Anti-corrosion spraying process based on polytetrafluoroethylene material

A technology of anti-corrosion spraying and fluorine materials, which is applied to coatings, devices for coating liquid on surfaces, and pre-treated surfaces, etc. It can solve problems such as affecting the service life of products, uneven spraying effects, and poor adsorption effects. Good quality, good anti-corrosion effect, good performance effect

Inactive Publication Date: 2019-11-01
江苏优氟防腐科技有限公司
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of the economy, various industries such as chemical industry, petroleum, shipbuilding, power plants, public utilities, etc. have increasingly urgent requirements for corrosion protection of pipelines and pumps, and their grades have been continuously improved. Specifically refers to polytetrafluoroethylene, and the anti-corrosion spraying process refers to spraying coatings on items to achieve anti-corrosion effects and avoid items being rusted; while the existing anti-corrosion spraying process based on PTFE materials, PTFE materials are used in other The spraying effect is not uniform during the spraying process, and the anti-corrosion time is short during use, which may cause shedding. At the same time, the adsorption effect is not good, so that there is a gap between the topcoat and the primer, resulting in corrosion, which affects the quality of the product. Service life, for this reason, we propose an anti-corrosion spraying process based on PTFE material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0021] When spraying, first clean the surface of the steel. Use 290Kpa of pressure water to rinse and clean the debris and stains on the surface of the steel for 10 minutes. Then use sandpaper to polish the surface of the steel to evenly polish the protrusions on the surface of the steel. When the temperature reaches about 20um, wipe clean with fluorocarbon thinner and dry in the sun to obtain clean and polished steel; sandblast the clean and polished steel, and use a sandblasting machine and air compressor to spray the steel substrate Sand treatment, the air compressor pressure is controlled at 0.7MPa, the sandblasting pressure is controlled at 0.35MPa, the sandblasting time is controlled at 6min, the sandblasting abrasive is 30 mesh black corundum, the surface roughness of the steel after sandblasting is 60μm, and the surface of the steel after rust removal Reach the St3 standard stipulated in "Steel surface corrosion grade and derusting grade before painting" GB / T8923-88, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
surface roughnessaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-corrosion spraying process based on a polytetrafluoroethylene material. The anti-corrosion spraying process based on the polytetrafluoroethylene material comprises thefollowing steps that 1, the surface treatment is carried out on a rolled steel, specifically, the cleaning treatment is carried out on the surface of the rolled steel firstly, sundries and stains on the surface of the rolled steel is washed and cleaned by using pressure water of 290 Kpa, and the time length is 10-15min; then an abrasive paper is used for grinding treatment, projections on the surface of the rolled steel is polished uniformly, and the roughness of the surface of the rolled steel reaches about 20 microns; a fluorocarbon diluting agent is used to wipe the surface of the rolled steel cleanly, and exposing and airing are carried out to obtain the clean and polished rolled steel. According to the anti-corrosion spraying process based on the polytetrafluoroethylene material, through the multiple spraying step process and the anti-corrosion function of the polytetrafluoroethylene material, the adhesiveness of the coating rolled steel is improved, the coating is not prone to fall off in use, and the quality of the rolled steel is improved; and meanwhile, the combination degree among primer, finish paint and the rolled steel is improved, the gap condition is avoided in the coating, the anti-corrosion property and the wear resistance of the rolled steel are greatly improved, and a good application prospect is realized.

Description

Technical field [0001] The invention belongs to the field of spraying technology, and particularly relates to an anticorrosive spraying process based on tetrafluorocarbon materials. Background technique [0002] With the development of economy, chemical, petroleum, shipbuilding, power plant, public utilities and other industries have increasingly urgent requirements for anti-corrosion of pipelines, pumps, etc., and the grades continue to improve, and higher and higher requirements for the anti-corrosion performance of materials are also put forward. PTFE materials Specifically refers to polytetrafluoroethylene, and the anti-corrosion spraying process refers to spraying coatings on objects to achieve anti-corrosion effect and avoid items from being rusted; while the existing anti-corrosion spraying process based on tetrafluoro materials, tetrafluoro materials are used in other The spraying effect is not uniform during the spraying process, and the anti-corrosion time is short duri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D7/14B05D3/12B05D1/06B05D7/00
CPCB05D1/06B05D3/12B05D7/14B05D7/584B05D2202/10B05D2506/15B05D2508/00
Inventor 吴洋
Owner 江苏优氟防腐科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products