A kind of foam fire extinguishing material containing closed-cell foam ceramic ball and preparation method thereof

A closed-cell foam ceramic and foam fire extinguishing technology, which is applied in fire protection equipment and other directions, can solve the problems of difficult spraying of foam fire extinguishing materials, poor damage resistance of foam covering layers, and short oil surface coverage time.

Active Publication Date: 2021-04-20
YANTAI UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, although the stability, fire resistance and re-ignition resistance of the three-phase foam have been improved during the performance test, the three-phase foam will also have the conventional foam fire extinguishing effect when actually fighting a super large sea oil spill fire. The injection of materials is difficult, the waste is serious, the foam covering layer has poor damage resistance, and the covering time on the oil surface is short, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of foam fire extinguishing material containing closed-cell foam ceramic ball and preparation method thereof
  • A kind of foam fire extinguishing material containing closed-cell foam ceramic ball and preparation method thereof
  • A kind of foam fire extinguishing material containing closed-cell foam ceramic ball and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A foam fire extinguishing material containing closed-cell foam ceramic balls comprises, in parts by weight, 100 g of fluoroprotein foam fire extinguishing agent, 100 g of closed-cell foam ceramic balls and 1000 g of water.

[0026] The preparation method of the above-mentioned foam fire extinguishing material containing closed-cell foam ceramic balls, the steps are as follows:

[0027] (1) Acid treatment: pour 1000mL concentrated sulfuric acid and 400mL, 30wt% hydrogen peroxide into 300g closed-cell foam ceramic balls, stir the mixture for 20min at a speed of 100-150 rpm, rinse the closed-cell foam ceramic balls with water ,dry;

[0028] (2) Alkali treatment: Pour 200mL, 25wt% ammonia water, 200mL, 30wt% hydrogen peroxide and 1000mL water into the acid-treated closed-cell foam ceramic ball, heat the mixed solution to 65°C, and use ultrasonic vibration with 100 rpm Stir at a rotating speed of 50 minutes, then filter and dry the closed-cell foam ceramic balls;

[0029] ...

Embodiment 2

[0033] A foam fire extinguishing material containing closed-cell foam ceramic balls, its components include: 200g of fluoroprotein foam fire extinguishing agent, 150g of closed-cell foam ceramic balls and 1000g of water.

[0034] The preparation method of the above-mentioned foam fire extinguishing material containing closed-cell foam ceramic balls, the steps are as follows:

[0035](1) Acid treatment: pour 1500mL concentrated sulfuric acid and 600mL, 30wt% hydrogen peroxide into 300g closed-cell foam ceramic balls, stir the mixture for 30min at a speed of 100-150 rpm, rinse the closed-cell foam ceramic balls with water ,dry;

[0036] (2) Alkali treatment: Pour 300mL, 25wt% ammonia water, 300mL, 30wt% hydrogen peroxide and 1500mL water into the acid-treated closed-cell foam ceramic ball, heat the mixed solution to 75°C, and use ultrasonic vibration with 150 rpm Stir for 60 minutes at a rotating speed of 10 minutes, then filter and dry the closed-cell foam ceramic balls;

[0...

Embodiment 3

[0041] A foam fire extinguishing material containing closed-cell foam ceramic balls, its components include: 150g of fluoroprotein foam fire extinguishing agent, 125g of closed-cell foam ceramic balls and 1000g of water.

[0042] The preparation method of the above-mentioned foam fire extinguishing material containing closed-cell foam ceramic balls, the steps are as follows:

[0043] (1) Acid treatment: pour 1250mL concentrated sulfuric acid and 500mL, 30wt% hydrogen peroxide into 300g of closed-cell foam ceramic balls, stir the mixture for 25min at a speed of 120 rpm, rinse the closed-cell foam ceramic balls with water, and dry ;

[0044] (2) Alkali treatment: Pour 250mL, 25wt% ammonia water, 250mL, 30wt% hydrogen peroxide and 1250mL water into the acid-treated closed-cell foam ceramic ball, heat the mixed solution to 70°C, use ultrasonic vibration and cooperate with 100-150 Stir at a speed of rev / min for 55min, then filter and dry the closed-cell foam ceramic balls;

[004...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of fire extinguishing materials, in particular to a foam fire extinguishing material containing closed-cell foam ceramic balls and a preparation method thereof. The closed-cell foam ceramic balls used in the present invention have relatively large specific gravity and hydrophilic and oil-repellent properties, so when mixed and sprayed to the sea surface as a fire extinguishing material, the closed-cell foam ceramic balls and fluoroprotein foam fire extinguishing agent form a layered structure , the closed-cell foam ceramic ball layer will move with the sea surface, play a buffer role on the foam protein layer above it, reduce the tearing and damage effect of the sea surface disturbance on the foam protein layer, ensure the continuity of the foam protein layer, and improve the foam protein layer. The sealing effect of the oil surface. In addition, foam protein is sandwiched between the closed-cell foam ceramic balls in the closed-cell foam ceramic ball layer, and the foam protein is well protected, with good stability and long fire resistance. Therefore, the foam fire extinguishing material of the present invention has good stability, burning resistance and resurgence resistance.

Description

technical field [0001] The invention belongs to the technical field of fire extinguishing materials, in particular to a foam fire extinguishing material containing closed-cell foam ceramic balls and a preparation method thereof. Background technique [0002] Oil chemical raw materials are generally flammable and explosive. Once a fire or explosion accident occurs, it will often cause huge economic losses. Therefore, there are strict operating specifications during storage and transportation. Even so, there are often oil fire accidents caused by various reasons in the world. Generally speaking, these oil product fire accidents can be divided into three types: static storage, land transportation, and dynamic floating. The floating type generally occurs during the ocean transportation of oil products. Compared with the static storage type and land transportation type oil fire, the dynamic floating type oil fire will quickly spread and spread on the sea surface due to the acti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A62D1/02
CPCA62D1/0071A62D1/0078
Inventor 李向明周光友朱小涛任桂娜杨晴
Owner YANTAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More