Steel waste acid and alkali liquor storage tank inner surface anticorrosion method

A storage tank and inner surface technology is applied in the field of anti-corrosion of the inner surface of the steel waste acid and alkali storage tank, which can solve the problems of delaying the construction period and increasing the cost, and achieves good welding seam sealing performance, low extrusion molding cost, and construction technology. simple effect

Inactive Publication Date: 2019-10-25
JIANGSU KEHUAN INNOVATIVE MATERIAL CO LTD +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

That increases the cost and delays the construction period

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] A method for anticorrosion of the inner surface of a steel waste acid and alkali storage tank, the specific steps comprising:

[0023] S1 uses a plastic extrusion molding machine to extrude a 500X500X8mm vinyl plate according to the curvature of the inner wall of the tank.

[0024] S2 is put into the tank from the manhole at the top of the tank, and the back of the vinyl plate and the inner wall of the tank are bonded with acid and alkali corrosion-resistant silicone rubber adhesive.

[0025] The S3 plate and the edge end of the plate are connected by pressure hot-melt method.

[0026] The method is to place the resistance heating sheet between the edges of two vinyl plates and heat it with electricity. When both sides are in a molten state, quickly pull out the heating sheet and press it firmly to realize pressure welding.

[0027] S4 is to strengthen the bonding strength and anti-corrosion performance of the weld seam. All the weld seam surfaces are welded with a vin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a steel waste acid and alkali liquor storage tank inner surface anticorrosion method. The steel waste acid and alkali liquor storage tank inner surface anticorrosion method utilizes the advantage of being strong in acid and alkali corrosion resistance of ethylene, and prepares a thick ethylene coating on the inner surface of a tank body. The steel waste acid and alkali liquor storage tank inner surface anticorrosion method includes the concrete steps that in a preparation method of the side wall anticorrosion coating, an extrusion forming machine is used for forming ethylene plates through extrusion according to the curvature of the inner wall of the tank body, the thickness of the ethylene plates is confirmed according to requirements of a user for use life, and the thicker the ethylene plates are, the longer the use life is; an acid and alkali corrosion resisting bonding agent is used for bonding the reverse sides of the ethylene plates and the inner wall of the tank body; a pressure hot melting method is used for connecting side ends of the ethylene plates; and the bottom and the top of the tank body are planes, flat ethylene plates can be directly purchased and cut into squares or other shapes facilitating splicing, and similarly, the reverse sides of the flat ethylene plates after being cut are bonded with the inner wall of the tank body, and the pressure hot melting method is used on the side faces of the flat ethylene plates after being cut. Due to the fact that the pressure melting weld is adopted, a weld joint is good in seal performance; the construction technology is simple, energy consumption is low, and efficiency is high; and forming and connection of the ethylene plates are low in cost and high in efficiency, the ethylene plates are long in use life, reduction of repair frequency and cost of a waste acid and alkali liquor storage tank is facilitated, and economic benefit of an enterprise is improved.

Description

technical field [0001] The invention belongs to the technical field of metal surface corrosion and protection, in particular to an anticorrosion method for the inner surface of a steel waste acid and alkali storage tank. Background technique [0002] Both waste acid and waste alkali liquid are hazardous waste products and must be treated in a harmless and resourceful manner. It is usually stored for a period of time in large storage tanks before processing. In order to ensure the structural strength requirements, large storage tanks are usually made of steel materials. The waste liquid contained in the tank is mixed acid or mixed alkali. The composition and concentration are not fixed. Some contain fluorine, some contain copper and so on. If the inner wall is not treated with anticorrosion, the steel tank will be severely corroded until perforated. [0003] Commonly used surface anti-corrosion technologies such as thermal spraying, laser cladding, surfacing, stick coati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B29C65/02B29C65/48B29C48/07
CPCB29C48/022B29C48/07B29C65/02B29C65/4855B29C66/61
Inventor 曲作鹏陈威王海军田欣利叶怀宇陈大智王海斗欧阳晓平
Owner JIANGSU KEHUAN INNOVATIVE MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products