Polyacrylonitrile-based carbon fiber and regulating method of surface groove structure of fiber

A polyacrylonitrile-based carbon fiber and groove technology, which is applied in the field of carbon fiber, can solve the problems of reduced effective force-bearing area of ​​fibers, large differences in the depth of grooves on the surface of fibers, and reduced strength, so as to achieve depth and uniformity, and realize The controllable groove structure and the effect of reducing the difference in solidification rate

Active Publication Date: 2019-07-23
山西钢科碳材料有限公司
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the polyacrylonitrile-based carbon fibers currently produced by manufacturers have large differences in the depth of grooves on the fiber surface (local grooves are extremely deep), large fiber surface roughness, and poor axial parallelism of groove fibers.
The deep local groove of the fiber leads to the reduction of the effective stress area and strength of the fiber, and the stress concentration point is easily formed at the bottom of the deep groove
The roughness of the fiber surface is large, the axial parallelism of the grooves is poor, and the grooves are messy and criss-crossed, which is not conducive to the seepage and uniform spreading of the sizing agent and composite resin along the grooves on the fiber surface. Low performance and large dispersion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyacrylonitrile-based carbon fiber and regulating method of surface groove structure of fiber
  • Polyacrylonitrile-based carbon fiber and regulating method of surface groove structure of fiber
  • Polyacrylonitrile-based carbon fiber and regulating method of surface groove structure of fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0093] 1) Preparation of spinning dope

[0094] Add the monomer acrylonitrile / itaconic acid / 2-acrylamido-2-methylpropanesulfonic acid into the reactor with stirring device according to the ratio of 97.8 / 1.00 / 1.2; the total monomer accounts for the mass percentage of the solution 25%. The dosage of the initiator azobisisobutyrocyanide is 2% of the total weight of the monomers, and the solution polymerization is carried out with dimethylformamide as the solvent. During the polymerization process, first bubble high-purity nitrogen into the reactor for 15 minutes to replace the air in the reaction system, then start stirring and raise the temperature to 60°C, and under the protection of nitrogen, polymerize at a constant temperature for 20 hours to obtain polyacrylonitrile spinning liquid.

[0095] 2) solidification molding

[0096] Wet spinning is adopted. After the spinning solution is sprayed out from the spinneret, it is solidified and formed by eight-stage coagulation bath...

Embodiment 2

[0131] The difference from Example 1 is that the type of regulator in the coagulation bath is changed from ethanol to n-propanol.

Embodiment 3

[0133] The difference from Example 1 is that the type of regulator in the coagulation bath is replaced by ammonia water from ethanol.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
densityaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a polyacrylonitrile-based carbon fiber and a regulating method of a surface groove structure of the fiber. According to the main technical scheme, the regulating method of thesurface groove structure of the polyacrylonitrile-based carbon fiber comprises the step that in the solidification forming procedure of the step of preparing the polyacrylonitrile-based carbon fiber,a spinning trickle sprayed out by a spinneret device is solidified and formed into nascent fibers, and the surface groove structure of the polyacrylonitrile-based carbon fiber is regulated by adjusting solubility parameters of a solidification bath liquid. The surface groove structure of the polyacrylonitrile-based carbon fiber is regulated to be within the following ranges that the maximal depthof the groove is 0.06-0.65 micrometer, the average groove depth is 0.043-0.49 micrometer, the fiber surface roughness is 0.01-0.12 micrometer, and the average spacing of the groove top is 0.1-0.6 micrometer. The regulating method is mainly used for effectively controlling the surface groove structure of the polyacrylonitrile-based carbon fiber, so that the groove depth is suitable, the surface roughness is suitable, and the groove axial parallelity is good.

Description

technical field [0001] The invention relates to the technical field of carbon fibers, in particular to a polyacrylonitrile-based carbon fiber and a method for regulating its surface groove structure. Background technique [0002] Carbon fiber is composed of a so-called "turbulent layer" structure formed by stacking flake graphite microcrystals along the axial direction of the fiber. The structure of carbon fiber is usually regarded as composed of two-dimensional ordered crystals and holes. From the perspective of development history, polyacrylonitrile-based carbon fiber is a new material developed to meet the needs of cutting-edge industries such as aerospace, aviation, and atomic energy. It has high tensile strength, high tensile modulus, low density, high temperature resistance, Anti-ablation, corrosion resistance, high electrical and thermal conductivity, low thermal expansion, self-lubrication and good biocompatibility and other comprehensive properties. [0003] Polyac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F9/22D01D5/06D01D10/02D01F6/38
CPCD01D5/06D01D10/02D01F6/38D01F9/22
Inventor 吕春祥邵伟隋敏李永红
Owner 山西钢科碳材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap