Heat treatment method for inhibiting recrystallization of 3D printed or welded single crystal superalloy

A heat treatment method and technology of superalloys, applied in the field of additive manufacturing and metal heat treatment, can solve problems such as large residual stress, and achieve the effects of improving microstructure, inhibiting recrystallization, and having strong feasibility

Active Publication Date: 2019-08-02
XI AN JIAOTONG UNIV
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, additively manufactured parts are subject to multiple "rapid heating-rapid cooling" thermal cycles, and the heat in the subsequent cladding process is not enough to completely eliminate the thermal stress of the cladding layer, so there is a large residual stress after the sample or part is cooled.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat treatment method for inhibiting recrystallization of 3D printed or welded single crystal superalloy
  • Heat treatment method for inhibiting recrystallization of 3D printed or welded single crystal superalloy
  • Heat treatment method for inhibiting recrystallization of 3D printed or welded single crystal superalloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] This example is an electron beam 3D printing single crystal superalloy. The necessary temperature and necessary time for stress relief annealing are determined in advance as 1100°C / 8 hours, and it is treated according to the heat treatment method described in this patent, namely:

[0069] (a) Clean up the alloy powder adhered to the surface of the 3D printed single crystal superalloy, and remove the surface miscellaneous crystals by grinding with a grinding wheel.

[0070] (b) Perform stress relief annealing, raise the temperature to 1100°C, take it out after 8 hours of heat preservation, and cool to room temperature under the protection of nitrogen.

[0071] (c) Standard heat treatment is performed.

[0072] The treated 3D printed single crystal superalloy slices were prepared for tissue observation and electron backscatter diffraction detection. like image 3 As shown, the 3D printed single crystal superalloy sample did not recrystallize after heat treatment according...

Embodiment 2

[0074] This example is a laser 3D printing single crystal superalloy, and the parameters of the stress relief annealing heat treatment are the same as those in Example 1, which is 1100°C / 8 hours. It is processed by the heat treatment method described in this patent, that is:

[0075] (a) Clean up the alloy powder adhered to the surface of the laser 3D printed single crystal superalloy, and sand the surface to remove the miscellaneous crystal layer.

[0076] (b) Stress-relief annealing is performed on the laser 3D printed single crystal superalloy, and the temperature is raised to 1100 ° C for 8 hours.

[0077] (c) Leave the laser 3D printed single crystal superalloy after stress relief annealing in the heat treatment furnace, change the furnace temperature, and perform standard heat treatment.

[0078] The treated 3D printed single crystal superalloy slices were prepared for tissue observation and electron backscatter diffraction detection. It was found that the 3D printed si...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a heat treatment method for inhibiting recrystallization of a 3D printed or welded single crystal superalloy, and belongs to the field of additive manufacturing and metal heattreatment. The method comprises the following steps of removing residual alloy powder and an impurity crystal layer on the surface of the 3D printed or welded single crystal superalloy, performing stress relief annealing on the 3D printed or welded single crystal superalloy to release internal residual stress on the premise of no recrystallization, performing standard heat treatment on the 3D printed or welded single crystal superalloy subjected to stress relief annealing after heat preservation for a necessary period of time at a necessary temperature, so that the strengthening gamma' phase of the 3D printed or welded single crystal superalloy grows to a predetermined size and is orderly arranged. The method can be use for improving the structure and performance of the 3D printed or welded single crystal superalloy, and subsequent heat treatment of the 3D printed or welded single crystal superalloy can be developed based on the method.

Description

technical field [0001] The invention belongs to the field of additive manufacturing and metal heat treatment, in particular to a heat treatment method for suppressing the recrystallization of a 3D printed or welded single crystal superalloy. Background technique [0002] The most direct and effective way to develop high-thrust, high-efficiency, and low-fuel-consumption aeroengines is to increase the gas inlet temperature before the turbine, and the increase in temperature is mainly limited by the temperature-bearing capacity of the turbine blades. The temperature of polycrystalline blades prepared by early powder deformation alloys is between 700 and 900°C, and the service temperature of polycrystalline blades prepared by forging technology can reach 950°C; 980°C; single crystal blades completely eliminate the adverse effects of grain boundaries on mechanical properties in high-temperature environments, and the service temperature can reach 1050-1100°C. [0003] However, si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22F1/10C22C19/05B22F3/24
CPCB22F3/24B22F2003/248C22C19/057C22F1/10
Inventor 陈凯黄润秋
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com