A kind of manufacture method of modified yttrium oxide

A manufacturing method and yttrium oxide technology, which are applied to the field of inorganic materials and their manufacturing, can solve the problems of poor process operation performance, low sand yield of fused yttrium oxide, low storage time of coating slurry powder, etc., so as to improve the process. Operation performance, high powder-to-liquid ratio, smooth surface effect

Active Publication Date: 2021-07-06
郑州振中电熔新材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the sand yield of fused yttrium oxide obtained by this method is low, and the powder-liquid ratio of the coating slurry made by this method is relatively low and the storage time is short, and the process performance is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of manufacture method of modified yttrium oxide
  • A kind of manufacture method of modified yttrium oxide
  • A kind of manufacture method of modified yttrium oxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of manufacture method of modified yttrium oxide, manufacture method comprises the steps:

[0031] Step 1: batching, taking 2-17 parts by weight of zirconia and 83-98 parts by weight of yttrium oxide, pulverizing them to a size smaller than or equal to 100 mesh, and mixing the pulverized zirconia and yttrium oxide evenly to obtain a mixed charge;

[0032] Step 2: Smelting, put the mixed charge into the electric arc furnace for smelting, the melting temperature is greater than or equal to 2410°C, after T 1 min time until the mixed charge is completely melted to obtain the modified yttrium oxide in molten state;

[0033] Further also include the following steps:

[0034] Step 3: cooling down, cooling the modified yttrium oxide melted in step 2 to room temperature;

[0035] Step 4: Crushing, smashing and sorting the modified yttrium oxide after cooling in step 3, the purpose of picking is to pick out the lumps that have not melted well on the surface and have raw m...

Embodiment 2

[0045] Step one, the ingredients will contain ZrO 2 3 parts by weight of fused desiliconized zirconium with a weight content greater than 99% and 97 parts by weight of yttrium oxide with a weight content of 3N are put into a mixer and mixed evenly to make a mixed charge.

[0046] Step 2, smelting, put the mixed charge into the electric arc furnace in batches, for example: smelting in a three-phase AC electric arc furnace until the charge is completely melted, and continue refining after melting. The time ratio of melting and refining is 3:2, each charge Carry out melting for 30 minutes, refining for 20 minutes, and the melting temperature is 2600°C.

[0047] Step 3, lowering the temperature, cooling down the melted melt to room temperature.

[0048]Step 4, smashing, smashing and picking the melt. The frit after picking is processed into sand and fine powder with the particle size required by the user by crushing equipment. The size above 100 mesh is less than 100 mesh. The c...

Embodiment 3

[0050] will contain ZrO 2 5 parts by weight of natural baddeleyite with a weight content greater than 99% and 95 parts by weight of yttrium oxide with a weight content of 4N are put into a mixer and mixed evenly to make a mixed charge. Other steps are the same as in Embodiment 1 and will not be repeated.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a kind of manufacturing method of modified yttrium oxide, a kind of manufacturing method of modified yttrium oxide, other manufacturing methods comprise the following steps: Step 1: batching, take 2-17 parts by weight of zirconia and 83-98 parts by weight 2 parts of yttrium oxide, pulverized to less than or equal to 100 mesh, and uniformly mixed the pulverized zirconia and yttrium oxide to obtain a mixed charge; step 2: smelting, putting the mixed charge into an electric arc furnace for melting, and the melting temperature is greater than or equal to 2410°C , after T 1 min until the mixed charge is completely melted to obtain a melt containing modified yttrium oxide in a molten state. The fused yttrium oxide produced by the present invention has a high sand production rate, which not only meets the needs of users but also reduces production costs, and the resulting coating slurry has a high powder-to-liquid ratio, which is beneficial to improving the density of the titanium alloy investment casting coating. Therefore, the quality of castings is improved, the coating slurry is not easy to gel, the storage time is long, the process operation performance is improved, and the surface layer of titanium alloy castings produced by investment casting is smooth.

Description

technical field [0001] The invention relates to an inorganic material and a manufacturing method thereof, in particular to a manufacturing method of modified yttrium oxide. Background technique [0002] Yttrium oxide is one of the minerals with relatively abundant reserves of rare earth oxides in my country. Among more than ten kinds of rare earth oxides, its price is relatively low, and it has some unique properties, such as high refractoriness and no reaction with titanium alloy melt; Fused yttrium oxide is a new product researched and developed with yttrium raw material by special process. It has the characteristics of high purity, large crystal size, high temperature resistance, good thermal conductivity, strong impermeability, etc. It can be used in titanium casting industry and special ceramic industry . [0003] At present, sintered yttrium oxide is used as the coating material for titanium alloy investment casting. The original powder of yttrium oxide is pressed into ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/505C04B35/66C04B35/626
Inventor 余鑫萌李起胜李群李疆鹰
Owner 郑州振中电熔新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com