Main grid positive silver paste suitable for step-by-step screen printing

A technology of screen printing and silver paste, applied in the direction of conductive materials, electrical components, circuits, etc. dispersed in non-conductive inorganic materials, can solve the problems of high cost and high solid content of paste, and achieve low cost and high conductivity Excellent, adhesion-enhancing effect

Active Publication Date: 2020-01-03
GUANGZHOU RUXING TECH DEV +1
View PDF12 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] However, the preparation of electrodes using the above slurry still has the following disadvantages:
[0009] 1) The improvement of electrical performance is mainly by improving the contact performance, which is very limited;
[0010] 2) The solid content of the slurry is higher and the cost is higher;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A busbar front silver paste suitable for step-by-step screen printing, comprising the following components in weight percentage: silver powder 80wt%, organic vehicle 10wt%, glass powder 2.0wt%, diluent 3.0wt%, nano silver Thread 3wt% and erucamide 2.0wt%;

[0034] The silver powder comprises the following components by weight percentage: 15wt% of spherical silver powder, 40wt% of spherical silver powder, 30wt% of flake silver powder and 15wt% of nano silver powder; the surface of the silver powder is coated with a fatty acid dispersant;

[0035] The organic vehicle comprises the following components in percentage by weight: terpineol 80wt%, thickener 12wt%, dispersant 4wt%, wetting agent 2wt% and thixotropic agent 2wt%; thickener is ethyl cellulose The mixture of cellulose and epoxy resin, and the weight ratio of ethyl cellulose and epoxy resin is 1:0.8, and the thixotropic agent is polyethylene wax.

[0036] The glass powder is a silicate glass, expressed in weight pe...

Embodiment 2

[0038] The busbar front silver paste of this embodiment is basically the same as that of Embodiment 1, except that the silicate glass of this embodiment is represented by the following oxide-based weight percentages: SiO 2 45wt%, PbO 30wt%, Bi 2 o 3 15wt%, B 2 o 3 8wt%, CuO 1wt%, and MnO 2 1 wt%.

Embodiment 3

[0040] The busbar front silver paste of this embodiment is basically the same as that of Embodiment 1, except that the silicate glass of this embodiment is represented by the following oxide-based weight percentages: SiO 2 50wt%, PbO 20wt%, Bi 2 o 3 18wt%, B 2 o 38wt%, ZnO 2wt, CuO 1wt%, and MnO 2 1 wt%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses main grid positive silver paste suitable for step-by-step screen printing. The slurry comprises the following components in percentage by weight: 78-89 wt% of silver powder, 5-15 wt% of an organic carrier, 1.2-3.0 wt% of glass powder, 2.0-15 wt% of a diluting agent and 0.2-5.0 wt% of an auxiliary. The glass powder comprises at least one of silicate glass, borate glass, phosphate glass and heavy metal oxide glass. The auxiliary comprises an adhesion promoter. By optimizing the formula composition, the prepared paste has the advantages of low solid content, low cost, goodconductivity and high adhesive force, and is suitable for step-by-step screen printing of a main grid part.

Description

technical field [0001] The invention relates to the field of electronic materials, in particular to a busbar front silver paste suitable for step-by-step screen printing. Background technique [0002] Improving the electrical performance and reducing the cost of crystalline silicon solar cells is an eternal theme in the photovoltaic industry. From new battery technology to new slurry technology, they are all centered on this theme. With the development of new battery technology, busbar battery paste is also constantly updated and improved. The busbar battery paste is suitable for printing the busbar part by step-by-step screen printing. It involves conventional p-type polycrystalline cells, monocrystalline cells, perc cells, n-type cells, n-pert cells, and topcon cells. . [0003] There are three printing methods for metallizing the main grid and sub-grid on the surface of the cell, including single printing, secondary printing and step-by-step printing. Single printing c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01B1/22H01L31/0224C03C3/108
CPCC03C3/108H01B1/22H01L31/022425
Inventor 黄淑枚丁冰冰孙倩黄铭
Owner GUANGZHOU RUXING TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap