A kind of pre-oxygenated filament core-spun yarn and its manufacturing method

A manufacturing method and technology of pre-oxidized yarn, which is applied in the direction of yarn, textile and papermaking, conjugated synthetic polymer artificial filament, etc., can solve the problems of low mechanical strength of pre-oxidized yarn, less application of pre-oxidized yarn, and not suitable for skin contact, etc. , to achieve excellent heat insulation effect, excellent thermal stability, improved wear resistance and wearability

Active Publication Date: 2022-07-05
义乌市恒达织带有限公司 +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, although pre-oxidized silk has many advantages of carbon fiber products, and the cost is much lower than that of carbon fiber, due to the low mechanical strength of pre-oxidized silk, it is easy to break and break, and it is not suitable for contact with the skin. fewer applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of pre-oxygenated filament core-spun yarn and its manufacturing method
  • A kind of pre-oxygenated filament core-spun yarn and its manufacturing method
  • A kind of pre-oxygenated filament core-spun yarn and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Refer to the attached Figure 1-3 , this embodiment provides a kind of manufacture method of pre-oxygen silk core-spun yarn, comprising the following steps:

[0033] S1. Put 5kg of common polyacrylonitrile resin with isotacticity of 20% and 2kg of high-grade polyacrylonitrile resin with isotacticity of 45% into a high-speed mixer for stirring and mixing for 10 hours to obtain a mixed resin.

[0034] S2, add 5kg of the above mixed resin and 12kg of dimethylformamide into the reaction kettle, and control the temperature of the reaction kettle to rise to 200°C at a uniform speed within 2h, so that the mixed resin and dimethylformamide are at a constant temperature of 200°C After 4 hours of continuous stirring and mixing under the conditions, the reaction kettle is vacuumed and debubble, and then the mixed materials are filtered to obtain the spinning dope.

[0035] S3, first use the dry and wet spinning technology to process the spinning dope through the screw extruder, t...

Embodiment 2

[0039] Refer to the attached Figure 1-3 , this embodiment provides a kind of manufacture method of pre-oxygen silk core-spun yarn, comprising the following steps:

[0040] S1. Put 5kg of common polyacrylonitrile resin with isotacticity of 10% and 4kg of high-grade polyacrylonitrile resin with isotacticity of 55% into a high-speed mixer for stirring and mixing for 10 hours to obtain a mixed resin.

[0041] S2, add 5kg of above-mentioned mixed resin and 15kg of dimethylformamide to the reaction kettle, and control the temperature of the reaction kettle to rise to 250°C at a uniform speed in 2h, so that the mixed resin and dimethylformamide are at a constant temperature of 250°C After 4 hours of continuous stirring and mixing under the conditions, the reaction kettle is vacuumed and debubble, and then the mixed materials are filtered to obtain the spinning dope.

[0042] S3, first use the dry and wet spinning technology to process the spinning dope through the screw extruder, t...

Embodiment 3

[0046] Refer to the attached Figure 1-3 , this embodiment provides a kind of manufacture method of pre-oxygen silk core-spun yarn, comprising the following steps:

[0047] S1. Put 5kg of common polyacrylonitrile resin with isotacticity of 5% and 3kg of high-grade polyacrylonitrile resin with isotacticity of 50% into a high-speed mixer for stirring and mixing for 10 hours to obtain a mixed resin.

[0048] S2, add 5kg of the above mixed resin and 12kg of dimethylformamide into the reaction kettle, and control the temperature of the reaction kettle to rise to 200°C at a uniform speed within 2h, so that the mixed resin and dimethylformamide are at a constant temperature of 200°C After 4 hours of continuous stirring and mixing under the conditions, the reaction kettle is vacuumed and debubble, and then the mixed materials are filtered to obtain the spinning dope.

[0049] S3, first use the dry and wet spinning technology to process the spinning dope through the screw extruder, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a pre-oxidized silk core-spun yarn and a manufacturing method thereof, belonging to the technical field of textiles. The manufacturing method of the pre-oxygenated filament core-spun yarn comprises the following steps: mixing common polyacrylonitrile resin and high-tacticity polyacrylonitrile resin to obtain a mixed resin; placing the mixed resin and dimethylformamide under high temperature conditions to carry out After mixing, filtering is carried out to obtain a spinning dope; first, the spinning dope is processed into primary fibers, and pre-oxidation treatment and spinning are carried out in sequence to obtain pre-oxidized filaments; After sizing pretreatment, the filaments are dried; finally, the dried pre-oxidized filaments are wrapped with short fiber rovings, and twisted and desizing are performed in turn to obtain the pre-oxidized filament core-spun yarn. The pre-oxygenated core-spun yarn obtained by the invention not only has high flame retardancy and excellent thermal stability, but also has high mechanical strength and suitable textile processing performance.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a pre-oxygenated core-spun yarn and a manufacturing method thereof. Background technique [0002] Pre-oxidized fiber refers to a black fiber with a partially cyclic structure formed by carbon-containing organic fiber precursor under high temperature pre-oxidation in an air medium. It has the characteristics of melting, no dripping, and environmental protection. [0003] However, although the pre-oxygen wire has many advantages of carbon fiber products, and the cost is much lower than that of carbon fiber, due to the low mechanical strength of the pre-oxygen wire, it is easy to break and break, and it is not suitable for contact with the skin. Therefore, the pre-oxygen wire is currently used in the field of consumption. less applications. SUMMARY OF THE INVENTION [0004] The purpose of the present invention is to provide a pre-oxygenated core-spun yarn and a manufacturing me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04D02G3/36D01F8/08D06M15/15D06M101/28
CPCD02G3/045D02G3/047D02G3/36D01F8/08D06M15/15D10B2331/021D10B2321/10D06M2101/28D06M2200/40
Inventor 竺铝涛方平钟俊杰
Owner 义乌市恒达织带有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com