Adhesive sticker material convenient to remove

A removable and convenient technology, applied in the direction of adhesives, film/sheet adhesives, adhesive types, etc., can solve the problem of affecting the appearance and use of the object to be pasted, can not meet the requirements of removable label materials, Problems such as poor mechanical properties of self-adhesive materials, to achieve the effects of convenient removability, low strength, and high adhesion

Active Publication Date: 2019-10-25
嘉兴艾科新材料科技有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] 1. The mechanical properties of the self-adhesive material are poor, and it is easy to be torn or broken, resulting in damage or loss of information printed on the surface of the self-adhesive material;
[0014] 2. After the self-adhesive material is pasted, it is inconvenient to remove, and it takes a lot of effort, and it is easy to tear the self-adhesive material, resulting in damage and loss of information printed on the surface of the self-adhesive material, which cannot meet the requirements of the removable label material requirements;
[0015] 3. After the self-adhesive material is pasted and removed, a large amount of residual glue will be left on the surface of the pasted object, which will affect the appearance and use of the pasted object

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] A self-adhesive material that is convenient to remove, including a surface material layer, an adhesive layer and a release paper substrate layer arranged in sequence; the adhesive layer is passed between the surface material layer and the release paper substrate layer Adhesive and peelable from each other;

[0057] The surface material layer is made of the following raw materials in parts by weight: 60-70 parts of polyethylene, 30-45 parts of styrene-ethylene-propylene-styrene copolymer, 2-3.5 parts of antioxidant, 3 parts of flame retardant ~6 parts, 2~5 parts of processing aids;

[0058] The adhesive layer is made of the following raw materials in parts by weight: 40-50 parts of methoxyethyl methacrylate-acrylic acid-butyl acrylate copolymer solution, octapentyl glycol diacrylate-acrylic acid-butyl acrylate 40-50 parts of ester copolymer solution, 15-25 parts of liquid rosin resin, 5-10 parts of polymethylhydroxydienyl siloxane;

[0059] The methoxyethyl methacrylat...

Embodiment 2

[0080] A self-adhesive material that is convenient to remove, including a surface material layer, an adhesive layer and a release paper substrate layer arranged in sequence; the adhesive layer is passed between the surface material layer and the release paper substrate layer Adhesive and peelable from each other;

[0081] The surface material layer is made of raw materials including the following parts by weight: 60 parts of polyethylene, 30 parts of styrene-ethylene-propylene-styrene copolymer, 2 parts of antioxidant, 3 parts of flame retardant, 2 parts of processing aid share;

[0082] The adhesive layer is made of raw materials including the following parts by weight: 40 parts of methoxyethyl methacrylate-acrylic acid-butyl acrylate copolymer solution, octapentyl glycol diacrylate-acrylic acid-butyl acrylate copolymer 40 parts of product solution, 15 parts of liquid rosin resin, 5 parts of polymethylhydroxydienyl siloxane;

[0083] The methoxyethyl methacrylate-acrylic ac...

Embodiment 3

[0104] A self-adhesive material that is convenient to remove, including a surface material layer, an adhesive layer and a release paper substrate layer arranged in sequence; the adhesive layer is passed between the surface material layer and the release paper substrate layer Adhesive and peelable from each other;

[0105] The surface material layer is made of raw materials including the following parts by weight: 70 parts of polyethylene, 45 parts of styrene-ethylene-propylene-styrene copolymer, 3.5 parts of antioxidant, 6 parts of flame retardant, 5 parts of processing aid share;

[0106] The adhesive layer is made of raw materials including the following parts by weight: 50 parts of methoxyethyl methacrylate-acrylic acid-butyl acrylate copolymer solution, octapentyl glycol diacrylate-acrylic acid-butyl acrylate copolymer 50 parts of product solution, 25 parts of liquid rosin resin, 10 parts of polymethylhydroxydienyl siloxane;

[0107] The methoxyethyl methacrylate-acrylic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an adhesive sticker material convenient to remove. The adhesive sticker material convenient to remove comprises a plane material layer, an adhesive layer and a release paper bottom material layer which are sequentially arranged; the plane material layer and the release paper bottom material layer are bonded through the adhesive layer and can be mutually peeled; and the plane material layer is prepared from the following raw materials in parts by weight: 60-70 parts of polyethylene, 30-45 parts of styrene-ethylene-propylene-styrol copolymer, 2-3.5 parts of an antioxygen,3-6 parts of a fire retardant and 2-5 parts of a processing agent. According to the adhesive sticker material convenient to remove, the adhesive sticker material convenient to remove is convenient toremove after sticking, the needed effort is small, the adhesive sticker material is not prone to being torn up, information existing on the surface of the adhesive sticker is guaranteed, and the adhesive sticker material is suitable for being used as a removable label material; and after the adhesive sticker material is stuck and removed, the amount of adhesive residue left on the surface of an stuck object is very small, and the appearance and using of the stuck object cannot be influenced.

Description

technical field [0001] The invention relates to the technical field of self-adhesive materials, in particular to a self-adhesive material that is easy to remove. Background technique [0002] Self-adhesive materials are divided into five categories: [0003] 1. According to the characteristics of the adhesive, it can be divided into permanent self-adhesive materials and removable self-adhesive materials; [0004] 2. According to the classification of adhesive coating technology, it can be divided into hot-melt self-adhesive materials, solvent-based self-adhesive materials and emulsion-type self-adhesive materials; [0005] 3. According to the classification of adhesive and chemical properties, it is divided into two kinds of self-adhesive materials: rubber base and acrylic; [0006] 4. According to the characteristics of the backing paper, it is divided into three kinds of self-adhesive materials: opaque backing paper, translucent backing paper and transparent backing pape...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/24C09J7/30C09J133/14C09J135/00C09J193/04C09J11/08
CPCC08K3/2279C08K5/098C08K5/103C08K5/1345C08K5/526C08L2205/035C09J11/08C09J133/14C09J135/00C09J2203/334C09J2423/046C09J2453/006C09J7/243C09J7/30C09J2301/41C08L35/00C08L93/04C08L83/04C08L33/14
Inventor 宣伟
Owner 嘉兴艾科新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap