Rust-proof coating for ship deck and preparation process of coating

A ship deck and anti-rust coating technology, which is applied in coatings, anti-corrosion coatings, and devices for coating liquid on the surface, can solve problems that affect the appearance, affect ship functions, and safety performance, and achieve improved corrosion inhibition performance, Good oxidation-reduction characteristics, the effect of inhibiting corrosion reaction

Inactive Publication Date: 2019-07-26
谭运学
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Once oxidized, it will not only affect the appearance, but also may seriously affect the function and safety performance of the ship

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rust-proof coating for ship deck and preparation process of coating
  • Rust-proof coating for ship deck and preparation process of coating

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0056] A preparation process for an antirust coating for ship decks, comprising the following steps:

[0057] Step 1. Grinding and blasting the surface of the ship's deck until the derusting level of the steel surface of the ship's deck reaches Sa3 level;

[0058] Step 2. Preparation of pre-dispersion: in ethanol aqueous solution, add water-based leveling agent, water-based wetting agent and corrosion inhibitor sequentially under the condition of 1000r / min with a high-speed mixer, and the feeding interval is 5min, and continue 1000r / min after all addition Stir for 20-24min, then use ultrasonic treatment for 15-18min;

[0059] Step 3. Preparation of anti-rust primer: under constant stirring at 500r / min, add half of the anti-rust filler into the silicone acrylic emulsion, then add 1 / 4 of the pre-dispersion and 1 / 4 of the dispersant, and finish adding Finally, continue to stir at 500r / min for 25-30min, transfer to sand milling equipment, grind until the slurry fineness is ≤35μm,...

Embodiment 1

[0070] The antirust coating for ship deck is made of the following raw materials in parts by weight: 30-40 parts of silicone acrylic emulsion, 50-60 parts of acrylic emulsion, 2.5-3 parts of polyethylene wax emulsion, 28-34 parts of fluorosilicon emulsion, antirust 12-16 parts of pigment, 3-5 parts of filler, 2-3 parts of nano-silica, 3-4 parts of corrosion inhibitor, 2-3 parts of dispersant, 2-3 parts of defoamer, 1.5- 2 parts, 1.5-2 parts of water-based wetting agent, 8-10 parts of ethanol aqueous solution.

Embodiment 2

[0072] The antirust coating for ship deck is made of the following raw materials in parts by weight: 30-40 parts of silicone acrylic emulsion, 50-60 parts of acrylic emulsion, 2.5-3 parts of polyethylene wax emulsion, 28-34 parts of fluorosilicon emulsion, antirust 12-16 parts of pigment, 3-5 parts of filler, 2-3 parts of nano-silica, 3-4 parts of corrosion inhibitor, 2-3 parts of dispersant, 2-3 parts of defoamer, 1.5- 2 parts, 1.5-2 parts of water-based wetting agent, 8-10 parts of ethanol aqueous solution.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a rust-proof coating for a ship deck. The rust-proof coating is prepared from, by weight, 30-40 parts of silicone acrylic emulsion, 50-60 parts of acrylic emulsion, 2.5-3 partsof polyethylene wax emulsion, 28-34 parts of fluoro-silicon emulsion, 12-16 parts of anti-rust pigments, 3-5 parts of fillers, 2-3 parts of nano-silicon dioxide, 3-4 parts of corrosion inhibitors, 2-3 parts of dispersing agents, 2-3 parts of defoaming agents, 1.5-2 parts of waterborne leveling agents, 1.5-2 parts of waterborne wetting agents and 8-10 parts of ethanol water. The invention furtherdiscloses a preparation process of the rust-proof coating for the ship deck. According to the coating, the corrosion inhibitors and the anti-rust pigments are added, a bottom layer, a middle layer anda surface layer have different structures are matched each other, so that the prepared coating has good hydrophobicity, water resistance can reach 62d, acid and alkali resistance can reach 35d, saltfog performance can reach 38d, and the coating has good corrosion resistance.

Description

technical field [0001] The invention belongs to the technical field of ship rust prevention, and in particular relates to a ship deck antirust coating and a preparation process thereof. Background technique [0002] A ship is composed of many parts. According to the function and use of each part, it can be comprehensively summarized into three parts: hull, ship power plant, and ship electrical. The hull is the basic part of the ship, which can be divided into the main part and the superstructure part. The main part generally refers to the part below the upper deck. It is a hollow body with a specific shape surrounded by the hull (bottom and side) and the upper deck. It is a key part to ensure that the ship has the required buoyancy, navigating performance and hull strength. . The hull is generally used for arranging power plants, loading cargo, storing fuel and fresh water, and arranging various other compartments. [0003] In order to ensure the strength of the hull, imp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D133/04C09D183/08C09D5/08C09D7/61B05D7/14B05D7/00B05D7/24
CPCB05D7/14B05D7/24B05D7/584B05D2202/10C08K2003/2272C08K2003/328C08K2003/387C08K2201/011C09D5/08C09D5/084C09D7/61C09D7/70C09D133/00C09D143/04C09D183/08C08L79/02C08K3/38C08K3/22C08K3/32C08L23/06C08K7/00C08K3/40C08K3/346C08K3/36
Inventor 不公告发明人
Owner 谭运学
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products