Ceramic composite sheet material and production process thereof

A ceramic composite and plate technology, applied in the production of ceramic materials, ceramic products, applications, etc., can solve problems such as short service life, and achieve the effects of high bonding stability, improved bonding strength and stability, and high hardness

Inactive Publication Date: 2019-11-08
湖北壁玉新材料科技有限公司
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a ceramic composite plate and a process for producing the ceramic composite plate, aiming at solving the problem of short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic composite sheet material and production process thereof
  • Ceramic composite sheet material and production process thereof
  • Ceramic composite sheet material and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A production process of a ceramic composite plate, comprising the following steps:

[0032] S1, crush each base material and pass through a 200-mesh sieve to obtain the powder, dry the powder so that the moisture content is between 5% and 6%, then mix the dried powder in parts by mass, and mix the base material divided into two parts;

[0033] S2, send the first base material to the press and press it into a blank with a pressure of 250MPa. After compaction, the thickness is 3.5mm, and then bisque-fired to form a blank. The bisque firing temperature is 1100°C and the time is 90min;

[0034] S3, transferring the base material to the kiln, mixing the second base material with the foaming agent and laying it on the green board, the thickness of the mixture containing the second base material is 20mm;

[0035] S4, raise the temperature of S3 to 1250°C, keep for 1.5h to burn the whole board;

[0036] S5, annealing and cooling the entire board, and then taking it out to a n...

Embodiment 2

[0049] A production process of a ceramic composite plate, comprising the following steps:

[0050] S1, crush each base material and pass through a 200-mesh sieve to obtain the powder, dry the powder so that the moisture content is between 5% and 6%, then mix the dried powder in parts by mass, and mix the base material divided into two parts;

[0051] S2, send the first base material to the press and press it into a blank with a pressure of 200MPa. After compaction, the thickness is 12mm, and biscuit-fired to form a blank. The bisque firing temperature is 1000°C and the time is 150min;

[0052] S3, transfer the base plate to the kiln, mix the second base material with the foaming agent and spread it on the base plate, the thickness of the mixture containing the second base material is 120mm;

[0053] S4, raise the temperature of S3 to 1250°C, keep for 2.5h to burn the whole board;

[0054] S5, annealing and cooling the entire board, and then taking it out to a natural environ...

Embodiment 3

[0067] A production process of a ceramic composite plate, comprising the following steps:

[0068] S1, crush each base material and pass through a 200-mesh sieve to obtain the powder, dry the powder so that the moisture content is between 5% and 6%, then mix the dried powder in parts by mass, and mix the base material divided into two parts;

[0069] S2, spread the first base material into the container, send it to the press and press it into a blank with a pressure of 280MPa. After compaction, the thickness is 5mm, and bisque-fire it into a blank. The bisque firing temperature is 1100°C and the time is 120min. ;

[0070] S3, transferring the base plate to the kiln, mixing the second base material with the foaming agent and laying it on the base plate, the thickness of the mixture containing the second base material is 70 mm;

[0071] S4, raising the temperature of S3 to 1250°C, keeping it for 2 hours to burn the whole board;

[0072] S5, annealing and cooling the entire bo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of ceramic composite sheet material production processes, and discloses a ceramic composite sheet material and a production process thereof. The ceramic composite sheet material includes an insulation layer and a decorative layer, the insulation layer and the decorative layer both include base materials, the insulation layer further includes a foaming agent, thedecorative layer further includes zirconium silicate, and the base materials are prepared from the components in parts by mass: 20-30 parts of kaoline, 10-15 parts of kieselguhr, 5-8 parts of talcum powder, 3-5 parts of clay, 5-8 parts of a lead-zinc tailing, 8-12 parts of a fluxing agent, 2-4 parts of the foaming agent and 1-3 parts of the zirconium silicate. The service life of the composite sheet material can be prolonged.

Description

technical field [0001] The invention relates to the technical field of production of ceramic composite panels, in particular to ceramic composite panels and a process for producing the ceramic composite panels. Background technique [0002] With the development and use of available resources, people pay more and more attention to energy conservation, and the insulation and cold protection of houses is also one of the means of energy conservation. At present, many buildings will fix insulation boards on the exterior walls of the building after the main body of the building is completed. The insulation boards play the role of heat preservation and cold protection. The insulation boards usually include an insulation layer with a porous structure and a decorative layer located outside the insulation layer. After being installed on the building, the decorative layer is located on the outside of the building, which is used to play an aesthetic role. [0003] Among them, after the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/32C04B38/02
CPCC04B33/1321C04B33/1324C04B33/32C04B38/02C04B2235/3201C04B2235/3208C04B2235/321C04B2235/3248C04B2235/3294C04B2235/3418C04B2235/3427C04B2235/3454C04B2235/36C04B2235/3826C04B2235/6562C04B2235/6567C04B2235/6583C04B2235/663C04B2235/96C04B2235/9607Y02P40/60
Inventor 罗浩铭邹铁军
Owner 湖北壁玉新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com