Ferrite stainless steel with excellent ridging property and surface quality and manufacturing method therefor

A stainless steel and ferrite technology, applied in the direction of manufacturing tools, furnaces, heat treatment equipment, etc., to achieve the effect of reducing the wrinkle height, low surface micro-groove area ratio, and high r value

Active Publication Date: 2019-07-30
浦项股份有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, there have been few attempts to improve the texture by symmetrical rolling or asymmetrical rolling of hot-rolled steel sheets coiled at high temperature before annealing, followed by continuous annealing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ferrite stainless steel with excellent ridging property and surface quality and manufacturing method therefor
  • Ferrite stainless steel with excellent ridging property and surface quality and manufacturing method therefor
  • Ferrite stainless steel with excellent ridging property and surface quality and manufacturing method therefor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0039] Hereinafter, embodiments of the present disclosure will be described in detail with reference to the accompanying drawings. These embodiments are provided to fully convey the concept of the disclosure to those of ordinary skill in the art. This disclosure may, however, be embodied in many different forms and should not be construed as limited to the exemplary embodiments set forth herein. In the drawings, in order to clearly describe the present disclosure, parts irrelevant to the description are omitted, and the size of elements may be exaggerated for clarity.

[0040] The ferritic stainless steel having excellent wrinkling characteristics and excellent surface quality according to an embodiment of the present disclosure contains 0.005% to 0.1% of carbon (C), 0.01% to 2.0% of silicon (Si ), 0.01% to 1.5% manganese (Mn), 0.05% or less phosphorus (P), 0.005% or less sulfur (S), 10% to 30% chromium (Cr), 0.005% to 0.1 % nitrogen (N), 0.005% to 0.2% aluminum (Al), the re...

Embodiment

[0083] Molten steel having the composition shown in Table 1 was continuously cast to prepare slabs, and the slabs were hot rolled by reheating. Then, the hot-rolled steel sheet with an initial thickness of 3 mm to 7 mm is cold-rolled once before thermal annealing.

[0084] Table 1

[0085]

[0086] The primary cold rolling is performed at a reduction ratio of 20% to 50% using conventional cold rolling or asymmetric cold rolling. After thermal annealing and pickling of the primary cold-rolled steel sheets, secondary cold rolling was performed at a reduction ratio of 50% to 85%, followed by cold annealing and pickling to prepare samples.

[0087] The samples were processed and subjected to a 15% tensile test in directions of 0°, 45° and 90° with respect to the rolling direction to measure the r value (Lankford value). From the r values ​​measured in all directions (r 0 、r 45 and r 90 ) to calculate the r-bar value (r-bar=(r 0 + r 90 +2*r 45 ) / 4). In addition, the wri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
heightaaaaaaaaaa
thicknessaaaaaaaaaa
aspect ratioaaaaaaaaaa
Login to view more

Abstract

Disclosed are ferrite stainless steel having an excellent ridging property and surface quality of a final product by changing a microstructure of a central portion of a cross section by further performing cold rolling before a heat treatment of hot-rolling annealing, and a manufacturing method therefor. Austenitic stainless steel according to the present invention comprises, in percentage by weight: 0.005 to 0.1% of C; 0.01 to 2.0% of Si; 0.01 to 1.5% of Mn; 0.05% or less of P; 0.005% or less of P; 10 to 30% of Cr; 0.005 to 0.1% of N; 0.005 to 0.2% of Al; and the balance being Fe and other unavoidable impurities, in which max is 20% or more and less than 50%, and a fine groove area ratio of a surface is 2.0% or less.

Description

technical field [0001] Embodiments of the present disclosure relate to a ferritic stainless steel having excellent ridging characteristics and excellent surface quality and a method of manufacturing the same, and more specifically, to A ferritic stainless steel having excellent wrinkling properties and excellent surface quality by improving the structure in the center of the thickness by rolling, and a manufacturing method thereof. Background technique [0002] Generally, stainless steels are classified according to composition or metal structure. According to the metal structure, stainless steel is divided into austenitic stainless steel, ferritic stainless steel, martensitic stainless steel and duplex stainless steel. Among these stainless steels, ferritic stainless steel, which is excellent in corrosion resistance despite having a small amount of expensive alloying elements, has been widely used in various kitchen utensils, automobile exhaust system parts, building mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/18C22C38/00C22C38/02C21D8/02C21D9/46
CPCC21D8/0405C21D8/0426C21D8/0436C21D8/0473C21D9/48C22C38/00C22C38/004C22C38/02C22C38/04C22C38/06C22C38/18C21D2211/005C21D6/002C22C38/40C22C38/001C21D8/0226C21D8/0236C21D9/46C21D8/0263C21D8/0268C21D8/0273C21D9/0081
Inventor 朴秀湖李凯蔓
Owner 浦项股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap