a preparation method thereof. Background technique [0002] With the upgrading of electronic products, the integration and simplification of electronic equipment, and the increasing requirements for batteries in fields such as electric vehicles and smart grids, lithium-ion batteries, lithium-air batteries, lithium-sulfur batteries, and fuel cells, etc., have caused Research boom at home and abroad. Lithium-ion batteries are currently the most widely used. Lithium-ion batteries have the advantages of high energy density and power density. However, traditional lithium-ion batteries use organic liquid electrolytes, which are prone to safety problems such as leakage, combustion, and explosion. In addition, metal lithium is prone to problems such as pulverization and lithium dendrite growth in the process ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M10/0562
CPCY02E60/10
Inventor 宋慧宇郑广丽
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap