Paint remover for metal surface epoxy resin

A technology for epoxy resin paint and metal surface, applied in the direction of chemical paint/ink remover, coating, etc., can solve the problems of unsatisfactory epoxy resin paint treatment on metal surface, etc., to achieve swelling, rapid paint stripping, The effect of reducing adhesion

Inactive Publication Date: 2019-07-26
祝亚琴
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this type of paint remover is thorough and has a wide range of applications, it is not ideal for the treatment of epoxy resin paint on metal surfaces.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Several identical steel plates to be stripped (the surface is the epoxy universal primer 280 of SIGMA company, the steel plate is a common steel plate, the surface is polished, and the thickness is 20 microns) is completely immersed in the paint remover solution, the paint remover The operating temperature range is 50°C. Every 1 minute, take out the steel plate to be stripped and observe whether the epoxy paint has been removed from the surface.

[0020] The paint stripper consists of 70 parts by weight of N, N-dimethylformamide, 3 parts by weight of anionic surfactants, 3 parts by weight of nonionic surfactants, 4 parts by weight of organic bases, 25 parts by weight of ethanol, 6 parts by weight of mineral spirits, 8 parts by weight of diphenylamine derivatives and 8 parts by weight of water. The time to test for complete removal was 11 minutes.

Embodiment 2

[0022] Several identical steel plates to be stripped (the surface is the epoxy universal primer 280 of SIGMA company, the steel plate is a common steel plate, the surface is polished, and the thickness is 20 microns) is completely immersed in the paint remover solution, the paint remover The operating temperature range is 50°C. Every 1 minute, take out the steel plate to be stripped and observe whether the epoxy paint has been removed from the surface.

[0023] The paint stripper consists of 65 parts by weight of N, N-dimethylformamide, 4 parts by weight of anionic surfactants, 4 parts by weight of nonionic surfactants, 5 parts by weight of organic bases, 22 parts by weight of ethanol, 7 parts by weight of mineral spirits, 9 parts by weight of diphenylamine derivatives and 8 parts by weight of water. The time to test for complete removal was 12 minutes.

Embodiment 3

[0025] Several identical steel plates to be stripped (the surface is the epoxy universal primer 280 of SIGMA company, the steel plate is a common steel plate, the surface is polished, and the thickness is 20 microns) is completely immersed in the paint remover solution, the paint remover The operating temperature range is 50°C. Every 1 minute, take out the steel plate to be stripped and observe whether the epoxy paint has been removed from the surface.

[0026] The paint stripper consists of 70 parts by weight of N,N-dimethylformamide, the anionic surfactant of 6 parts by weight, the nonionic surfactant of 6 parts by weight, the organic base of 8 parts by weight, the ethanol of 12 parts by weight, 10 parts by weight of mineral spirits, 3 parts by weight of diphenylamine derivatives and 9 parts by weight of water. The time to test for complete removal was 17 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a paint remover for metal surface epoxy resin. The paint remover consists of 50-70 parts by weight of N, N-dimethylformamide, 1-5 parts by weight of anionic surfactants, 1-5 parts by weight of nonionic surfactants, 3-10 parts by weight of organic base, 20-30 parts by weight of ethanol, 5-7 parts by weight of solvent oil, 4-12 parts by weight of diphenylamine derivatives and 3-9 parts by weight of water. The diphenylamine derivatives are selected, so that the adhesive force between epoxy resin and metal can be greatly reduced, and rapid paint removal can be realized onthe metal surface.

Description

technical field [0001] The invention relates to a paint remover for metal surface epoxy resin paint. Background technique [0002] Organic paint remover is a liquid mixed with chlorinated hydrocarbons, benzene series, esters, alcohols, ethers and other solvents. Invented organic paint remover has become the mainstream paint remover in the market because of its advantages of convenient use, high paint removal efficiency, good stability and low metal corrosion. For example, in the patent "paint remover for polyester and polyesterimide enamelled copper round wire paint film", the formula of paint remover is announced, and its components are: 30-50% formic acid, 30% ~40% trichloromethane, 5~35% mixed cresols, invention 0~5% additive composition. In the patent of "a powerful paint remover", it is announced that the mass fraction is 0-5% surfactant, 72-78% dichloromethane, 0-3% ethyl acetate, 0.78-0.8% thickener , Invention 0.6-0.7% paraffin, 4.85-10% phenol, 5-9% ethanol, 0-6%...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D9/04
CPCC09D9/005C09D9/04
Inventor 祝亚琴
Owner 祝亚琴
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com