Application of ionic liquid in preparation of modified activated carbon, modified activated carbon and preparation method thereof

An ionic liquid and activated carbon technology, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of activated carbon modifiers polluting the environment, long adsorption time, low adsorption efficiency, etc., to improve adsorption efficiency and reduce the possibility of The effect of sex, convenient operation

Active Publication Date: 2022-02-11
HEBEI UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the low adsorption efficiency of existing activated carbon, the long time for adsorption and the potential safety hazard of spontaneous combustion, and the environmental pollution caused by activated carbon modifiers, the present invention provides an application of ionic liquid in the preparation of modified activated carbon, modified activated carbon and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Application of ionic liquid in preparation of modified activated carbon, modified activated carbon and preparation method thereof
  • Application of ionic liquid in preparation of modified activated carbon, modified activated carbon and preparation method thereof
  • Application of ionic liquid in preparation of modified activated carbon, modified activated carbon and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A preparation method of modified activated carbon, comprising the following steps:

[0027] (1) After mixing proline and imidazole with a molar ratio of 1:1, gradually raise the temperature to 90°C at a rate of 5°C / h, keep warm until the system is uniform and transparent, and then the imidazole-proline ionic liquid is obtained;

[0028] (2) The above-mentioned ionic liquid and activated carbon were mixed at a mass ratio of 4:1, treated at a constant temperature of 100° C. for 24 hours, and filtered to obtain modified activated carbon.

Embodiment 2

[0030] A preparation method of modified activated carbon, comprising the following steps:

[0031] (1) After mixing alanine and methanesulfonic acid with a molar ratio of 1:2, gradually raise the temperature to 85°C at a rate of 3°C / h, keep warm until the system is uniform and transparent, and obtain alanine-methanesulfonate ion liquid;

[0032] (2) The above-mentioned ionic liquid and activated carbon were mixed at a mass ratio of 5:1, treated at a constant temperature of 110° C. for 30 h, and centrifuged to obtain modified activated carbon.

Embodiment 3

[0034] A preparation method of modified activated carbon, comprising the following steps:

[0035] (1) After mixing phenylalanine and methanesulfonic acid with a molar ratio of 1:5, the temperature is gradually raised to 80°C at a rate of 7°C / h, and the temperature is kept until the system is uniform and transparent to obtain phenylalanine-methanesulfonic acid acid ionic liquid;

[0036] (2) The above-mentioned ionic liquid and activated carbon were mixed at a mass ratio of 6:1, treated at a constant temperature of 120°C for 36 hours, and filtered to obtain modified activated carbon.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of adsorption materials, and specifically discloses the application of an ionic liquid in the preparation of modified activated carbon, the modified activated carbon and a preparation method thereof. The preparation method comprises the following steps: mixing the ionic liquid and activated carbon, treating at a constant temperature of 100-120° C. for 24-36 hours, and obtaining modified activated carbon through separation treatment. The modified activated carbon provided by the present invention increases the saturated adsorption capacity of organic waste gas by about 120%, increases the spontaneous ignition point by about 30°C, improves the adsorption efficiency of the modified activated carbon, increases the spontaneous ignition point, and reduces the possibility of spontaneous combustion.

Description

technical field [0001] The invention relates to the technical field of adsorption materials, in particular to the application of an ionic liquid in the preparation of modified activated carbon, the modified activated carbon and a preparation method thereof. Background technique [0002] In recent years, with the development of the national economy, people have higher and higher requirements for the quality of the air environment. Among them, organic waste gas, as a kind of air pollutants, has attracted many scholars because of its long duration and high toxicity. attention. Activated carbon is often used as an adsorption material for organic waste gas treatment because of its rich pore structure, large specific surface area, and good chemical stability. However, activated carbon generally has the problems of low adsorption efficiency and long adsorption time during the adsorption process, and spontaneous combustion may also occur during storage, transportation, and use. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/20B01J20/30
CPCB01J20/20
Inventor 张金锋柳晓凯任红威李晨曦张楠朱鸿宇赵子乾
Owner HEBEI UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com