Starlight glazed ceramic tile and preparation method thereof

A technology of ceramic tiles and star glaze, applied in the field of ceramic tile preparation, can solve the problems of lack of unique new products, single presentation effect, serious homogenization phenomenon, etc., achieves good pattern definition, meets diverse needs, and is trendy decorative effect

Active Publication Date: 2019-11-22
GUANGDONG XINRUNCHENG CERAMICS
View PDF8 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a starlight glazed ceramic tile and its preparation method, aiming at solving the problem that existing ceramic til

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Starlight glazed ceramic tile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The preparation method of starlight glazed ceramic tile comprises the following steps:

[0029] (1) Press the powder into a green body, and dry the green body at 150°C for 1.5 hours;

[0030] (2) Clean the surface of the green body, and spray water on the surface of the green body to make the surface of the green body wet;

[0031] (3) Apply primer on the surface of the green body;

[0032] (4) Use screen printing color glaze, preferably use 100 mesh all-through screen;

[0033] (5) Inkjet printing pattern;

[0034] (6) Apply transparent bright dry granules on the brick surface, preferably evenly spread the transparent bright dry granules on the brick surface in the shape of sand;

[0035] (7) Put the green body in step (6) into a kiln for firing at a temperature of 1150°C and a firing time of 60 minutes;

[0036] (8) Softly polish the transparent bright dry particles protruding from the surface of the fired tiles to obtain starlight glazed ceramic tiles.

[0037] ...

Embodiment 2

[0042] The preparation method of starlight glaze ceramic tile is identical with embodiment 1.

[0043] Starlight Glazed Porcelain Tiles, see figure 1 , including body layer 1, bottom glaze layer 2, chromogenic glaze layer 3 and dry granular glaze layer 4 from bottom to top.

[0044] Wherein, the transparent light dry granules used in the dry granule glaze layer include 38 parts by weight of potassium feldspar, 12 parts of burnt talc, 10 parts of calcite, 33 parts of quartz, 10 parts of barium carbonate, 10 parts of calcined alumina, 5 parts air knife soil and 3 parts zinc oxide. The preparation method of the transparent glossy dry granule is the same as that of Example 1.

[0045] The formula and preparation method of the bottom glaze are the same as in Example 1.

[0046] The formula and the preparation method of chromogenic glaze are identical with embodiment 1.

Embodiment 3

[0048] The preparation method of starlight glaze ceramic tile is identical with embodiment 1.

[0049] Starlight glazed ceramic tiles, from bottom to top, include body layer, bottom glaze layer, colored glaze layer and dry grain glaze layer.

[0050] Wherein, the transparent light dry granules used in the dry granule glaze layer include 38 parts by weight of potassium feldspar, 12 parts of burnt talc, 8 parts of calcite, 33 parts of quartz, 12 parts of barium carbonate, 10 parts of calcined alumina, 5 parts of air knife soil and 3 parts zinc oxide. The preparation method of the transparent glossy dry granule is the same as that of Example 1.

[0051] The formula and preparation method of the bottom glaze are the same as in Example 1.

[0052] The formula and the preparation method of chromogenic glaze are identical with embodiment 1.

[0053] The difference of embodiment 1,2,3 is that the proportioning of calcite and barium carbonate is different in the formula of transpare...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a starlight glazed ceramic tile which comprises a green body layer, a ground glaze layer, a chromophoric glaze layer and a dry granular glaze layer from bottom to top. The preparation method comprises the following steps: (1) pressing powder into a green body, and drying the green body at 145-160 DEG C for 1-1.5 hours; (2) cleaning the surface of the green body, and spraying water to the surface of the green body to wet the surface of the green body; (3) applying ground glaze to the surface of the green body; (4) carrying out silk-screen printing to form the chromophoric glaze; (5) performing ink-jet printing of patterns; (6) applying transparent bright dry granules to the brick surface; (7) putting the green body obtained in the step (5) into a kiln, and firing thegreen body for 40-60 minutes at the temperature of 1150-1200 DEG C; and (8) performing soft polishing on the transparent bright dry granules protruding out of the surface of the fired ceramic tile toobtain the starlight glaze ceramic tile. The protruding surface of the ceramic tile is in a fine and soft matte feeling, but the whole ceramic tile is in a flashing spot starlight effect, the patterndefinition is good, the product is extremely attractive, and the blank of the product on the market is filled up.

Description

technical field [0001] The invention relates to the technical field of ceramic tile preparation, in particular to a starlight glazed ceramic tile and a preparation method thereof. Background technique [0002] With the rapid development of the economy and the continuous improvement of people's living standards, consumers have begun to have higher requirements for the decoration effect of the indoor environment. At present, there are many types of ceramic tiles in the building ceramics industry: polished tiles, antique tiles, porcelain tiles, dry-grain glazed tiles, fully polished glazed tiles, diamond glazed tiles, etc. The above-mentioned types of tiles have their own characteristics, which meet the different needs of consumers to a certain extent. However, the above-mentioned products have been flooding the market for many years. The products have a single effect, serious homogeneity, and consumers are gradually fatigued. There is a lack of unique and trend-setting new pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00C03C8/04C04B41/89
CPCC03C8/00C03C8/04C04B41/52C04B41/89
Inventor 关润淡关伟洪关伟铿段锦霞梁耀联张庆刚廉光赵令逸黄建忠李焰红莫炳基张青波赖毓生辛肖桃梁文勇
Owner GUANGDONG XINRUNCHENG CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap