Low-cost S420NL low-temperature toughness steel plate and manufacturing method

A technology of low temperature toughness and manufacturing method, which is applied in the field of iron and steel smelting, can solve the problems of unsatisfactory low temperature impact performance, unfavorable welding performance, and large amount of alloy added, and achieves the effects of excellent welding performance, low alloy cost and simple production process.

Active Publication Date: 2019-10-22
NANJING IRON & STEEL CO LTD
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high carbon content of the above-mentioned steel design, the low-temperature impact performance is not ideal; the amount of alloy added is high, and the production cost is high; the CEV is too high, which is not good for welding performance; in addition, the steel plate needs to be normalized, and the production process is many and the cost is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] This embodiment provides a low-cost S420NL low-temperature tough steel plate and its manufacturing method, and the thickness of the steel plate is 60 mm.

[0053] Its chemical composition and mass percentage are as follows: C: 0.14%, Mn: 1.51%, Si: 0.35%, P: 0.012%, S: 0.003%, Nb: 0.028%, V: 0.045%, Ni: 0.28%, Alt: 0.026%, CEV: 0.43%, the balance is Fe and impurities.

[0054] Steps include:

[0055] S1. Steelmaking process: molten steel P: 0.012% when using converter for deep dephosphorization, molten steel S: 0.003% for molten iron pretreatment and LF deep desulfurization, continuous casting production to prepare a slab with a thickness of 260 mm;

[0056] S2. Heating process: the billet is heated in a heating furnace, the heating coefficient is 11.6min / cm, and the heating temperature is 1218°C;

[0057] S3. Rolling process: two-stage controlled rolling process is adopted, the first stage is rough rolling, and the rolling end temperature is 1022°C; the second stage ...

Embodiment 2

[0061] This embodiment provides a low-cost S420NL low-temperature tough steel plate and its manufacturing method, and the thickness of the steel plate is 60 mm.

[0062] Its chemical composition and mass percentage are as follows: C: 0.13%, Mn: 1.55%, Si: 0.32%, P: 0.010%, S: 0.002%, Nb: 0.026%, V: 0.043%, Ni: 0.27%, Alt: 0.033%, CEV: 0.43%, the balance is Fe and impurities.

[0063] Steps include:

[0064] S1. Steelmaking process: molten steel P: 0.010% when using converter for deep dephosphorization, molten steel S: 0.002% for molten iron pretreatment and LF deep desulfurization, continuous casting production to prepare a slab with a thickness of 260 mm;

[0065] S2. Heating process: the billet is heated in a heating furnace, the heating coefficient is 12.2min / cm, and the heating temperature is 1193°C;

[0066] S3. Rolling process: Two-stage controlled rolling process is adopted, the first stage is rough rolling, and the rolling end temperature is 1193°C; the second stage ...

Embodiment 3

[0070] This embodiment provides a low-cost S420NL low-temperature tough steel plate and its manufacturing method, and the thickness of the steel plate is 40 mm.

[0071] Its chemical composition and mass percentage are as follows: C: 0.13%, Mn: 1.46%, Si: 0.27%, P: 0.014%, S: 0.003%, Nb: 0.023%, V: 0.038%, Ni: 0.24%, Alt: 0.028%, CEV: 0.41%, the balance is Fe and impurities.

[0072] Steps include:

[0073] S1, steelmaking process: molten steel P: 0.014% when using converter for deep dephosphorization, molten steel S: 0.003% for molten iron pretreatment and LF deep desulfurization, continuous casting production to prepare a slab with a thickness of 260mm;

[0074] S2. Heating process: the billet is heated in a heating furnace, the heating coefficient is 11.1min / cm, and the heating temperature is 1204°C;

[0075] S3. Rolling process: two-stage controlled rolling process is adopted, the first stage is rough rolling, and the rolling end temperature is 1012°C; the second stage i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-cost S420NL low-temperature toughness steel plate and a manufacturing method and relates to the technical field of iron and steel smelting. Chemical components of the low-cost S420NL low-temperature toughness steel plate comprise, by mass percentage, 0.12-0.15% of C, 1.40-1.60% of Mn, 0.20-0.40% of Si, smaller than or equal to 0.015% of P, smaller than or equal to 0.005% of S, 0.015-0.030% of Nb, 0.030-0.050% of V, 0.10-0.30% of Ni, 0.020-0.050% of Alt, smaller than or equal to 0.45% of CEV and the balance Fe and impurities. Low-carbon content design is adopted for the low-cost S420NL low-temperature toughness steel plate, normalizing heat treatment is replaced by a normalizing rolling process, a normalizing heat treatment process is eliminated, the S420NL low-temperature toughness steel plate with the performance fully meeting the EN10025-3 standard requirement is obtained, the production cost is low, and economical and efficient production is achieved.

Description

technical field [0001] The invention relates to the technical field of iron and steel smelting, in particular to a low-cost S420NL low-temperature tough steel plate and a manufacturing method. Background technique [0002] S420NL steel plate is an EN10025-3 standard product, which requires normalizing or normalizing rolling delivery. It is mainly used in key structural parts such as large bridges, long-span buildings, wind power, hydropower, and marine engineering. Steel plates are not only required to have a high strength grade, but also have strict requirements on the product's low-temperature impact performance, lamellar tear resistance, internal quality, and welding performance. The greater the thickness of the steel plate, the greater the rolling compression ratio is required to improve the quality of internal segregation and porosity. During smelting, the content of low phosphorus and sulfur should be controlled to improve the cleanliness of molten steel, so as to ensu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/02C22C38/04C22C38/12C22C38/08C22C38/06C21D8/02
CPCC21D8/0205C21D8/0226C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12
Inventor 潘中德吴俊平谯明亮方磊刘继宏陈富强高飞李伟张淼
Owner NANJING IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com